Ending the Chase for a Perfect Binder: Role of Surface Chemistry Variation and its Influence on Silicon Anodes

Influence of the Polyacrylic Acid Binder Neutralization Degree on the Initial Electrochemical Behavior of a Silicon/Graphite Electrode

The role of the physicochemical properties of the water-soluble polyacrylic acid (PAA) binder in the electrochemical performance of highly loaded silicon/graphite 50/50 wt % negative electrodes has been examined as a function of the neutralization degree x in PAAH_1-xLi_x at the initial cycle in an electrolyte not containing ethylene carbonate. Electrode processing in the acidic PAAH binder at pH 2.5 leads to a deep copper corrosion, resulting in a significant electrode cohesion and adhesion to the current collector surface, but the strong binder rigidity may explain the big cracks occurring on the electrode surface at the first cycle. The nonuniform binder coating on the material surface leads to an important degradation of the electrolyte, explaining the lowest initial Coulombic efficiency and the lowest reversible capacity among the studied electrodes. When processed in neutral pH, the PAAH_0.22Li_0.78 binder forms a conformal artificial solid electrolyte interphase layer on the material surface, which minimizes the electrolyte reduction at the first cycle and then maximizes the initial Coulombic efficiency. However, the low mechanical resistance of the electrode and its strong cracking explain its low reversible capacity. Electrodes prepared at intermediate pH 4 combine the positive assets of electrodes prepared at acidic and neutral pH. They lead to the best initial performance with a notable areal capacity of 7.2 mA h cm^-2 and the highest initial Coulombic efficiency of around 90%, a value much larger than the usual range reported for silicon/graphite anodes. All data obtained with complementary characterization techniques were discussed as a function of the PAA polymeric chain molecular conformation, microstructure, and surface adsorption or grafting, emphasizing the tremendous role of the binder in the electrode initial performance.

Probing clustering dynamics between silicon and PAA or LiPAA slurries under processing conditions

This work explores the complex interplay between slurry aggregation, agglomeration, and conformation (i.e. shape) of poly(acrylic acid) (PAA) and lithiated poly(acrylic acid) (LiPAA) based silicon slurries as a function of shear rate, and the resulting slurry homogeneity. These values were measured by small angle neutron scattering (SANS) and rheology coupled ultra-small angle neutron scattering (rheo-USANS) at conditions relevant to battery electrode casting. Different binder solution preparation methods, either a ball mill (BM) process or a planetary centrifugal mixing (PCM) process, dramatically modify the resulting polymer dynamics and organization around a silicon material. This is due to the different energy profiles of mixing where the more violent and higher energy PCM causes extensive breakdown and reformation of the binder, which is now likely in a branched conformation, while the lower energy BM results in simply lower molecular weight linear polymers. The break down and reorganization of the polymer structure affects silicon slurry homogeneity, which affects subsequent electrode architecture.