Biomaterial composed of chitosan, riboflavin, and hydroxyapatite for bone tissue regeneration

Biomaterial engineering approaches involve using a combination of miscellaneous bioactive molecules which may promote cell proliferation and, thus, form a scaffold with the environment that favors the regeneration process. Chitosan, a naturally occurring biodegradable polymer, possess some essential features, i.e., biodegradability, biocompatibility, and in the solid phase good porosity, which may contribute to promote cell adhesion. Moreover, doping of the materials with other biocompounds will create a unique and multifunctional scaffold that will be useful in regenerative medicine. This study is focused on the manufacturing and characterization of composite materials based on chitosan, hydroxyapatite, and riboflavin. The resulting films were fabricated by the casting/solvent evaporation method. Morphological and spectroscopy analyses of the films revealed a porous structure and an interconnection between chitosan and apatite. The composite material showed an inhibitory effect on Staphylococcus aureus and exhibited higher antioxidant activity compared to pure chitosan. In vitro studies on riboflavin showed increased cell proliferation and migration of fibroblasts and osteosarcoma cells, thus demonstrating their potential for bone tissue engineering applications.

In Situ Crystallization of Hydroxyapatite on Carboxymethyl Cellulose as a Biomimetic Approach to Biomass-Derived Composite Materials

Nanohydroxyapatite (HAP) was crystallized in an aqueous solution of carboxymethyl cellulose (CMC) to prepare the composites of CMC and HAP with a stable interface between them with the aim of developing a sustainable tough biomass composite material inspired by bone. The temperature (room temperature to 90 °C) and the concentration of CMC (0.83-13.2 g/L) were optimized for the mechanical properties of the composites. The composite containing 67 wt % HAP prepared at 50 °C in the presence of 9.9 g/L CMC exhibited the largest flexural strength of 113 ± 2 MPa and the elastic modulus of 7.7 ± 0.3 GPa. X-ray diffraction showed that nanometer-sized HAP crystals were formed with a large aspect ratio, and energy-dispersive X-ray spectroscopy and infrared spectroscopy revealed that CMC was bound to the surface of HAP through an ionic interaction between Ca²⁺ and COO^-. Since the composite has a higher flexural strength than polyamide 6 (92 MPa) and a higher elastic modulus than polyamide 6 with 40 wt % glass fiber (5.5 GPa), it can be used as new tough biomass composite material to replace petroleum-derived engineering plastics.

Nanotechnological Applications Hold a Pivotal Position in Boosting Stem Cells Osteogenic Activity: In Vitro and In Vivo Studies

This approach was constructed to appraise the therapeutic effectiveness of a single i.v. dose of osteoblasts generated from co-culturing BM-MSCs with nano-HA, Pt-NPs, or Pt-HA-nanocomposite in osteoporotic rats. MSCs were grown, propagated in culture, and characterized. The effect of the suggested nanoplatforms on the survival, osteogenic differentiation, and mineralization of BM-MSCs was assessed by MTT assay, real-time PCR analysis, and Alizarin red S staining, respectively. Thereafter, the generated osteoblasts were employed for the treatment of ovariectomized rats. Our results revealed that the selected nanoplatforms upregulate the expression of osteogenic differentiation related genes (Runx-2 and BMP-2) significantly and enhance calcium deposition in BM-MSCs after 7 and 21 days, respectively, whereas the in vivo study validated that the infusion of the generated osteoblasts considerably downturn serum BALP, BSP, and SOST levels; upswing OSX level; and regain femur bone mineralization and histoarchitecture. Conclusively, the outcomes of this work provide scientific evidence that transplanting osteoblasts derived from differentiation of BM-MSCs in the presence of nanoplatforms in ovariectomized rats restores bone remodeling balance which constitutes a new hope for the treatment of osteoporosis.

Ectopic osteogenesis and scaffold biodegradation of nano-hydroxyapatite-chitosan in a rat model

The bone-formation and scaffold-biodegradation processes have not been fully characterized. This study aimed to determine the osteogenic ability of nHA-CS osteo-induced bone marrow mesenchymal stem cell (BMSC) composites and to explore the relationship between bone formation and scaffold biodegradation. The nHA-CS osteo-induced BMSC composites (nHA-CS+cells group) and the nHA-CS scaffolds (nHA-CS group) were implanted into the femoral spatium intermusculare of SD rats. At 2, 4, 6, 8, and 12 weeks post-implantation, the rat femurs were scanned using computerized tomography (CT), and the CT values of the implants were measured and comparatively analyzed. The implants were then harvested and subjected to hematoxylin and eosin (HE) and Masson's trichrome staining, and the percentages of bone area, scaffold area and collagen area were compared between the two groups. The CT values of the implants were higher in the nHA-CS+cells group than the nHA-CS group at the same time points (P < 0.05). Histological analysis revealed that de novo bone and collagen formation in the pores of the scaffolds gradually increased from 2 weeks post-implantation in both groups and that the scaffold gradually degraded as bone formation proceeded. However, more de novo bone and collagen formation and scaffold degradation occurred in the nHA-CS+cells group than in the nHA-CS group at the same time points (P < 0.05). In conclusion, nHA-CS osteo-induced BMSC composites are promising bone tissue engineering substitutes, and osteo-induced BMSCs can significantly enhance the osteogenic ability and play an active role in the degradation of nHA-CS scaffolds on par with bone formation.

Removal of Cadmium and Lead from Aqueous Solution by Hydroxyapatite/Chitosan Hybrid Fibrous Sorbent: Kinetics and Equilibrium Studies

Hydroxyapatite (HAp)/chitosan composites were prepared by a coprecipitation method, dropping a mixture of chitosan solution and phosphoric acid solution into a calcium hydroxide solution. Using the HAp/chitosan composites prepared, HAp/chitosan hybrid fibers with various HAp contents were prepared by a wet spinning method. X-ray diffraction and scanning electron microscopy analyses revealed that HAp particles were coated onto the surface of the fiber, and the surface roughness increased with increasing the HAp contents in the fiber. In order to evaluate the heavy metal removal characteristics of the HAp/chitosan hybrid fiber, adsorption tests were conducted and the results were compared with those of bare chitosan fibers. The results showed better performance in heavy metal ion removal for the HAp/chitosan hybrid fiber than the chitosan fiber. As the HAp content in the hybrid fiber increased, the removal efficiency of heavy metal ions also increased due to the increase of the specific surface area of the HAp/chitosan hybrid fiber. Adsorption kinetic and isotherm tests revealed that Pb2+and Cd2+adsorption to the hybrid fiber follows pseudo-second-order kinetic and Langmuir-type adsorption, respectively.