Translucency of nanoparticle-reinforced PMMA denture base material: An in-vitro comparative study

The aim of this study was to assess the translucency of denture base acrylic resin reinforced with zirconium dioxide (ZrO₂NPs), silicon dioxide (SiO₂NPs), and diamond (DNPs) nanoparticles. A total of 130 heat-polymerized acrylic discs (15×2.5 mm) were fabricated conventionally and divided into control and experimental groups according to nanoparticle type and concentration (0.5, 1, 1.5, and 2.5 wt%). Unmodified acrylic resin specimens served as control. All specimens were thermocycled (5,000 cycles). Translucency was measured using a spectrophotometer. ANOVA and post-hoc Turkeys' test were used for data analysis at α=0.05. The translucency of modified PMMA was significantly lower than control (p<0.05) except 0.5% ZrO₂NPs and SiO₂NPs (p>0.05) which exhibited the highest translucency values among modified groups. As the NPs concentration increased, the translucency decreased and the lowest value was seen with 2.5% DNPs (1.18±0.10). The addition of ZrO₂NPs, SiO₂NPs, and DNPs into denture base resin decreased the translucency.

Electroplated telescopic retainers with zirconia primary crowns: 3-year results from a randomized clinical trial

OBJECTIVE

The objective of the study was to investigate the clinical outcome for electroplated telescopic removable dental prostheses (E-RDPs) with zirconia primary crowns.

MATERIALS AND METHODS

Sixty E-RDPs, with primary crowns manufactured from either cobalt-chromium alloy or zirconia, were fabricated for 56 participants. Electroplating was used to produce gold copings directly on the telescopic primary crowns. These copings were bonded intra-orally to the prosthesis framework. After 36 months, prosthesis survival and number of complications were assessed. Statistical analysis was performed by the use of Kaplan-Meier modeling and the log-rank test.

RESULTS

Survival of the E-RDPs, 96.4% after 3 years, was identical in both groups. The need for aftercare was high but not significantly different: technical complications were observed for 37% and 42.9% of the prostheses for the zirconia and cobalt-chromium alloy primary crowns, respectively. Fracture of composite veneer was the most frequent complication (59.1%). The incidence of fractured abutment teeth, decementation, and endodontic problems was 7.9% in the zirconia group and 14% in the control group. The majority of abutment-level complications were treated restoratively. A significant difference was found for maximum probing depth at the abutment teeth: In the zirconia group, it decreased by 0.2 mm, whereas it increased by 0.8 mm in the control group (p = 0.04).

CONCLUSIONS

After 3 years of observation, survival of zirconia E-RDPs was favorable and comparable with that of established double-crown-retained prostheses. Further studies must clarify whether there are benefits of zirconia primary crowns for periodontal health.

CLINICAL RELEVANCE

Although these results encourage the use of zirconia primary crowns, more research is necessary to reduce the number of complications observed for secondary telescopic crowns, for example, failure of the veneer.