Influence of mold cavity thickness on electrical, morphological and thermal properties of polypropylene/carbon micromoldings

In this work, a comparative study on the electrical conductivity (σ) and thermal properties of polypropylene (PP)/carbon microparts with different part thickness (namely, 0.85 and 0.50 mm) is reported. Two different types of carbon filler (i.e., CNT and CB) were adopted to study the efficacy of different carbon fillers in improving the σ of PP/carbon microparts. In general, the σ of 0.85 mm thickness microparts were higher than the 0.50 mm thickness microparts, regardless of the carbon filler type and testing directions. This suggested that higher shearing conditions that prevailed in the microinjection molding (μIM) process were unfavorable for the formation of intact conductive pathways in corresponding moldings, albeit the distribution of carbon fillers turned better with increasing shear rates, as confirmed by morphology observations. The thermal stability of PP/carbon microparts increased with increasing filler concentration. Moreover, the increase of thermal stability was more appreciable for CB-filled microparts which was related to the formation of a CB network structure arising from the use of Ketjenblack® EC-600JD CB that characterized by high surface area (∼1400 m2/g). Differential scanning calorimetry results showed that prior thermomechanical histories (including melt blending and μIM) experienced by the polymer melts had an influence on the thermal behavior of subsequent moldings. Also, there existed a strong shear flow-induced crystallization of polymer chains during μIM because the crystallinity of microparts was higher than that of feed materials.

Effect of Hybrid Carbon Fillers on the Electrical and Morphological Properties of Polystyrene Nanocomposites in Microinjection Molding

The effect of hybrid carbon fillers of multi-walled carbon nanotubes (CNT) and carbon black (CB) on the electrical and morphological properties of polystyrene (PS) nanocomposites were systematically investigated in microinjection molding (μIM). The polymer nanocomposites with three different filler concentrations (i.e., 3, 5 and 10 wt %) at various weight ratios of CNT/CB (100/0, 30/70, 50/50, 70/30, 0/100) were prepared by melt blending, then followed by μIM under a defined set of processing conditions. A rectangular mold insert which has three consecutive zones with decreasing thickness along the flow direction was adopted to study abrupt changes in mold geometry on the properties of resultant microparts. The distribution of carbon fillers within microparts was observed by scanning electron microscopy, which was correlated with electrical conductivity measurements. Results indicated that there is a flow-induced orientation of incorporated carbon fillers and this orientation increased with increasing shearing effect along the flow direction. High structure CB is found to be more effective than CNT in terms of enhancing the electrical conductivity, which was attributed to the good dispersion of CB in PS and their ability to form conductive networks via self-assembly. Morphology observations indicated that there is a shear-induced depletion of CB particles in the shear layer, which is due to the marked difference of shear rates between the shear and core layers of the molded microparts. Moreover, an annealing treatment is beneficial to enhance the electrical conductivity of CNT-containing microparts.