Melt rheology and extrudate swell properties of talc filled polyethylene compounds

An experimental study of high-density polyethylene (HDPE) composites filled with talc (0-15 wt.%) was carried out to investigate the rheological properties. The apparent melt viscosity, melt density, and die-swell ratio (B) of the composites were measured at constant shear stress and constant shear rate by using a melt flow indexer and capillary rheometer. The experimental conditions were set to a temperature range from 190 to 220 °C for both apparatuses whereas a load range from 5 to 12.16 kg was selected for melt flow indexer and shear rate range from 1 to 10000 s^-1 for capillary rheometer. The initial study showed that the talc particulates did not influence the melt viscosity compared with the neat HDPE but decreased the elasticity of the polymer system. The HDPE/talc systems obeyed power-law model in shear stress-shear rate variations and were shear thinning, meanwhile, the die-swell increased with an increased wall shear rate and shear stress. The melt density of the composites increased linearly with an increase of the filler weight fraction and decreased with the increase of the testing temperature. The talc-HDPE composites showed compressible in the molten state.

Design and Synthesis of Polysiloxane Based Side Chain Liquid Crystal Polymer for Improving the Processability and Toughness of Magnesium Hydrate/Linear Low-Density Polyethylene Composites

In this study, a polysiloxane grafted by thermotropic liquid crystal polymer (PSCTLCP) is designed and synthesized to effectively improve the processability and toughness of magnesium hydroxide (MH)/linear low-density polyethylene (LLDPE) composites. The obtained PSCTLCP is a nematic liquid crystal polymer; the liquid crystal phase exists in a temperature range of 170 to 275 °C, and its initial thermal decomposition temperature is as high as 279.6 °C, which matches the processing temperature of MH/LLDPE composites. With the increase of PSCTLCP loading, the balance melt torque of MH/LLDPE/PSCTLCP composites is gradually decreased by 42% at 5 wt % PSCTLCP loading. Moreover, the power law index of MH/LLDPE/PSCTLCP composite melt is smaller than 1, but gradually increased with PSCTLCP, the flowing activation energy of PSCTLCP-1.0 is lower than that of MH/LLDPE at the same shear rate, indicating that the sensitivity of apparent melt viscosity of the composites to shear rate and to temperature is decreased with the increase of PSCTLCP, and the processing window is broadened by the addition of PSCTLCP. Besides, the elongation at break of MH/LLDPE/PSCTLCP composites increases from 6.85% of the baseline MH/LLDPE to 17.66% at 3 wt % PSCTLCP loading. All the results indicate that PSCTLCP can significantly improve the processability and toughness of MH/LLDPE composites.