Optical surface properties and morphology of MgO and CaO nanocrystals

Optical absorption and photoluminescence emission properties of dehydroxylated MgO and CaO nanocrystals are discussed with respect to particle morphology and size. On MgO nanocubes with pronounced corner and edge features two emission bands at 3.4 and 3.3 eV result from the excitation of 4-coordinated surface O(4C)(2-) anions in edges at 5.4 eV and of regular oxygen-terminated corners at 4.6 eV, respectively. Morphologically ill-defined CaO particles are a factor of 5 larger, do not display regular corner features, and show only one photoluminescence emission band at 3.0 eV. The associated excitation spectrum indicates electronic excitations above the energy required to excite regular oxygen-terminated CaO corners. It is concluded that in the case of morphologically well-defined MgO nanocubes variations in the next coordination of oxygen-terminated corners can effectively be probed by photoluminescence spectroscopy and thus allows for discrimination between 3-coordinated surface O(2-) in regular corner sites and kinks.

Inside Powders: A Theoretical Model of Interfaces between MgO Nanocrystallites

The electron- and hole-trapping and optical properties of a wide variety of interfaces between MgO nanocrystallites are investigated for the first time using a quantum-mechanical embedded-cluster method and time-dependent density functional theory. We conclude that delocalized holes can be transiently trapped at a large number of places within a powder. However, it is more energetically favorable for holes to trap on low-coordinated anions on the nanocrystallite surface, forming O- species. Electrons are trapped at few interfaces but are readily trapped by surface kink and corner sites. Contrary to common perception, our calculations of optical absorption spectra indicate that a variety of features buried within a powder can be exited with photon energies less than 5 eV, usually used to selectively excite low-coordinated surface sites.

Kinetic Model of Energy Transfer Processes Between Low-Coordinated Ions on MgO by Photoluminescence Decay Measurements

Photoluminescence decay studies of emitting species on MgO nanocubes at room temperature provide evidence of three surface species characterized by an excitation and emission wavelength couple {lambda(exc);lambda(em)}. Species A corresponds to {lambda(exc)=240 nm; lambda(em)=380 nm}, whereas the couple {lambda(exc)=280 nm; lambda(em)=470 nm} is assigned to two species: B and B', the former is involved in energy transfer from excited state A* and the latter in direct emission from excited state B'*. A simple model for energy transfer from species A* to B is proposed. The numerical resolution of equations corresponding to this model is in good agreement with experimental data. This method quantifies the kinetics of intrinsic emission and energy transfer processes. Lifetime values indicate that phosphorescence is taking place, and species A, B and B' are identified as edge O(2-) (4 C), corner O(2-) (3 C) and kink O(2-) (3 C) oxide ions respectively.

Physicochemical and in Situ Photoluminescence Study of the Reversible Transformation of Oxide Ions of Low Coordination into Hydroxyl Groups upon Interaction of Water and Methanol with MgO†,‖

The interaction of water and methanol with MgO samples with different distributions of oxide ions of low coordination has been investigated by physical techniques, particularly in situ photoluminescence. First, the three photoluminescence fingerprints of oxide ions vs their coordination number have been obtained for samples outgassed at 1273 K. By a pseudo quantitative approach, the relative distribution of the oxide ions of low coordination O(2-)LC (where LC = 3C, 4C, and 5C refer to tri-, tetra-, and pentacoordinated oxide ions, respectively) was determined and correlated with the shape and size of MgO particles determined by TEM and XRD. The photoluminescence of surfaces of MgO obtained after outgassing at increasing temperature or after interaction of water or methanol with a clean surface, i.e., obtained by outgassing at 1273 K, was then studied and evidenced three other photoluminescent species assigned to surface OH groups. The nature and mechanism of formation of the hydroxyls groups responsible for these new luminescent species are discussed in relation with their thermal stability and FTIR experiments.