The effect of production regime and crucible materials on the thermal properties of sodium phosphate glasses produced from salts

Composites for bone repair: phosphate glass fibre reinforced PLA with varying fibre architecture

Internal fixation for bone fractures with rigid metallic plates, screws and pins is a proven operative technique. However, refracture's have been observed after rigid internal fixation with metal plates and plate fixation has been known to cause localised osteopenia under and near the plate. In the present study, resorbable composites comprising a PLA matrix reinforced with iron doped phosphate glass fibres were investigated. Non-woven random mat laminates of approximately 30% and 45% fibre volume fraction (V(f)) were produced, along with unidirectional and 0°-90° samples of approximately 20% V(f). The non-woven composite laminates achieved maximum values of 10 GPa modulus and 120 MPa strength. The 0-90º samples showed unexpectedly low strengths close to matrix value (~50 MPa) although with a modulus of 7 GPa. The UD specimens exhibited values of 130 MPa and 11.5 GPa for strength and modulus respectively. All the modulus values observed were close to that expected from the rule of mixtures. Samples immersed in deionised water at 37°C revealed rapid mechanical property loss, more so for the UD and 0-90º samples. It was suggested that continuous fibres wicked the degradation media into the composite plates which sped up the deterioration of the fibre-matrix interface. The effect was less pronounced in the non-woven random mat laminates due to the discontinuous arrangement of fibres within the composite, making it less prone to wicking. Random mat composites revealed a higher mass loss than the UD and 0°-90° specimens, it was suggested this was due to the higher fibre volume fractions of these composites and SEM studies revealed voidage around the fibres by day 3. Studies of pH of the degradation media showed similar profiles for all the composites investigated. An initial decrease in pH was attributed to the release of phosphate ions into solution followed by a gradual return back to neutral.

Cytocompatibility and Effect of Increasing MgO Content in a Range of Quaternary Invert Phosphate-based Glasses

Recently, phosphate-based glass (PBG) fibers have been used to reinforce the biodegradable polymers polycaprolactone and polylactic acid, in order to fabricate materials suitable for use as resorbable bone fracture fixation devices. However, the PBG fibers investigated tended to degrade too quickly for application. Therefore, more durable PBG formulations were sought with emphasis remaining firmly placed on their biocompatibility. In this study, four invert PBG formulations (in the system P2O5—CaO—MgO—Na 2O) were produced with fixed phosphate and calcium content at 40 and 25 mol%, respectively. MgO was added at 10—30 mol% in place of Na 2O and the maximum divalent cation to phosphate ratio obtained was 1.375. Thermal analyses showed a linear increase in Tg with increasing MgO content. This was proposed to be due to an increase in the cross-link density of the glass network, which also improved the chemical durability of the glass. EDX analyses were also conducted to verify the final composition of the glass. XRD analyses confirmed the amorphous nature of the glasses investigated. Rapid quenching of the Mg30 glass revealed a degree of surface crystallization, which was shown to be a CaMgP2O7 phase. The degradation rates of the glasses investigated decreased with increasing MgO content. The decrease in rate seen was almost two orders of magnitude (a ×50 difference was seen between glass Mg0 and Mg30). The cytocompatibility studies of the formulations investigated showed good cellular response over time for up to 14 days. Statistical analysis revealed that the formulations investigated gave a response comparable to the tissue culture plastic control. It is suggested that invert PBG provide degradation profiles and the cytocompatibility response desired to make these glasses useful for bone repair applications.