Oxidation and other property changes of a remelted highly crosslinked UHMWPE in retrieved tibial bearings

Influence of radiation conditions on the wear behaviour of Vitamin E treated UHMWPE gliding components for total knee arthroplasty after extended artificial aging and simulated daily patient activities

The long term performance of total knee arthroplasty (TKA) with regards to the bearing materials is related to the aging behaviour of these materials. The use of highly crosslinked materials in hip arthroplasty improved the clinical outcome. Nevertheless, the outcome for these materials compared to conventional UHMWPE (ultra-high molecular weight polyethylene) remains controversial in TKA and alternative bearing materials may be advantageous to improve its outcome in the second and third decade. The aim of this study is the evaluation of the influence of radiation conditions on the wear behaviour of Vitamin E blended UHMWPE gliding components for TKA by simulation of extended aging and high demanding daily patient activities. For a medium radiation dose (30 kGy), the influence of the irradiation type (E-beam or Gamma radiation) and the thermal conditions (room temperature (RT) or heated to 115 °C) are evaluated in comparison to non-irradiated material. Significant influences on the wear behaviour were found for the radiation source and temperature during irradiation. Furthermore, no relevant degradation of the tested materials was observed after extended artificial aging. There was a good correspondence between the wear pattern in this study and retrievals.

Effects of Vitamin E-Stabilized Ultra High Molecular Weight Polyethylene on Oxidative Stress Response and Osteoimmunological Response in Human Osteoblast

High Crosslink process was introduced in the development of joint prosthetic devices, in order to decrease the wear rate of ultrahigh molecular weight polyethylene (UHMWPE), but it also triggers the formation of free radicals and oxidative stress, which affects the physiological bone remodeling, leading to osteolysis. Vitamin E stabilization of UHMWPE was proposed to provide oxidation resistance without affecting mechanical properties and fatigue strength. The aim of this study is to evaluate the antioxidant effect of vitamin E added to UHMWPE on oxidative stress induced osteolysis, focusing in particular on the oxidative stress response in correlation with the production of osteoimmunological markers, Sclerostin and DKK-1, and the RANKL/OPG ratio compared to conventional UHMWPE wear debris. Human osteoblastic cell line SaOS2 were incubated for 96 h with wear particles derived from crosslinked and not crosslinked Vitamin E-stabilized, UHMWPE without Vitamin E, and growth medium as control. Cellular response to oxidative stress, compared to not treat cells, was evaluated in terms of proteins O-GlcNAcylation, cellular levels of OGA, and OGT proteins by immunoblotting. O-GlcNAcylation and its positive regulator OGT levels are increased in the presence of Vitamin E blended UHMWPE, in particular with not crosslinked Vit E stabilized UHMWPE. Conversely, the negative regulator OGA increased in the presence of UHMWPE not blended with Vitamin E. Vitamin E-stabilized UHMWPE induced a decrease of RANKL/OPG ratio compared to UHMWPE without Vitamin E, and the same effect was observed for Sclerostin, while DKK-1 was not significantly affected. In conclusion, Vitamin E stabilization of UHMWPE increased osteoblast response to oxidative stress, inducing a cellular mechanism aimed at cell survival. Vitamin E antioxidant effect influences the secretion of osteoimmunological factors, shifting the bone turnover balance toward bone protection stimuli. This suggests that Vitamin E-Stabilization of UHMWPE could contribute to reduction of oxidation-induced osteolysis and the consequent loosening of the prosthetic devices, therefore improving the longevity of total joint replacements.

Antioxidant-stabilized highly crosslinked polyethylene in total knee arthroplasty

Aims

The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts.

Materials and Methods

A total of 19 A-XLPE tibial inserts were retrieved during revision TKA and matched to 18 retrieved XLPE inserts according to the demographics of the patients, with a mean length of implantation of 15 months (1 to 42). The percentage areas of PE damage on the articular surfaces and the modes of damage were measured. The density of crosslinking of the PE and oxidation were measured at loaded and unloaded regions on these surfaces.

Results

A-XLPE inserts had higher rates of burnishing and lower rates of pitting and scratching compared with XLPE. There were no differences in the density of crosslinking at loaded and unloaded regions. A-XLPE showed higher oxidation indices in the unloaded surface region compared with XLPE. There were no differences in the levels of oxidation in the loaded regions.

Conclusion

Retrieval analysis of A-XLPE did not reflect a clinically relevant difference in surface damage, density of crosslinking, or oxidation compared with XLPE tibial inserts at short-term evaluation. Cite this article: Bone Joint J 2018;100-B:1330–5.