Complex Nanostructures from Materials based on Metal-Organic Frameworks for Electrochemical Energy Storage and Conversion

Enhancing dye degradation using a novel cobalt metal-organic framework as a peroxymonosulfate activator

Among transition metals, cobalt ions exhibit superior catalytic activity in the peroxymonosulfate (PMS) degradation of pollutants. However, practical application is hindered by their high rate of ion leaching and the propensity for particle reunion issues. In this study, a novel cobalt metal-organic framework catalyst, denoted as CUST-565 ([Co3(BTB)2(BIPY)2]·4.5H2O·DMA), was synthesized via a one-step solvothermal method. The obtained crystal was employed as a catalyst to activate PMS for degrading two pollutants, methyl orange (MO) and rhodamine B (RhB), in wastewater. The catalyst demonstrated efficacy in PMS, achieving 97% degradation of MO and 98% degradation of RhB within 30 min at an initial concentration of 20.0 mg L-1. Additionally, various factors affecting dye degradation, including PMS dosage, catalyst dosage, temperature, initial pH, and coexisting anions, were investigated. Radical quenching experiments confirmed the presence of sulfate radicals (SO4˙-), hydroxyl radicals (HO˙), superoxide radicals (O2˙-), and singlet oxygen (1O2) in the system. After four cycles, CUST-565 retained its ability to catalytically degrade approximately 80% of the pollutants. These observed stability and reusability properties, corroborated by a series of characterization analyses before and after use, suggest that CUST-565 exhibits reliable performance. This work contributes to the development of cobalt-PMS catalysts for efficiently degrading dyes in wastewater.

Cobalt nanoparticle-catalysed N-alkylation of amides with alcohols

A protocol for efficient N-alkylation of benzamides with alcohols in the presence of cobalt-nanocatalysts is described. Key to the success of this general methodology is the use of highly dispersed cobalt nanoparticles supported on carbon, which are obtained from the pyrolysis of cobalt(ii) acetate and o-phenylenediamine as a ligand at suitable temperatures. The catalytic material shows a broad substrate scope and good tolerance to functional groups. Apart from the synthesis of a variety of secondary amides (>45 products), the catalyst allows for the conversion of more challenging aliphatic alcohols and amides, including biobased and macromolecular amides. The practical applicability of the catalyst is underlined by the successful recycling and reusability.

3D Oxide-Derived Ru Catalyst for Ultra-Efficient Hydrogenation of Levulinic Acid to γ-Valerolactone

γ-valerolactone (GVL) is a key value-added chemical catalytically produced from levulinic acid (LA), an important biomass derivative platform chemical. Here an ultra-efficient 3D Ru catalyst generated by in situ reduction of RuZnOx nanoboxes is reported; the catalyst features a well-defined structure of highly dispersed in situ oxide-derived Ru (IOD-Ru) clusters (≈1 nm in size) spatially confined within the 3D nanocages with rich mesopores, which guarantees a maximized atom utilization with a high exposure of Ru active sites as well as a 3D accessibility for substrate molecules. The IOD-Ru exhibits ultrahigh performance for the hydrogenation of LA into GVL with a record-breaking turnover frequency (TOF) up to 59400 h-1 , 14 times higher than that of the ex situ reduction of RuZnOx nanoboxes catalyst. Structural characterizations and theoretical calculations collectively indicate that the defect-rich and coordination-unsaturated IOD-Ru sites can boost the activation of the carbonyl group in LA with a significantly lowered energy barrier of hydrogenation.

A Two-dimensional Metal-Organic Framework as Promising Cathode for Advanced Lithium Storage

Anthraquinone electrode materials are promising candidates for lithium-ion batteries (LIBs) due to the abundance of anthraquinone and the high theoretical capacity, and good reversibility of the anthraquinone electrodes. However, the active anthraquinone materials are soluble in organic electrolytes, resulting in a sharp decay of capacity during the charge and discharge processes. Herein, we report on a two-dimensional calcium anthraquinone 2,3-dicarboxy metal-organic framework (2D CaAQDC MOF) fabricated using a simple hydrothermal method. The 2D CaAQDC MOF not only effectively inhibits the dissolution of active electrode substances into the electrolyte, but also promotes the diffusion of lithium ion into the pores of the MOF. When used as a cathode for the LIBs, the resulting CaAQDC electrode delivers a high specific capacity of ~100 mAh g-1 at a current density of 50 mA g-1 after 200 cycles, demonstrating its good cycle stability. Even at a high current density of 200 mA g-1 , the CaAQDC electrode exhibits a specific capacity of ~60 mAh g-1 . The fabricated 2D coordination polymers effectively restrains the dissolution of anthraquinone into the organic electrolyte and enhances the structural stability, which greatly improves the electrochemical performance of anthraquinone. These research results offer a rational molecular design strategy to address the dissolution of this and other active organic electrode materials.

Recent progress of MOF-functionalized nanocomposites: From structure to properties

Metal-organic frameworks (MOFs) are novel crystalline porous materials assembled from metal ions and organic ligands. The adaptability of their design and the fine-tuning of the pore structures make them stand out in porous materials. Furthermore, by integrating MOF guest functional materials with other hosts, the novel composites have synergistic benefits in numerous fields such as batteries, supercapacitors, catalysis, gas storage and separation, sensors, and drug delivery. This article starts by examining the structural relationship between the host and guest materials, providing a comprehensive overview of the research advancements in various types of MOF-functionalized composites reported to date. The review focuses specifically on four types of spatial structures, including MOFs being (1) embedded in nanopores, (2) immobilized on surface, (3) coated as shells and (4) assembled into hybrids. In addition, specific design ideas for these four MOF-based composites are presented. Some of them involve in situ synthesis method, solvothermal method, etc. The specific properties and applications of these materials are also mentioned. Finally, a brief summary of the advantages of these four types of MOF composites is given. Hopefully, this article will help researchers in the design of MOF composite structures.

Laser-Assisted Design of MOF-Derivative Platforms from Nano- to Centimeter Scales for Photonic and Catalytic Applications

Laser conversion of metal-organic frameworks (MOFs) has recently emerged as a fast and low-energy consumptive approach to create scalable MOF derivatives for catalysis, energy, and optics. However, due to the virtually unlimited MOF structures and tunable laser parameters, the results of their interaction are unpredictable and poorly controlled. Here, we experimentally base a general approach to create nano- to centimeter-scale MOF derivatives with the desired nonlinear optical and catalytic properties. Five three- and two-dimensional MOFs, differing in chemical composition, topology, and thermal resistance, have been selected as precursors. Tuning the laser parameters (i.e., pulse duration from fs to ns and repetition rate from kHz to MHz), we switch between ultrafast nonthermal destruction and thermal decomposition of MOFs. We have established that regardless of the chemical composition and MOF topology, the tuning of the laser parameters allows obtaining a series of structurally different derivatives, and the transition from femtosecond to nanosecond laser regimes ensures the scaling of the derivatives from nano- to centimeter scales. Herein, the thermal resistance of MOFs affects the structure and chemical composition of the resulting derivatives. Finally, we outline the "laser parameters versus MOF structure" space, in which one can create the desired and scalable platforms with nonlinear optical properties from photoluminescence to light control and enhanced catalytic activity.

Ni-Rh-based bimetallic conductive MOF as a high-performance electrocatalyst for the oxygen evolution reaction

Metal-organic frameworks (MOFs) have recently been considered the promising catalysts due to their merits of abundant metal sites, versatile coordination groups, and tunable porous structure. However, low electronic conductivity of most MOFs obstructs their direct application in electrocatalysis. In this work, we fabricate an Ni-Rh bimetallic conductive MOF ([Ni2.85Rh0.15(HHTP)2]n/CC) grown in situ on carbon cloth. Abundant nanopores in the conductive MOFs expose additional catalytic active sites, and the advantageous 2D π-conjugated structure helps accelerate charge transfer. Owing to the introduction of Rh, [Ni2.85Rh0.15(HHTP)2]n/CC exhibited substantially improved oxygen evolution reaction (OER) activity and exhibited only an overpotential of 320 mV to achieve the current density of 20 mA cm-2. The remarkable OER performance confirmed by the electrochemical tests could be ascribed to the synergistic effect caused by the doped Rh together with Ni in [Ni2.85Rh0.15(HHTP)2]n/CC, thereby exhibiting outstanding electrocatalytic performance.

Effective construction of a CuCo MOF@graphene functional electrocatalyst for hydrogen evolution reaction

Electrochemical water splitting is considered a green and sustainable method of producing hydrogen energy. Herein, to pursue a highly efficient hydrogen evolution reaction, we fabricated high-performance electrocatalysts, by utilizing a bimetallic (Cu and Co) metal-organic framework to modify rGO through a one-step in situ approach. The synthesized CuCoOC@rGO presents a highly ordered structure with a defect-rich porous surface for the hydrogen evolution reaction (HER). Specifically, the appropriate adjustment of metal (Cu and Co), 1,3,5-benzenetricarboxylic acid (H3BTC), and rGO ratios leads to a well-defined morphology, which creates a defect-rich porous surface. Characterized by XRD, SEM, EDS, FT-IR spectroscopy, Raman spectroscopy, XPS, and BET, the morphology exposes more active sites, strong evidence for the promotion of electrocatalytic efficiency. Upon the analysis of the experimental data, the obtained CuCoOC@rGO catalyst exhibits excellent activity in alkaline media with a low overpotential of 120 mV at a current density of 10 mA cm-2, and a Tafel slope of 124 mV dec-1 for the hydrogen evolution reaction (HER). Guided by the structure-activity relationship, the superior HER activity of CuCoOC@rGO in alkaline electrolyte could originate from many sources, including: (1) as a self-supported substrate, CuCoOC@rGO not only leads to profitable electrical contact and mechanical stability but also firmly roots into the rGO without extra binders. (2) The highly ordered structure provides smooth ion and electron transport channels, which are conducive to electrolyte infiltration and gas release. (3) The abundance of defective pores on the surface of the nanoarrays, which offers more active sites for the catalytic process. This study provides new prospects for the rational design and fabrication of advanced hierarchical functional electrocatalysts for application in electrochemical energy devices.

Stannate-Based Materials as Anodes in Lithium-Ion and Sodium-Ion Batteries: A Review

Binary metal oxide stannate (M₂SnO₄; M = Zn, Mn, Co, etc.) structures, with their high theoretical capacity, superior lithium storage mechanism and suitable operating voltage, as well as their dual suitability for lithium-ion batteries (LIBs) and sodium-ion batteries (SIBs), are strong candidates for next-generation anode materials. However, the capacity deterioration caused by the severe volume expansion problem during the insertion/extraction of lithium or sodium ions during cycling of M₂SnO₄-based anode materials is difficult to avoid, which greatly affects their practical applications. Strategies often employed by researchers to address this problem include nanosizing the material size, designing suitable structures, doping with carbon materials and heteroatoms, metal-organic framework (MOF) derivation and constructing heterostructures. In this paper, the advantages and issues of M₂SnO₄-based materials are analyzed, and the strategies to solve the issues are discussed in order to promote the theoretical work and practical application of M₂SnO₄-based anode materials.

Influence of ZIF-9 and ZIF-12 structure on the formation of a series of new Co/N-doped porous carbon composites as anode electrodes for high-performance lithium-ion batteries

A series of new Co/N-doped porous carbon composites, denoted as Co/CZIF-9 and Co/CZIF-12, containing Co nanoparticles encapsulated in nitrogen-doped carbon matrices were prepared by annealing Co-based zeolite imidazolate framework materials, ZIF-9 and ZIF-12, as the efficient precursors at different temperatures. The structural features of the as-synthesized composites at 900 °C were determined by analytical methods with high reliability. Consequently, Co/CZIF-12_900 exhibits a high first specific discharge capacity of 971.0 mA h g^-1 at a current density of 0.1 A g^-1. Notably, the specific discharge/charge capacity of Co/CZIF-12_900 reaches about 508.8 mA h g^-1 at 0.1 A g^-1 after 100 cycles. The outstanding behaviors can be accounted for by the efficient incorporation of hetero-nitrogen doping and the Co nanoparticles within the layered structure of porous carbon, enhancing electrical conductivity and structural stability and limiting volume change during the intercalation/deintercalation of Li⁺ ions. These findings suggest that the Co/CZIF-12_900 material could be employed as a promising anode electrode for energy storage products.

Applications of Metal-Organic Frameworks and Their Derivatives in Electrochemical CO2 Reduction

Electrochemically reducing CO2 to more reduced chemical species is a promising way that not only enables the conversion of intermittent energy resources to stable fuels, but also helps to build a closed-loop anthropogenic carbon cycle. Among various electrocatalysts for electrochemical CO2 reduction, multifunctional metal-organic frameworks (MOFs) have been employed as highly efficient and selective heterogeneous electrocatalysts due to their ultrahigh porosity and topologically diverse structures. Up to now, great progress has been achieved in the design and synthesis of highly active and selective MOF-related catalysts for electrochemical CO2 reduction reaction (CO2RR), and their corresponding reaction mechanisms have been thoroughly studied. In this review, we summarize the recent progress of applying MOFs and their derivatives in CO2RR, with a focus on the design strategies for electrocatalysts and electrolyzers. We first discussed the reaction mechanisms for different CO2RR products and introduced the commonly applied electrolyzer configurations in the current CO2RR system. Then, an overview of several categories of products (CO, HCOOH, CH4, CH3OH, and multi-carbon chemicals) generated from MOFs or their derivatives via CO2RR was discussed. Finally, we offer some insights and perspectives for the future development of MOFs and their derivatives in electrochemical CO2 reduction. We aim to provide new insights into this field and further guide future research for large-scale applications.

MOFs Containing Solid-State Electrolytes for Batteries

The use of metal-organic frameworks (MOFs) in solid-state electrolytes (SSEs) has been a very attractive research area that has received widespread attention in the modern world. SSEs can be divided into different types, some of which can be combined with MOFs to improve the electrochemical performance of the batteries by taking advantage of the high surface area and high porosity of MOFs. However, it also faces many serious problems and challenges. In this review, different types of SSEs are classified and the changes in these electrolytes after the addition of MOFs are described. Afterward, these SSEs with MOFs attached are introduced for different types of battery applications and the effects of these SSEs combined with MOFs on the electrochemical performance of the cells are described. Finally, some challenges faced by MOFs materials in batteries applications are presented, then some solutions to the problems and development expectations of MOFs are given.

Metal Organic Framework Cubosomes

We demonstrate a general strategy for the synthesis of ordered bicontinuous-structured metal organic frameworks (MOFs) by using polymer cubosomes (PCs) with a double primitive structure (Im 3 ‾ ${\bar{3}}$ m symmetry) as the template. The filling of MOF precursors in the open channel of PCs, followed by their coordination and removal of the template, generates MOF cubosomes with a single primitive topology (Pm 3 ‾ ${\bar{3}}$ m) and average mesopore diameters of 60-65 nm. Mechanism study reveals that the formation of ZIF-8 cubosomes undergoes a new MOF growth process, which involves the formation of individual MOF seeds in the template, their growth and eventual fusion into the cubosomes. Their growth kinetics follows the Avrami equation with an Avrami exponent of n=3 and a growth rate of k=1.33×10^-4 , indicating their fast 3D heterogeneous growth mode. Serving as a bioreactor, the ZIF-8 cubosomes show high loading of trypsin enzyme, leading to a high catalytic activity in the proteolysis of bovine serum albumin.

Rationally Designed Manganese-Based Metal-Organic Frameworks as Altruistic Metal Oxide Precursors for Noble Metal-Free Oxygen Reduction Reaction

The sluggish oxygen reduction reaction (ORR) at the cathode is challenging and hinders the growth of hydrogen fuel cells. Concerning kinetic values, platinum is the best known catalyst for ORR; however, its less abundance, high cost, and corrosive nature warrant the development of low-cost catalysts. We report the hydrothermal synthesis of two novel Mn-based metal-organic frameworks (MOFs), [Mn₂(DOT)(H₂O)₂]_n (Mn-SKU-1) and [Mn₂(DOT)₂(BPY)₂(THF)]_n (Mn-SKU-2) (DOT = 2,5-dihydroxyterephthalate; BPY = 4,4'-bipyridine). Mn-SKU-1 contains dimeric Mn(II) centers where the two corner-shared MnO₆ octahedra fuse to give rise to an infinite Mn₂O₁₀ cluster, whereas the two Mn(II) ions coordinate to DOT and BPY moieties to give rise to a pillared structure in Mn-SKU-2 and form a 3D → 3D homo-interpenetration MOF with a twofold interpenetrated net. The pyrolysis of as-synthesized Mn-MOFs at 600 °C under N₂ produced exclusively porous α-Mn₂O₃ composites (PSKU-1 and PSKU-2), with the BET surface area of 90.8 (for PSKU-1) and 179.3 m² g^-1 (for PSKU-2). These mesoporous MOF-derived α-Mn₂O₃ composites were modified as cathode materials for the electrocatalytic reduction of oxygen. The onset potential for the oxygen reduction reaction was found to be 0.90 V for PSKU-1 and 0.93 V for PSKU-2 versus RHE in 0.1 M KOH solution, with the current density of 4.8 and 6.0 mA cm^-2, respectively, at 1600 rpm. Based on the RDE/RRDE results, the electrocatalytic oxygen reduction occurs majorly via the four-electron process. The electrocatalyst PSKU-2 is cheap, easy to use, retains 90% of its activity after 10 h of continuous use, and offers higher recyclability than Pt/C. The onset potential maximum current density and kinetic values (J_k = 11.68 mA cm^-2 and Tafel slope = 85.0 mV dec^-1) obtained in this work are higher than the values reported for pure Mn₂O₃.

Low volume expansion hierarchical porous sulfur-doped Fe2O3@C with high-rate capability for superior lithium storage

Ingenious morphology design and doping engineering have remarkable effects on enhancing conductivity and reducing volume expansion, which need to be improved by transition metal oxides serving as anode materials for lithium-ion batteries. Herein, S_0.15-Fe₂O₃@C nano-spindles with a hierarchical porous structure are obtained by carbonizing MIL-88B@PDA and subsequent high-temperature S-doping. Kinetic analysis showed that S-doping increases capacitive contribution, enhances charge transfer capability and accelerates Li⁺ diffusion rate. Therefore, the S_0.15-Fe₂O₃@C electrode exhibits superior lithium storage performance with a remarkable specific capacity of 1014.4 mA h g^-1 at 200 mA g^-1, ultrahigh rate capability of 513.1 mA h g^-1 at 5.0 A g^-1, and excellent cycling stability of 842.3 mA h g^-1 at 1.0 A g^-1 after 500 cycles. Moreover, the size of S_0.15-Fe₂O₃@C particles barely changed after 50 cycles, indicating an extremely low volume expansion, related to the carbon shell, fine Fe₂O₃ nanoparticles, abundant voids inside, and improved kinetics. This strategy can be applied to other metal oxides for synthesizing anodes with high-rate capability and low volume expansion.

Fabrication of nanosheet-assembled hollow copper-nickel phosphide spheres embedded in reduced graphene oxide texture for hybrid supercapacitors

Owing to their metalloid characteristics with high electrical conductivity, transition metal phosphides (TMPs) have attracted considerable research attention as prospective cathodes for hybrid supercapacitors. Unfortunately, they usually exhibit low rate performance as well as poor longevity, which does not meet the demands of hybrid supercapacitors. The nanocomposite constructed from reduced graphene oxide (rGO) and TMPs with a highly porous nature can effectively overcome the above-mentioned issues, greatly widening their utilization. In this work, we fabricated nanosheet-assembled hollow copper-nickel phosphide spheres (NH-CNPSs) by the controllable phosphatizing of copper-nickel-ethylene glycol (CN-EG) precursors. Then, porous NH-CNPSs were embedded in rGO texture (NH-CNPS-rGO) to form a unique porous nanoarchitecture. The obtained NH-CNPS-rGO has several advantages benefiting as the cathode electrode, such as (i) the hollow structure as well as porous nanosheets are conducive to fast electrolyte diffusion, (ii) the electrical conductivity of NH-CNPS is further enhanced when coupled with the rGO texture, hence promoting electron transfer in the whole structure, (iii) wrapping NH-CNPSs within the rGO texture endows the nanocomposite with much better structural stability, resulting in longer durability of the electrode, And (iv) the porous structures generated in the nanocomposite provide a perfect space for reducing the mass transfer resistance and accessing the electrolyte, thereby boosting the reaction kinetics. The tests demonstrated that the optimal NH-CNPS-rGO electrode revealed a capacity of up to 1075 C g^-1, a superior rate capacity, and exceptional longevity of 94.7%. Moreover, a hybrid supercapacitor (NH-CNPS-rGO‖AC) equipped with the NH-CNPS-rGO-cathode electrode and activated carbon (AC)-anode electrode represented a satisfactory energy density of 64 W h kg^-1 at 801 W kg^-1 and amazing longevity (91.8% retention after 13 000 cycles), which endorses the promising potential of NH-CNPS-rGO for high-efficiency supercapacitors. This research showcases an appropriate method to engineer hollow TMP-rGO nanocomposites as effective materials for supercapacitors.

Porous Single Crystals at the Macroscale: From Growth to Application

ConspectusPorous materials have wide applications in the fields of catalysis, separation, and energy conversion and storage. Porous materials contain pores that are specifically designed to achieve expectant performance. The solid phases in porous materials are normally completely continuous to form the basic porous frame while the pores are fluid phase within the solid phase. Single crystals are macroscopic materials in three spatial dimensions with the constituent atoms, ions, molecules, or molecular assemblies arranged in an orderly repeating pattern with the ordered structures. The growth of single crystals is indeed a process to arrange these constituents in three dimensions into a repeating pattern within the materials. Today the applications of single crystals are exponentially growing in wide fields, and single crystals are therefore unacknowledged as the pillars of our modern technology. Introducing porosity into single crystals would be expected to create a new kind of porous material in which the basic porous frames are single-crystalline and free of grain boundaries. The structural symmetry is completely maintained within the basic porous frames which are a continuous solid phase, but it is completely lost inside the pores. The porous architecture is free of grain boundaries, and the fully interconnected skeletons are in single-crystalline states within the basic porous frames. Single crystals with porosities can therefore be considered to be a new kind of porous material, but they are single-crystal-like because the structural symmetry is maintained only in the skeletons and completely lost within the pores. We therefore call them porous single crystals or consider them in porous single-crystalline states to stand out with their structural features. Porous single crystals at the macroscale combine the advantages of porous materials and single crystals to incorporate both porosity and structural coherence in a porous architecture, leading to invaluable opportunities to alter the material's properties by controlling the unique structural features to enhance its performance. However, the growth of single crystals in three dimensions reduces the formation of porosities, leading to a fundamental challenge for introducing porosity into single crystals in a traditional process of crystal growth. In this Account, we report the rational design, growth methodology, and microstructural engineering of porous single crystals in a solid-solid transformation. We rationally design a high-density mother phase in a single-crystalline state and transform it into a low-density new phase in a single-crystalline state to introduce porosities into single crystals even incorporating the removal of specific compositions from the mother phase during the growth of porous single crystals. The porosity can be tailored by controlling the change in relative densities from the mother phase to the porous single crystals while the pore size can be engineered by controlling the fabrication conditions. Considering the unique structural features, we explore their functionalities and applications in photoelectrochemical energy conversion, electrochemical alkane conversion, and electrochemical energy storage. We believe that the materials, if tailored into porous single-crystalline states, would not only find a broad range of applications in other fields but also enable a new path for material innovations.

Metal-organic frameworks and their derivatives for metal-ion (Li, Na, K and Zn) hybrid capacitors

Metal-ion hybrid capacitors (MIHCs) hold particular promise for next-generation energy storage technologies, which bridge the gap between the high energy density of conventional batteries and the high power density and long lifespan of supercapacitors (SCs). However, the achieved electrochemical performance of available MIHCs is still far from practical requirements. This is primarily attributed to the mismatch in capacity and reaction kinetics between the cathode and anode. In this regard, metal-organic frameworks (MOFs) and their derivatives offer great opportunities for high-performance MIHCs due to their high specific surface area, high porosity, topological diversity, and designable functional sites. In this review, instead of simply enumerating, we critically summarize the recent progress of MOFs and their derivatives in MIHCs (Li, Na, K, and Zn), while emphasizing the relationship between the structure/composition and electrochemical performance. In addition, existing issues and some representative design strategies are highlighted to inspire breaking through existing limitations. Finally, a brief conclusion and outlook are presented, along with current challenges and future opportunities for MOFs and their derivatives in MIHCs.

Zeolite Imidazolate Frameworks (ZIFs) Derived Nanomaterials and their Hybrids for Advanced Secondary Batteries and Electrocatalysis

Zeolite imidazolate frameworks (ZIFs), as a typical class of metal-organic frameworks (MOFs), have attracted a great deal of attention in the field of energy storage and conversation due to their chemical structure stability, facile synthesis and environmental friendliness. Among of ZIFs family, the zinc-based imidazolate framework (ZIF-8) and cobalt-based imidazolate framework (ZIF-67) have considered as promising ZIFs materials, which attributed to their tunable porosity, stable structure, and desirable electrical conductivity. To date, various ZIF-8 and ZIF67 derived materials, including carbon materials, metal oxides, sulfides, selenides, carbides and phosphides, have been successfully synthesized using ZIFs as templates and evaluated as promising electrode materials for secondary batteries and electrocatalysis. This review provides an effective guide for the comprehension of the performance optimization and application prospects of ZIFs derivatives, specifically focusing on the optimization of structure and their application in secondary batteries and electrocatalysis. In detail, we present recent advances in the improvement of electrochemical performance of ZIF-8, ZIF-67 and ZIF-8@ZIF-67 derived nanomaterials and their hybrids, including carbon materials, metal oxides, carbides, oxides, sulfides, selenides, and phosphides for high-performance secondary batteries and electrocatalysis.

The synthesis of CoS/MnCo2O4-MnO2 nanocomposites for supercapacitors and energy-saving H2 production

In this study, CoS/MnCo₂O₄-MnO₂ (CMM) nanocomposites were synthesized by hydrothermal and then electrochemical deposition. Their electrochemical properties were systematically investigated for supercapacitors and energy-saving H₂ production. As an electrode material for supercapacitor, CMM demonstrates a specific capacitance of 2320F g^-1 at 1 A/g, and maintains a specific capacitance of 1216F g^-1 at 10 A/g. It also shows 72.8 % capacitance retention after 8000 cycles. The aqueous asymmetric supercapacitor exhibited high energy storage capacity (887.86F g^-1 specific capacitance at a current density of 1 A/g), good rate performance and cycling stability. Besides, CMM shows outstanding urea oxidation reaction(UOR) and glycol oxidation reaction (MOR) performances for H₂ production. Compared to oxygen evolution reaction (OER) (1.635 V) at 20 mA cm^-2, the potentials were reduced by 213 mV for UOR and 233 mV for MOR, respectively. Therefore, this study shows the promising practical applications of CMM nanocomposites for energy storage and energy-saving H₂ production.

Metal-organic framework (MOF) composites as promising materials for energy storage applications

Metal-organic framework (MOF) composites are considered to be one of the most vital energy storage materials due to their advantages of high porousness, multifunction, various structures and controllable chemical compositions, which provide a great possibility to find suitable electrode materials for batteries and supercapacitors. However, MOF composites are still in the face of various challenges and difficulties that hinder their practical application. In this review, we introduce and summarize the applications of MOF composites in batteries, covering metal-ion batteries, lithium-sulfur batteries, lithium-oxygen batteries and zinc-air batteries, as well as supercapacitors. In addition, the application challenges of MOF composites in batteries and supercapacitors are also summarized. Finally, the basic ideas and directions for further development of these two types of electrochemical energy storage devices are proposed.

Lead(II)-Azido Metal–Organic Coordination Polymers: Synthesis, Structure and Application in PbO Nanomaterials Preparation

The current study aims to explain recent developments in the synthesis of Pb(II)-azido metal-organic coordination polymers. Coordination polymers are defined as hybrid materials encompassing metal-ion-based, organic linkers, vertices, and ligands, serving to link the vertices to 1D, 2D, or 3D periodic configurations. The coordination polymers have many applications and potential properties in many research fields, primarily dependent on particular host–guest interactions. Metal coordination polymers (CPs) and complexes have fascinating structural topologies. Therefore, they have found numerous applications in different areas over the past two decades. Azido-bridged complexes are inorganic coordination ligands with higher fascination that have been the subject of intense research because of their coordination adaptability and magnetic diversity. Several sonochemical methods have been developed to synthesize nanostructures. Researchers have recently been interested in using ultrasound in organic chemistry synthetics, since ultrasonic waves in liquids accelerate chemical reactions in heterogeneous and homogeneous systems. The sonochemical synthesis of lead–azide coordination compounds resulted from very fantastic morphologies, and some of these compounds are used as precursors for preparing nano lead oxide. The ultrasonic sonochemistry approach has been extensively applied in different research fields, such as medical imaging, biological cell disruption, thermoplastic welding, food processing, and waste treatment. CPs serve as appropriate precursors for preparing favorable materials at the nanoscale. Using these polymers as precursors is beneficial for preparing inorganic nanomaterials such as metal oxides.

Unraveling timescale-dependent Fe-MOFs crystal evolution for catalytic ozonation reactivity modulation

Iron-based metal-organic frameworks (Fe-MOFs) have been considered competitive catalyst candidates for the effective degradation of organic pollutants via advanced oxidation processes (AOPs) due to their unique porous architecture and tunable active site structure. However, little is known about the role of synergetic relationship between porous architecture and active site exposure of Fe-MOFs on catalysis for AOPs yet. Here, we demonstrated an overlooked compromise over these two features on modulating the catalytic ozonation reactivity of MIL-53(Fe) through a timescale-dependent crystal evolution. Enabled by intramolecular hydrogen bonds, the MIL-53(Fe) was subjected to six evolution steps in terms of crystal morphology, leading to a volcano plot of catalytic ozonation reactivity for Rhodamine B (RhB) degradation versus the crystallization time. Evidence suggested that the surface area of MIL-53(Fe) decreased dramatically, while the density of accessible active site increased when prolonging crystallization time, allowing for the facile modulation of catalytic ozonation reactivity of MIL-53(Fe). Electron paramagnetic resonance and fluorescence quantification tests verified that the screened MIL-53(Fe)s had a much better capacity for ∙OH generation than benchmark ozonation catalyst α-MnO₂ and α-FeOOH. Moreover, the MIL-53(Fe) with the highest reactivity (i.e., MIL-53(Fe)-18H) could effectively destruct a broad spectrum of emerging and refractory organic pollutants and allow the thorough purification of secondary effluents discharged from textile dyeing & finishing industry for in situ reuse. Therefore, our study advances the understanding of the compromise effect between porous architecture and active site on catalysis reactivity of Fe-MOFs and promotes the rational design of more effective Fe-MOFs as well as their derivatives for environmental applications.

Portable metal-organic framework alginate beads for high-sensitivity fluorescence detection and effective removal of residual pesticides in fruits and vegetables

Pesticides have been emerged as major organic pollutants in environment, owing to widely spread and intrinsic high toxicity in agricultural productivity. Herein, we designed and synthesized a practicability and portable metal-organic framework (MOF) based composite beads MOF-alginate-Ca²⁺-polyacrylic acid (kgd-M1@ACPs) consist of biocompatible host material (sodium alginate) and fluorescent center with blue emission (where kgd-M1 stands for {[Cd(tbia)·H₂O]·2H₂O}_n), which was further developed for high-efficiency and naked-eye 2,6-dichloro-4-nitroaniline (DCN) monitoring in fruits and vegetables. Significantly, the kgd-M1@ACPs shows obvious fluorescent quench towards toxic pesticide DCN with a low limit of detection (LOD) of 0.09 μM and high recovery from 98.08 to 104.37%. Moreover, the kgd-M1@ACPs also presents an excellent DCN adsorption ability. This work demonstrates that smart material kgd-M1@ACPs is expected to be a good candidate for detection and removal of DCN in real fruits and vegetables, which will present a broad prospect for monitoring and treating pesticides.

Freestanding Metal-Organic Frameworks and Their Derivatives: An Emerging Platform for Electrochemical Energy Storage and Conversion

Metal–organic frameworks (MOFs) have recently emerged as ideal electrode materials and precursors for electrochemical energy storage and conversion (EESC) owing to their large specific surface areas, highly tunable porosities, abundant active sites, and diversified choices of metal nodes and organic linkers. Both MOF-based and MOF-derived materials in powder form have been widely investigated in relation to their synthesis methods, structure and morphology controls, and performance advantages in targeted applications. However, to engage them for energy applications, both binders and additives would be required to form postprocessed electrodes, fundamentally eliminating some of the active sites and thus degrading the superior effects of the MOF-based/derived materials. The advancement of freestanding electrodes provides a new promising platform for MOF-based/derived materials in EESC thanks to their apparent merits, including fast electron/charge transmission and seamless contact between active materials and current collectors. Benefiting from the synergistic effect of freestanding structures and MOF-based/derived materials, outstanding electrochemical performance in EESC can be achieved, stimulating the increasing enthusiasm in recent years. This review provides a timely and comprehensive overview on the structural features and fabrication techniques of freestanding MOF-based/derived electrodes. Then, the latest advances in freestanding MOF-based/derived electrodes are summarized from electrochemical energy storage devices to electrocatalysis. Finally, insights into the currently faced challenges and further perspectives on these feasible solutions of freestanding MOF-based/derived electrodes for EESC are discussed, aiming at providing a new set of guidance to promote their further development in scale-up production and commercial applications.

Critical Review, Recent Updates on Zeolitic Imidazolate Framework-67 (ZIF-67) and Its Derivatives for Electrochemical Water Splitting

Design and construction of low-cost electrocatalysts with high catalytic activity and long-term stability is a challenging task in the field of catalysis. Metal-organic frameworks (MOF) are promising candidates as precursor materials in the development of highly efficient electrocatalysts for energy conversion and storage applications. This review starts with a summary of basic concepts and key evaluation parameters involved in the electrochemical water-splitting reaction. Then, different synthesis approaches reported for the cobalt-based Zeolitic imidazolate framework (ZIF-67) and its derivatives are critically reviewed. Additionally, several strategies employed to enhance the electrocatalytic activity and stability of ZIF-67-based electrocatalysts are discussed in detail. The present review provides a succinct insight into the ZIF-67 and its derivatives (oxides, hydroxides, sulfides, selenides, phosphide, nitrides, telluride, heteroatom/metal-doped carbon, noble metal-supported ZIF-67 derivatives) reported for oxygen evolution reaction (OER), hydrogen evolution reaction (HER), and overall water splitting applications. Finally, this review concludes with the associated challenges and the perspectives on developing the best economic, durable electrocatalytic materials.

Self-supported metal-organic framework-based nanostructures as binder-free electrodes for supercapacitors

Metal-organic frameworks (MOFs), an interesting class of functional inorganic materials, have recently emerged as suitable electrode materials or templates/precursors of electrode materials for supercapacitors (SCs). The key in utilizing MOF-based electrode materials is to address the low electronic conductivity and poor stability issues. Therefore, the rational design and fabrication of self-supported binder-free electrodes is considered the most promising strategy to address these challenges. In this review, we summarize the recent advances in the design and manufacture of self-supported MOF-based nanostructures and their use as binderless electrodes for SCs, especially over the last five years. The synthesis strategies for constructing pristine MOFs, MOF composites and MOF derivative arrays are overviewed. By highlighting the advantages and challenges of each class of electrode materials, we hope that this review will provide some insights into the rational design of MOF-based electrode materials to promote the future development of this highly exciting field.

Tuning Phase Structure of Nickel-Ruthenium Alloys via MOFs In Situ Hydrolysis toward Enhanced Hydrogen Evolution Performance in Alkaline

Metal organic frameworks (MOFs) and corresponding derivatives have attracted wide attention. As electrocatalysts, these derivatives (metal, metal compound, and associated composites) have a wide range of application in water-splitting devices, fuel cells, and other hydrogen-related technologies. However, with the exception of pyrolysis, limited studies have documented generated metal nanoparticles from MOFs hydrolysis reactions. Herein, NiRu dual-phase alloy nanoparticles are synthesized via in situ MOFs hydrolysis mediating solvothermal reduction reaction. The hcp-phase NiRu alloys can be rationally tuned by modulating experimental parameters of feeding metal ratio and reaction time. The volcanic link between hydrogen evolution reaction activity and the descriptor of d band center is investigated using experimentally determined valence bands. Furthermore, compared with fcc-phase NiRu alloys, it is theoretically revealed that hcp-phase NiRu alloys optimize d band structure and have a lower energy barrier. This finding broadens the range of application for MOFs hydrolysis reactions and highlights advantages of metal alloys manufactured from MOFs hydrolysis reactions.

Modulating the Chemical Microenvironment of Pt Nanoparticles within Ultrathin Nanosheets of Isoreticular MOFs for Enhanced Catalytic Activity

The catalytic activity of metal nanoparticles (MNPs) embedded in metal-organic frameworks (MOFs) is affected by the electronic interactions between MNPs and MOFs. In this report, we fabricate a series of ultrathin nanosheets of isoreticular MOFs (NMOFs) with different metal nodes as supports and successfully encapsulate Pt NPs within these NMOFs, affording Pt@NMOF-Co, Pt@NMOF-Ni₁Co₁, Pt@NMOF-Ni₃Co₁, and Pt@NMOF-Ni nanocomposites. The microchemical environment on the surface of Pt NPs can be modulated by varying the metal nodes of NMOFs. The catalytic activity of the nanocomposites toward liquid-phase hydrogenation of 1-hexene shows obvious difference, in which Pt@NMOF-Ni possesses the highest activity followed by Pt@NMOF-Ni₃Co₁, Pt@NMOF-Ni₁Co₁, and Pt@NMOF-Co in a decreasing order of activity. Obviously, increasing gradually the amount of Ni²⁺ nodes in the carriers can improve the catalytic activity. The difference of catalytic activity of the nanocomposites might originate from the distinct electron interactions between Pt NPs and NMOFs, as ascertained by X-ray photoelectron spectroscopy spectrum and density functional theory calculations. This work provides a rare example that the catalytic activity of MNPs could be controlled by accurately regulating the microchemical environment using ultrathin NMOFs as supports.

Micro/macrostructure and multicomponent design of catalysts by MOF-derived strategy: Opportunities for the application of nanomaterials-based advanced oxidation processes in wastewater treatment

Advanced oxidation processes (AOPs) have demonstrated an effective wastewater treatment method. But the application of AOPs using nanomaterials as catalysts is challenged with a series of problems, including limited mass transfer, surface fouling, poor stability, and difficult recycling. Recently, metal-organic frameworks (MOFs) with high tunability and ultrahigh porosity are emerging as excellent precursors for the delicate design of the structure/composition of catalysts and many MOF-derived catalysts with distinct physicochemical characteristics have shown optimized performance in various AOPs. Herein, to elucidate the structure-composition-performance relationship, a review on the performance optimization of MOF-derived catalysts to overcome the existing problems in AOPs by micro/macrostructure and multicomponent design is given. Impressively, MOF-derived strategy for the design of catalyst materials from the aspects of microstructure, macrostructure, and multicomponent (polymetallic, heteroatom doping, M/C hybrids, etc.) is firstly presented. Moreover, important advances of MOF-derived catalysts in the application of various AOPs (Fenton, persulfate-based AOPs, photocatalysis, electrochemical processes, hybrid AOPs) are summarized. The relationship between the unique micro/macrostructure and/or multicomponent features and performance optimization in mass transfer, catalytic efficiency, stability, and recyclability is clarified. Furthermore, the challenges and future work directions for the practical application of MOF-derived catalysts in AOPs for wastewater treatment are provided.

Conductive bimetal organic framework nanorods decorated with highly dispersed Co3O4nanoparticles as bi-functional electrocatalyst

The poor electronic conductivity and low intrinsic electrocatalytic activity of metal organic frameworks (MOFs) greatly limit their direct application in electrocatalytic reactions. Herein, we report a conductive two-dimensionalπ-dconjugated Ni and Co bimetal organic framework (MOF)-NiCo-(2,3,6,7,10,11-hexaiminotriphenylene) (NiCo-HITP) nanorods decorated with highly dispersed Co₃O₄nanoparticles (NPs) as a promising bi-functional electrocatalyst towards oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) through an effective and facile strategy by modifying the rod-shaped -Ni₃HITP₂crystals using cobalt ions. The triggered electrocatalytic activity of the resulting MOF-based materials was achieved by increasing the electrical conductivity (7.23 S cm^-1) originated from Ni₃HITP₂substrate and also by creating the cooperative catalysis sites of Co-N_xand Co₃O₄NPs. Optimized syntheses show a promising ORR activity with a high half-wave potential (0.77 V) and also a significantly improved OER activity compared with pure Ni₃HITP₂in alkaline electrolyte. Furthermore, a rechargeable Zn-air battery using the as-prepared material as air-cathode also shows a high power density (143.1 mW cm^-2)-even comparable to a commercial Pt/C-RuO₂-based battery. This methodology offers a new prospect in the design and synthesis of non-carbonized MOF bi-functional electrocatalysts for efficient catalysis towards ORR and OER.