Physical, mechanical, and in vitro biological analysis of bioactive fibers‐based dental composite

Effect of nanofibers as reinforcement on resin-based dental materials: A systematic review of in vitro studies

This systematic review provides an update on the effect of nanofibers as reinforcement on resin-based dental materials. A bibliographic search was conducted in MEDLINEPubMed, Embase, Web of Science, Scopus, BVS (LILACS, BBO e IBECS), Cochrane, LIVIVO, and gray literature (BDTD) to identify relevant articles up to May 2021. In vitro studies that evaluated and compared the mechanical properties of nanofibers resin-based composite materials, were eligible. No publication year or language restriction was applied, and methodological quality was assessed using two methods. In a total of 6100 potentially eligible studies, 81 were selected for full-text analysis and 35 were included for qualitative analysis. Of the 35 included studies, a total of 29 studies evaluated the flexural strength (FS) of the materials. These groups were distinguished according to the resin-based materials tested and nanofiber types. Most of the studies evaluated materials composed of glass fibers and demonstrated higher values of FS when compared to resin-based materials without nanofibers. The incorporation of nanofibers into resin-based dental materials improved the mechanical properties compared to resin-based materials without nanofibers, suggesting better performance of these materials in high-stressbearing application areas. Further clinical studies are required to confirm the efficacy of resin-based materials with nanofibers.

Preparation of Nano-Apatite Grafted Glass-Fiber-Reinforced Composites for Orthodontic Application: Mechanical and In Vitro Biofilm Analysis

This study aimed to fabricate nano-hydroxyapatite (nHA) grafted/non-grafted E-glass-fiber-based (nHA/EG) and E-glass fiber (EG) orthodontic retainers and to compare their properties with commercially available retainers. Stainless-steel (SS) retainers and everStick Ortho (EST) were used as control groups. The retainers were evaluated with Raman spectroscopy and bonded to bovine teeth. The samples were fatigued under cyclic loading (120,000 cycles) followed by static load testing. The failure behavior was evaluated under an optical microscope and scanning electron microscope. The strain growth on the orthodontic retainers was assessed (48h and 168h) by an adhesion test using Staphylococcus aureus and Candida albicans. The characteristic peaks of resin and glass fibers were observed, and the debonding force results showed a significant difference among all of the groups. SS retainers showed the highest bonding force, whereas nHA/EG retainers showed a non-significant difference from EG and EST retainers. SS retainers’ failure mode occurred mainly at the retainer–composite interface, while breakage occurred in glass-fiber-based retainers. The strains’ adhesion to EST and EG was reduced with time. However, it was increased with nHA/EG. Fabrication of nHA/EG retainers was successfully achieved and showed better debonding force compared to other glass-fiber-based groups, whereas non-linear behavior was observed for the strains’ adhesion.

Monomer Release from Dental Resins: The Current Status on Study Setup, Detection and Quantification for In Vitro Testing

Improvements in mechanical properties and a shift of focus towards esthetic dentistry led to the application of dental resins in various areas of dentistry. However, dental resins are not inert in the oral environment and may release monomers and other substances such as Bisphenol-A (BPA) due to incomplete polymerization and intraoral degradation. Current research shows that various monomers present cytotoxic, genotoxic, proinflammatory, and even mutagenic effects. Of these eluting substances, the elution of BPA in the oral environment is of particular interest due to its role as an endocrine disruptor. For this reason, the release of residual monomers and especially BPA from dental resins has been a cause for public concern. The assessment of patient exposure and potential health risks of dental monomers require a reliable experimental and analytical setup. However, the heterogeneous study design applied in current research hinders biocompatibility testing by impeding comparative analysis of different studies and transfer to the clinical situation. Therefore, this review aims to provide information on each step of a robust experimental and analytical in vitro setup that allows the collection of clinically relevant data and future meta-analytical evaluations.

A laboratory study to assess the physical, mechanical, and 3-D structural properties of nano-apatite grafted glass fibre-based endodontic posts

AIM

To fabricate and characterize nano-hydroxyapatite (nHA) grafted and non-grafted glass fibre-based endodontic posts.

METHODOLOGY

Experimental glass fibre posts were fabricated using silanized nHA grafted (ex-HA) and non-grafted glass fibre (ex-P) reinforced resins. The structural analysis and morphological patterns were analysed with Fourier transform infrared spectroscopy and scanning electron microscopy, respectively. EverStick^® glass fibre posts (eS) were used as a control group. The degree of conversion, flexural strength, and flexural modulus was investigated and the fractured structure was evaluated with a scanning electron microscope. Root canals were prepared in human extracted teeth restored with experimental and control posts. The push-out bond strength was evaluated with radicular dentine at days 7, 30, and 90, and the presence of voids at the interface were measured at day 1, 7, 30, and 90 with micro-computed tomography. The Shapiro-Wilk test and one-way ANOVA post-hoc Tukey's test were performed. The level of significance was set at 0.05.

RESULTS

The SEM and FTIR confirmed the presence of a silane-coupling agent on the glass fibres. The ex-HA post had a significantly lower degree of conversion compared to the ex-P post (p = .0008), but a significantly higher conversion than the eS post (p = .0014). The maximum flexural strength value was obtained with the ex-HA post with an insignificant difference (p = .366) compared to ex-P post and a significant difference (p = .029) compared to the eS post. The flexural modulus of ex-HA, ex-P, and eS posts were significantly different (p = .037). Similarly, the ex-HA post had a significantly higher push-out bond strength at days 7 and 30 (p = .037) compared to the ex-P and eS posts. The volume of voids had a nonlinear behaviour amongst the groups with no significant difference between the posts.

CONCLUSION

The fabrication of the experimental posts was successful and the ex-HA post had greater flexural strength and push-out bond strength compared to the ex-P post. The degree of conversion of the ex-HA post was lower than the ex-P and eS posts. The volume of voids of ex-HA and ex-P posts was lower than that of eS posts.