Influence of thermocycling on shear bond strength of glass ionomer cement to Er:YAG laser-prepared enamel

The Effects of Silver, Zinc Oxide, and Titanium Dioxide Nanoparticles Used as Dentin Pretreatments on the Microshear Bond Strength of a Conventional Glass Ionomer Cement to Dentin

Aim

This study was conducted to evaluate the effects of three nanoparticle solutions used as dentin pretreatments on the microshear bond strength (µSBS) of a conventional glass ionomer cement (GIC) to dentin.

Materials and Methods

Ninety intact human molars were used after sectioning their occlusal surfaces to expose flat dentin surfaces. The specimens were randomly assigned to nine groups (n = 10). Group A was the control group (without using the cavity disinfectant). In groups B, C, D, and E, the prepared dentin surfaces were treated with 1 cc 2% chlorhexidine (CHX), 0.1% silver nanoparticle (SNP), 0.1% titanium dioxide nanoparticle (TNP), and 0.1% zinc oxide nanoparticle (ZNP) solutions for 1 minute, respectively, before applying the conditioner. CHX, SNPs, TNPs, and ZNPs were applied for 1 minute after applying the conditioner in groups F, G, H, and I, respectively. The specimens were restored with a conventional GIC and underwent µSBS testing after 24 hours. The data were analyzed using the one-way analysis of variance and Tukey’s test (p=0.05).

Results

The applications of the nanoparticles (SNP, TNP, and ZNP) after the conditioner were associated with significantly greater µSBS values compared to that of the control group (p values < 0.05). Significantly higher µSBS values were observed when TNP or ZNP was applied after the conditioner compared to their applications before the conditioner (p values < 0.05). The highest µSBS values were observed when TNP was applied after the conditioner.

Conclusion

Dentin pretreatment with the nanoparticles after applying the conditioner enhanced the bond strength of the GIC to dentin compared with the control group. The best results were obtained for the TNPs applied after the conditioner.

Effect of Er:YAG Laser Etching on the Shear Bond Strength and Microleakage of Self-Glazed Zirconia Ceramics

Objective: To investigate the effect of Er:YAG laser irradiation on the shear bond strength (SBS) and microleakage of self-glazed zirconia (SZ) ceramics. Background: SZ is a novel type ceramic; laser irradiation has started to be used in the surface treatment of different ceramics, while SZ has been rarely studied to improve the bond quality. Methods: One hundred twenty blocks (5 mm × 5 mm × 5 mm) of SZ ceramics were produced and split into eight groups following different surface treatments (n = 15): Group A: no treatment; Group B: standard grid processing; and Group C-H: different Er:YAG laser power settings (100, 200, 300, 400, 500, and 600 mJ). Ten blocks of each group received the measurement of SBS and fracture mode analysis, three blocks underwent the evaluation of the microleakage depths, and the other two blocks were observed under the scanning electronic microscopy (SEM). Results: Group F obtained the highest SBS and the lowest microleakage depth without damaging the ceramic surface structure, which was statistically significant compared with the control group and gridding group (p < 0.05), whereas the difference was not statistically significant (p > 0.05) between group E and group F. The results of bonding performance were consistent with failure types and observation of surface characterizations in SEM images. Conclusions: According to the results here, Er:YAG irradiation had effect on surface treatment. In addition, 400 mJ Er:YAG could increase the SBS and decrease the microleakage depth on SZ ceramics without damaging the surface structure.

Comparison of an Er: YAG laser osteotome versus a conventional drill for the use in osteo- odonto-keratoprosthesis (OOKP)

OBJECTIVES

The osteo-odonto-kerato-prosthesis (OOKP) procedure is a complex, multi-stage, multidisciplinary surgical intervention for the treatment of severe corneal blindness. One step of the OOKP consists of creating a precise hole into a tooth in which an optic cylinder is subsequently inserted; its shape must ensure a perfect watertight fit. The Er: YAG laser (L) used in this study is part of CARLO®, the first laser osteotome that enables surgical planning based on computed tomography data, robot guidance, and a precise execution of laser cuts in teeth and bone tissue, using laser photoablation rather than conventional mechanical methods. The purpose of this study was to assess whether the Er: YAG laser is non-inferior compared to a conventional drill.

METHODS

Thirty-two bovine incisors were grounded to a thickness of 1.5 mm. In 16 teeth, a 3.5 mm hole was drilled progressively into each tooth, using dental burs (B) of increasing diameter that were attached to a fixed drill machine. In the other 16 teeth, a hole was created using an Er: YAG laser at a wavelength of 2.94 µm (Part of CARLO®). In seven teeth of each group, the cylinder was inserted and fixated with polymethylmethacrylate (PMMA) bone cement. In the remaining seven teeth of each group, the cylinder was inserted without fixation material (press-fit). After bonding and drying, all specimens were stored in water until force measurements were recorded using a uniaxial traction machine. The force required to move the optical cylinder out of the hole in the tooth was measured using an Instron 3344 testing system. Scanning electron microscope (SEM) and light microscope (LM) visualization of the holes created with the laser and the drill were performed in two teeth (SEM)/four teeth (LM) per method.

RESULTS

Significant differences (P < 0.001) were found for the following parameters: B PMMA versus B press-fit; B PMMA versus L press-fit; L PMMA versus B press-fit; L PMMA-L press-fit. This shows that PMMA bone cement fixation is superior to press-fit. No significant differences were found between B PMMA-L PMMA (P = 0.93) and B press-fit-L press-fit (P = 0.83). The SEM pictures showed a smoother surface using L.

CONCLUSIONS

The laser cut holes were as strong as bur-drilled holes, although SEM pictures showed a smoother surface of the laser cut holes. Hence, laser osteotomes open the possibility to custom fit the hole exactly to the width of the cylinder, which represents a potential advantage of the laser over the conventional bur. Lasers Surg. Med. 51:531-537, 2019. © 2019 Wiley Periodicals, Inc.