Measuring the elastic properties of fine wire

Effect of soft drinks on the physical and chemical features of nickel-titanium-based orthodontic wires

OBJECTIVE

The purpose of this study was to evaluate the effect of three popular soft drinks on the Young's modulus, hardness, surface topography and chemical composition of widely used nickel-titanium-based orthodontic wires.

MATERIALS AND METHODS

Thirty-two specimens (20 mm in length) were cut from the straight portion of pre-formed 0.019 × 0.025 inch Nitinol Heat-Activated archwires and randomly divided into four groups of eight specimens each: Group A1 (Coca Cola(®) regular); Group A2 (Santal(®) orange juice); Group A3 (Gatorade(®)); Group B (distilled, deionized water; dH(2)O). Each specimen was immersed in 10 ml of one of the soft drinks or dH(2)O, control, for 60 min, at 37°C. At the end of the soaking time, the Young's modulus and hardness were determined using a nanoindenter. Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS) was used to characterize the effects on the topography and chemical composition of the wires.

RESULTS

No statistically significant differences were found between the groups either in the Young's modulus or in hardness after the selected soaking protocol. Besides some surface colour changes, the topography and the chemical composition of the wires were not affected by the immersion in any of the chosen soft drinks.

CONCLUSIONS

These in-vitro results suggest that the consumption of soft drinks cannot be acknowledged as one possible reason for the degradation of the physical and chemical properties of heat activated nickel titanium orthodontic wires in patients undergoing fixed orthodontic treatment.

Measuring mechanical properties of fine-wire cross-sections used in medical devices

In this study, it was demonstrated that the nanoindentation technique can be used to measure the elastic modulus and hardness of fine-wire cross-sections with diameters ranging from 100-200 microm. Using miniature optics and a specially developed micrometer positioning system, measurements were successfully performed on the wire cross-sections with an accuracy of 1 microm. Homogeneous wire cross-sections, such as MP35N (high-strength nickel-cobalt alloy), composite wires such as MP35N with a silver core (MP35N/Ag-core), and platinum-clad tantalum (Pt-clad Ta) were studied. From the nanoindentation measurements, the elastic modulus and hardness at different positions and depths were calculated. It was found that both elastic modulus and hardness reached a constant value below the hardened surface, which resulted from mechanical polishing. Material properties obtained from the measurements were compared with the literature values of bulk materials as well as available results on fine wires. The data from the wire cross-sections, especially the uniform material samples, showed that both the elastic modulus and hardness were significantly lower near the outer 10-15 microm of the wire as compared to the rest of the wire, which is due to surface weakening during manufacturing. In addition, both modulus and hardness showed a small but consistent "sawtooth" variation across the diameter of the wires, excluding the outer 10-15 microm, that is postulated to be induced by the distribution of residual stress.