Reactivity and Controlled Redox Reactions of Salt-like Intermetallic Compounds in Imidazolium-Based Ionic Liquids

Synthesis and Physical Properties of Tunable Aryl Alkyl Ionic Liquids (TAAILs) Comprising Imidazolium Cations Blocked with Methyl-, Propyl- and Phenyl-Groups at the C2 Position

Imidazolium-based ionic liquids are very popular for different applications because of their low viscosity and melting point. However, the hydrogen atom at the C2 position of the imidazolium cation can easily be deprotonated by a base, resulting in a reactive carbene. If an inert ionic liquid is needed, it is necessary to introduce an unreactive alkyl or aryl group at the C2 position to prevent deprotonation. Tunable aryl alkyl ionic liquids (TAAILs) were first introduced by our group in 2009 and are characterized by a phenyl group at the N1 position, which offers the possibility to fine-tune the physicochemical properties by using different electron-donating or -withdrawing substituents. In this work, we present a new series of TAAILs where the C2 position is blocked by a methyl, propyl or phenyl group. For each of the blocking groups, the phenyl and three different phenyl derivatives (2-Me, 4-OMe, 2,4-F₂ ) are compared with respect to melting point, viscosity, conductivity and electrochemical window. In addition, the differences between blocked and unblocked TAAILs with regard to their electrochemical reduction potentials are investigated by quantum chemical methods.

Synthesis of Type II Ge and Ge-Si Alloyed Clathrates Using Solid-State Electrochemical Oxidation of Zintl Phase Precursors

Germanium clathrates with the type II structure are open-framework materials that show promise for various applications, but the difficulty of achieving phase-pure products via traditional synthesis routes has hindered their development. Herein, we demonstrate the synthesis of type II Ge clathrates in a two-electrode electrochemical cell using Na₄Ge_4-ySi_y (y = 0, 1) Zintl phase precursors as the working electrode, Na metal as the counter/reference electrode, and Na-ion conducting β″-alumina as the solid electrolyte. The galvanostatic oxidation of Na₄Ge₄ resulted in voltage plateaus around 0.34-0.40 V vs Na/Na⁺ with the formation of different products depending on the reaction temperature. When using Na₄Ge₃Si as a precursor, nearly phase-pure, alloyed type II Ge-Si clathrate was obtained at 350 °C. The Na atoms in the large (Ge,Si)₂₈ cages of the clathrate occupied off-centered positions according to Rietveld refinement and density functional theory calculations. The results indicate that electrochemical oxidation of Zintl phase precursors is a promising pathway for synthesizing Ge clathrates with type II structure and that Si alloying of the Zintl phase precursor can promote selective clathrate product formation over other phases.

Type-II Clathrate Na24-δ Ge136 from a Redox-Preparation Route

The metastable type-II clathrate Na24-δ Ge136 was obtained from Na12 Ge17 by applying a two-step procedure. At first, Na12 Ge17 was reacted at 70 °C with a solution of benzophenone in the ionic liquid (IL) 1,3-dibutyl-2-methylimidazolium-bis(trifluoromethylsulfonyl) azanide. The IL was inert towards Na12 Ge17 , but capable of dissolving the sodium salts formed in the redox reaction. By annealing at 340 °C under an argon atmosphere, the X-ray amorphous intermediate product was transformed to crystalline Na24-δ Ge136 (δ≈2) and α-Ge in an about 1 : 1 mass ratio. The product was characterized by X-ray powder diffraction, chemical analysis, and 23 Na solid-state NMR spectroscopy. Metallic properties of Na24-δ Ge136 were revealed by a significant Knight shift of the 23 Na NMR signals and by a Pauli-paramagnetic contribution to the magnetic susceptibility. At room temperature, Na24-δ Ge136 slowly ages, with a tendency to volume decrease and sodium loss.