Narrow-disperse or monodisperse crosslinked and functional core–shell polymer particles prepared by two-stage precipitation polymerization

Precipitation Polymerization: A Powerful Tool for Preparation of Uniform Polymer Particles

Precipitation polymerization (PP) is a powerful tool to prepare various types of uniform polymer particles owing to its outstanding advantages of easy operation and the absence of any surfactant. Several PP approaches have been developed up to now, including traditional thermo-induced precipitation polymerization (TRPP), distillation precipitation polymerization (DPP), reflux precipitation polymerization (RPP), photoinduced precipitation polymerization (PPP), solvothermal precipitation polymerization (SPP), controlled/‘‘living’’ radical precipitation polymerization (CRPP) and self-stabilized precipitation polymerization (2SPP). In this review, a general introduction to the categories, mechanisms, and applications of precipitation polymerization and the recent developments are presented, proving that PP has great potential to become one of the most attractive polymerization techniques in materials science and bio-medical areas.

Modular poly(ethylene glycol) scaffolds provide the ability to decouple the effects of stiffness and protein concentration on PC12 cells

This research focused on developing a modular poly(ethylene glycol) (PEG) scaffold, assembled from PEG microgels and collagen I, to provide an environment to decouple the chemical and mechanical cues within a three-dimensional scaffold. We first characterized the microgel fabrication process, examining the size, polydispersity, swelling ratio, mesh size and storage modulus of the polymer particles. The resulting microgels had a low polydispersity index, PDI=1.08, and a diameter of ~1.6 μm. The mesh size of the microgels, calculated from the swelling ratio, was 47.53 Å. Modular hydrogels (modugels) were then formed by compacting N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride/N-hydroxysuccinimidyl group-activated microgels with PEG-4arm-amine and 0, 1, 10, or 100 μg ml(-1) collagen. The stiffness (G(∗)) of the modugels was not significantly altered with the addition of collagen, allowing for modification of the chemical environment independent from the mechanical properties of the scaffold. PC12 cell aggregation increased in modugels as collagen concentrations increased and cell viability in modugels was improved over bulk PEG hydrogels. Overall, these results indicate that further exploration of modular scaffolds formed from microgels could allow for a better understanding of the relationship between the chemical and mechanical properties and cellular behavior.

Functionalization of polymer microspheres using click chemistry

We describe a new method to covalently link a wide variety of molecules to the surface of colloidal polymer microspheres using the Cu(I)-catalyzed azide-alkyne reaction, most commonly known under the class of reactions identified by the term click chemistry. The method is generic and readily applied to a spectrum of colloidal particle systems allowing surfaces to be tailored with virtually any desired functionality. To demonstrate this method, polystyrene microspheres were functionalized with two different polyethylene oxide-based polymers, and changes in hydrodynamic radii after functionalization were measured using dynamic light scattering. Control of surface functional groups was demonstrated by fluorescently labeling the colloidal microspheres using the same Cu-catalyzed azide-alkyne cycloaddition reaction.