ADM guidance-Ceramics: guidance to the use of fractography in failure analysis of brittle materials

Wear of ceramic-based dental materials

An investigation is made of wear mechanisms in a suite of dental materials with a ceramic component and tooth enamel using a laboratory test that simulates clinically observable wear facets. A ball-on-3-specimen wear tester in a tetrahedral configuration with a rotating hard antagonist zirconia sphere is used to produce circular wear scars on polished surfaces of dental materials in artificial saliva. Images of the wear scars enable interpretation of wear mechanisms, and measurements of scar dimensions quantify wear rates. Rates are lowest for zirconia ceramics, highest for lithium disilicate, with feldspathic ceramic and ceramic-polymer composite intermediate. Examination of wear scars reveals surface debris, indicative of a mechanism of material removal at the microstructural level. Microplasticity and microcracking models account for mild and severe wear regions. Wear models are used to evaluate potential longevity for each dental material. It is demonstrated that controlled laboratory testing can identify and quantify wear susceptibility under conditions that reflect the essence of basic occlusal contact. In addition to causing severe material loss, wear damage can lead to premature tooth or prosthetic failure.

Chipping of veneering ceramic on a lithium disilicate anterior single crown: Description of repair method and a fractographic failure analysis

OBJECTIVE

This article presents a retrospective analysis of an anterior single crown that showed chipping of the veneering ceramic, the clinical stages of intraoral repair made in composite resin, and fractographic analysis of the causes of failure.

CLINICAL CONSIDERATIONS

The ceramic chipping occurred in the incisal and labial surfaces of the crown, 1 year after installation. Clinical examination revealed the presence of occlusal interference, which was probably responsible for chipping. Vinyl-polysiloxane impression was made from the patient, and epoxy replica was produced. The replica was gold coated and inspected under the optical microscopy and scanning electron microscope (SEM) for descriptive fractography. Optical microscopy and SEM images showed that chipping initiated at the incisal edge, where it is possible to note an area of damage accumulation. At the labial surface, multiple arrest lines with their convex sides facing the incisal edge were observed. The fractured area was repaired intraorally with composite resin, and the patient's occlusion was checked and monitored.

CONCLUSION

According to the fractographic analysis, occlusal interference was related to ceramic chipping in the incisal edge. Intraoral repair technique with composite resin was indicated for this moderate chipping.

CLINICAL SIGNIFICANCE

Retrieval analysis of chipping ceramic delivers better understanding of the failure origin and could prevent future failures. Intraoral repair is a practical and conservative technique and may be performed in a single clinical session without requiring the removal of prosthesis.

Fractographic analysis of lithium silicate crown failures during sintering

The two-step production process of glass-ceramic dental restorations involves a computer-aided design/computer-aided machining step followed by a crystallization firing for the final material properties to be achieved. Certain firing parameters are believed to trigger spontaneous fracture of crowns during the cooling process. In this study, cooling fractures have been reproducibly observed and investigated using fractography combined with material (glass transition temperature) and process (cooling rate) characterization. Stress distribution was visualized using birefringence measurements. Fractographic observations revealed fracture starting at the intaglio side of the crowns specifically at contact points with the support firing pins. Further analysis showed that a fast cooling rate was applied during the glass transition region. Thermal stresses were concentrated around the firing pin supports and released the fracture. To prevent such fractures, a slow cooling protocol below the glass transition temperature is our recommendation to dental technicians. Furthermore, the use of planar firing pad or paste supports is advised over the use of point contact supports.

Influence of substrate design for in vitro mechanical testing

Background

The goal of this study was to evaluate the influence of dental substrate simulator material, and the presence of root and periodontal ligament on the stress distribution in an adhesively-cemented monolithic crown.

Material and Methods

Five (5) 3D models according to the substrate simulator material and shape were modeled with CAD software for conducting non-linear finite element analysis (FEA): Tooth with and without periodontal ligament - subgroup "pl" (groups Tooth+pl and Tooth-pl), machined tooth in epoxy-resin with and without pulp chamber - subgroup "pc" (ER+pc and ER-pc) and simplified epoxy-resin substrate without pulp chamber and roots (SiER). Next, adhesively-cemented monolithic crowns in zirconia reinforced lithium silicate were modeled over each substrate. The solids were then imported in STEP format to the analysis software and the contact between teeth and cylinder was considered perfectly bonded; whereas, the contacts involving the resin cement were considered as non-separated. The materials were considered isotropic, linearly elastic, and homogeneous. An axial load (600 N) was applied to the occlusal surface and results of maximum principal stress (MPa) on the restoration were required.

Results

FEA revealed that all evaluated subtracts showed the crown intaglio surface as the most stressed region. The average stress and stress peaks were similar for restorations cemented onto Tooth+pl, Tooth-pl and ER+pc substrates, but, 13% higher in comparison to ER-pc and SiER substrates.

Conclusions

Simplified substrates can be used to evaluate posterior full crown behavior without periodontal ligaments and roots, since the rigidity of the specimen is taken into account. Key words:Finite element analysis, axial loading, computed assisted numerical analisys, monolithic crowns,methodological study.

Translational research on clinically failed zirconia implants

OBJECTIVES

To provide fractographic analysis of clinically fractured zirconia implants recovered with their cemented crown. To calculate bending moments, corresponding stress and crack onset location on the implant's fracture surface using a mathematical model integrating spatial coordinates of the crown-implant part and occlusal loading obtained from 2D and 3D images.

METHODS

15 fractured zirconia implants parts (11 posterior and 4 anterior) with their all- ceramic crowns still cemented on it were recovered. The implants were first generations from four manufacturers (AXIS Biodental, Z-Systems, Straumann, Swiss Dental Solutions). The time-to-failure varied between 2weeks and 9years. Fractography was performed identifying the failure origin and characteristic surface crack features. From 2D and 3D digital images of the crown-implant part, spatial coordinates anchoring the crown's occlusal contacts with the implant's central axis and reference plane were integrated in a mathematical model spreadsheet. Loads of 500 N in total were selectively distributed over identified occlusal contacts from wear patterns. The resultant bending and torsion moments, corresponding shear, tensile, maximum principal stress and von Mises stress were calculated. The fracture crack onset location on the implant's fracture surface was given by an angular position with respect to an occlusal reference and compared with the location of the fracture origin identified from fractographic analysis.

RESULTS

Implants fractured from the periphery of the smaller inner diameter between two threads at the bone-entrance level except for one implant which failed half-way within the bone. The porous coating (AXIS Biodental) and the large grit alumina sandblasting (Z-System) created surface defects directly related to the fracture origin. The model spreadsheet showed how occlusal loading with respect to the implant's central axis affects bending moments and crack onset. Dominant loads distributed on contacts with important wear pattern provided a calculated crack onset location in good agreement with the fractographic findings of the fracture origin.

SIGNIFICANCE

Recovered broken zirconia implant parts with their restorative crowns can provide not only information regarding the failure origin using fractography but also knowledge regarding occlusal crown loading with respect to the implant's axis. The mathematical model was helpful in showing how occlusal loading affects the location of the fracture initiation site on clinical zirconia implant fracture cases.

Effect of margin design on fracture load of zirconia crowns

Zirconia‐based restorations are showing an increase as the clinicians’ preferred choice at posterior sites because of the strength and esthetic properties of such restorations. However, all‐ceramic restorations fracture at higher rates than do metal‐based restorations. Margin design is one of several factors that can affect the fracture strength of all‐ceramic restorations. The aim of this study was to assess the effect of preparation and crown margin design on fracture resistance. Four groups of bilayer zirconia crowns (with 10 crowns in each group) were produced by hard‐ or soft‐machining technique, with the following four different margin designs: chamfer preparation (control); slice preparation; slice preparation with an additional cervical collar of 0.7 mm thickness; and reduced occlusal thickness (to 0.4 mm) on slice preparation with an additional cervical collar of 0.7 mm thickness. Additionally, 10 hard‐machined crowns with slice preparation were veneered and glazed with feldspathic porcelain. In total, 90 crowns were loaded centrally in the occlusal fossa until fracture. The load at fracture was higher than clinically relevant mastication loads for all preparation and margin designs. The crowns on a chamfer preparation fractured at higher loads compared with crowns on a slice preparation. An additional cervical collar increased load at fracture for hard‐machined crowns.

Recent advances in understanding the fatigue and wear behavior of dental composites and ceramics

Dental composite and ceramic restorative materials are designed to closely mimic the aesthetics and function of natural tooth tissue, and their longevity in the oral environment depends to a large degree on their fatigue and wear properties. The purpose of this review is to highlight some recent advances in our understanding of fatigue and wear mechanisms, and how they contribute to restoration failures in the complex oral environment. Overall, fatigue and wear processes are found to be closely related, with wear of dental ceramic occlusal surfaces providing initiation sites for fatigue failures, and subsurface fatigue crack propagation driving key wear mechanisms for composites, ceramics, and enamel. Furthermore, both fatigue and wear of composite restorations may be important in enabling secondary caries formation, which is the leading cause of composite restoration failures. Overall, developing a mechanistic description of fatigue, wear, and secondary caries formation, along with understanding the interconnectivity of all three processes, are together seen as essential keys to successfully using in vitro studies to predict in vivo outcomes and develop improved dental restorative materials.

The effect of extended glaze firing on the flexural fatigue strength of hard-machined ceramics

STATEMENT OF PROBLEM

It is unclear whether an extended glaze firing could improve the long-term mechanical performance of densely sintered CAD-CAM ceramics.

PURPOSE

The purpose of this in vitro study was to analyze the effect of an extended glaze firing on the flexural fatigue strength (FFS) of densely sintered milled (hard-machined) leucite-based (LEU) and lithium disilicate-based (DIS) ceramics.

MATERIAL AND METHODS

Disks were machined from ceramic blocks and divided into 6 groups (n=20) according to the material, LEU or DIS, and to the applied glaze firing: manufacturer-recommended glaze (G group), extended glaze (EG group), and control/no firing (C group). The surface roughness of the disks was measured before and after firing by using a contact profilometer, and data were compared by paired sample tests. Specimens were submitted to fatigue by using the staircase test design in water (piston-on-3 balls; 500 000 cycles, 20 Hz, and sinusoidal loading). Mean (±SD) FFS values were then calculated and analyzed by using 1-way analysis of variance and post hoc Tukey test (α=.05).

RESULTS

Surface roughness did not change after the firing (P>.05). The highest FFS value in both ceramics was obtained after EG firing (LEU-EG=80.52 ±6.3 MPa; DIS-EG=147.25 ±10.5 MPa), which was statistically superior to G firing (LEU-G=73 ±6.8 MPa, P=.003; DIS-G=134.34 ±15.6 MPa; P=.023) and C group (LEU-C=61.94 ±6.3 MPa; P<.001; DIS-C=134.13 ±17.3 MPa; P=.023).

CONCLUSIONS

EG firing optimized the biaxial flexural fatigue strength of hard-machined leucite and lithium disilicate ceramics compared with conventional glaze firing.

Fracture loads and failure modes of customized and non-customized zirconia abutments

OBJECTIVE

This study aimed to evaluate the fracture load and pattern of customized and non-customized zirconia abutments with Morse-taper connection.

METHODS

18 implants were divided into 3 groups according to the abutments used: Zr - with non-customized zirconia abutments; Zrc - with customized zirconia abutments; and Ti - with titanium abutments. To test their load capacity, a universal test machine with a 500-kgf load cell and a 0.5-mm/min speed were used. After, one implant-abutment assembly from each group was analyzed by Scanning Electron Microscopy (SEM). For fractographic analysis, the specimens were transversely sectioned above the threads of the abutment screw in order to examine their fracture surfaces using SEM.

RESULTS

A significant difference was noted between the groups (Zr=573.7±11.66N, Zrc=768.0±8.72N and Ti=659.1±7.70N). Also, the zirconia abutments fractured while the titanium abutments deformed plastically. Zrc presented fracture loads significantly higher than Zr (p=0.009). All the zirconia abutments fractured below the implant platform, starting from the area of contact between the abutment and implant and propagating to the internal surface of the abutment. All the zirconia abutments presented complete cleavage in the mechanical test. Fractography detected differences in the position and pattern of fracture between the two groups with zirconia abutments, probably because of the different diameters in the transmucosal region.

SIGNIFICANCE

Customization of zirconia abutments did not affect their fracture loads, which were comparable to that of titanium and much higher than the maximum physiological limit for the anterior region of the maxilla.

Hygroscopic expansion of self-adhesive resin cements and the integrity of all-ceramic crowns

OBJECTIVE

Low pH neutralization and subsequent remnant hydrophilicity can lead to hygroscopic expansion of self-adhesive resin cements (SARCs) after water storage. The aim of this in vitro study was to investigate the effects of hygroscopic expansion of SARCs, used as luting and partial core build-up material, on integrity and cement gap thickness increase of all-ceramic CAD/CAM crowns.

METHODS

Human third molars (n=48) were prepared and anatomical all-ceramic CAD/CAM crowns were manufactured (VITABLOCS Mark II, VITA Zahnfabrik). Crowns internal surfaces were HF etched and silanized. The prepared teeth with their respective crowns were divided into 6 groups (n=8). In groups 1, 3 and 5 the coronal dentin was removed to simulate a partial core build-up. Groups 1 and 2 were luted with iCEM (Heraeus Kulzer), 3 and 4 with RelyX Unicem 2 Automix (3M), 5 and 6 with Variolink Esthetic DC (Ivoclar Vivadent). All specimens were dual cured and stored in distilled water at 37°C. Crown integrity was controlled at baseline and in regular intervals until 180 days. Cement gap thickness was measured using an optical 3D scanner (ATOS Triple scan, GOM) at baseline and after 180 days. Crown integrity was statistically analysed using Kaplan-Meier survival analysis and cement gap thickness increase using two-way ANOVA (α=0.05).

RESULTS

After 180 days storage, crack formation was observed in all specimens of group 1 (mean survival time of 85.5 days), in one specimen of group 2 and in two specimens of group 4. Two-way ANOVA analysis revealed a statistically significant interaction between material type and build-up on cement gap size increase for iCEM.

SIGNIFICANCE

Within the limits of this study, the application of SARCs with low pH neutralization as partial build-up material under CAD/CAM crowns is not recommended for clinical use.

Fractographic analyses of failed one-piece zirconia implant restorations

BACKGROUND

Promising results of initial clinical trials with yttria-stabilized zirconia have led to more extensive use of zirconia in dental implant superstructures. The applications have extended to abutments and complex individually designed crown-abutment one-piece structures. Little is known about their clinical success and the primary cause of failures.

PURPOSE

The aim of this study was to identify the cause of fracture of retrieved implant-retained one-piece prostheses that failed during clinical use.

METHODS

Nine fractured restorations were analyzed with fractographic methods and their fracture origins were identified.

RESULTS

All but two of the fractures originated in an area of tight contact between the implant or titanium screw and the abutment base. Results of the evaluation showed that zirconia-based implant restorations with very thin walls in the region connecting the prosthesis to the implant are vulnerable to damage from the screw retaining process and fracture from non-axial loads. Two restorations failed due to veneer fractures.

SIGNIFICANCE

The findings suggest that large crowns on narrow implants or implants with internal fixation should preferably not be made with zirconia abutments, or that a new design approach should be considered.

Thermal cracks of implant-based zirconia four-unit restorations: A fractographic analysis of two restorations fractured during production

Two zirconia-based 4-unit restorations intended for the same patient fractured during the veneering process even though the prolonged cooling protocol recommended by the manufacturers was used. Fractographic analyses revealed that both restorations fractured as a result of thermal shock, but at different times during production. Further investigation is necessary to optimize the firing protocols for large zirconia-based restorations and avoid fracture due to thermal shock.

Practical and theoretical considerations on the fracture toughness testing of dental restorative materials

BACKGROUND

An important tool in materials research, development and characterization regarding mechanical performance is the testing of fracture toughness. A high level of accuracy in executing this sort of test is necessary, with strict requirements given in extensive testing standard documents. Proficiency in quality specimen fabrication and test requires practice and a solid theoretical background, oftentimes overlooked in the dental community.

AIMS

In this review we go through some fundamentals of the fracture mechanics concepts that are relevant to the understanding of fracture toughness testing, and draw attention to critical aspects of practical nature that must be fulfilled for validity and accuracy in results. We describe our experience with some testing methodologies for CAD/CAM materials and discuss advantages and shortcomings of different tests in terms of errors in testing the applicability of the concept of fracture toughness as a single-value material-specific property.

Fractography of clinically fractured, implant-supported dental computer-aided design and computer-aided manufacturing crowns

Today, a substantial part of the dental crown production uses computer-aided design and computer-aided manufacturing (CAD/CAM) technology. A recent step in restorative dentistry is the replacement of natural tooth structure with pre-polymerized and machined resin-based methacrylic polymers. Recently, a new CAD/CAM composite was launched for the crown indication in the load-bearing area, but the clinical reality forced the manufacturer to withdraw this specific indication. In parallel, a randomized clinical trial of CAD/CAM composite crowns luted on zirconia implant abutments revealed a high incidence of failure within the first year of service. Fractured crowns of this clinical trial were retrieved and submitted to a fractographic examination. The aim of the case series presented in this article was to identify failure reasons for a new type of CAD/CAM composite crown material (Lava Ultimate; 3M Oral Care, St. Paul, Minnesota, USA) via fractographic examinations and analytical assessment of luting surfaces and water absorption behavior. As a result, the debonding of the composite crowns from the zirconia implant abutments was identified as the central reason for failure. The adhesive interface was found the weakest link. A lack of silica at the zirconia surface certainly has compromised the bonding potential of the adhesive system from the beginning. Additionally, the hydrolytic stress released from swelling of the resin-based crown (water absorption) and transfer to the luting interface further added to the interfacial stress and most probably contributed to a great extend to the debonding failure.