Development and Investigation of PEDOT:PSS Composition Coated Fabrics Intended for Microwave Shielding and Absorption

This study presents the investigation of the electromagnetic properties and resistance performance of electrically conductive fabrics coated with composition containing the conjugated polymer system poly(3,4-ethylenedioxythiophene)-polystyrene sulfonate (PEDOT:PSS). The developed fabrics were intended for electromagnetic radiation (EMR) shielding in microwave range and for absorbing microwaves in radar operating range, so as to act as radar absorbing materials (RAM). The measurements of reflection and transmission of the developed fabrics were performed in a frequency range of 2-18 GHz, which covers the defined frequencies relevant to the application. Four types of fabrics with different fiber composition (polyamide; polyamide/cotton; wool and para-aramid/viscose) were selected and coated with conductive paste using screen printing method. It was found that EMR shielding effectiveness (SE) as well as absorption properties depend not only the amount of conductive paste topped on the fabric, but also resides in the construction parameters of fabrics. Depending on such fabric structural parameters as density, mass per unit area, type of weave, a layer of shield (or coating) just sticks on the fabric surface or penetrates into fabric, changing the shield thickness and herewith turning SE results. Meanwhile, the fiber composition of fabrics influences mostly bonding between fibers and polymer coating. To improve the resistance performance of the developed samples, a conventional textile surface modification technique, atmospheric plasma treatment, was applied. Initially, before plasma treatment and after treatment the fabrics were evaluated regarding an aqueous liquid repellency test, measuring the contact angles for the water solvent. The influence of plasma treatment on resistance performance of coated fabrics was evaluated by subjecting the plasma treated samples and untreated samples to abrasion in the Martindale abrasion apparatus and to multiplex washing cycles. These investigations revealed that applied plasma treatment visibly improved abrasion resistance as a result of better adhesion of the coating. However, washing resistance increased not so considerably.

Robust Design of PC/ABS Filled with Nano Carbon Black for Electromagnetic Shielding Effectiveness and Surface Resistivity

This study focuses on the electromagnetic interference shielding effectiveness (EMI SE), dissipation of electrostatic discharge (ESD), and surface resistivity of polymer blends between polycarbonate (PC) and acrylonitrile–butadiene–styrene (ABS) filled with carbon black powder (CBp) and carbon black masterbatch (CBm). The mixtures of PC/ABS/CB composites were prepared by the injection molding for the 4-mm thickness of the specimen. The D-optimal mixture design was applied in this experiment. The EMI SE was measured at the frequency of 800 and 900 MHz with a network analyzer, MIL-STD-285. The result showed that the EMI SE was increased when the amount of filler increased. The surface resistivity of the composites was determined according to the ASTM D257. It was found that the surface resistivity of the plastic with no additives was 1012 Ω/ square. When the amount of fillers was added, the surface resistivity of plastic composites decreased to the range of 106–1011 Ω/square, which was suitable for the application without the electrostatic discharge. The optimization of multi-response showed using high amounts of PC and CB was the best mixture of this research.

Electromagnetic wave absorption polyimide fabric prepared by coating with core–shell NiFe2O4@PANI nanoparticles

The NiFe₂O₄@PANI/PI fabric exhibited excellent microwave attenuation performance, favorable mechanical properties and was appropriate for large-scale production.

High performance electromagnetic wave absorbers derived from PC/SAN blends containing multiwall carbon nanotubes and Fe3O4 decorated onto graphene oxide sheets

A high performance electromagnetic wave absorber with high surface resistivity and enhanced attenuation constant was designed using uneven distribution of lossy materials in PC/SAN blends.

Electromagnetic Functionalized and Core−Shell Micro/Nanostructured Polypyrrole Composites

Core-shell micro/nanostructured and electromagnetic functionalized polypyrrole (PPy) composites were prepared by a self-assembly process associated with the template method in the presence of p-toluenesulfonate acid (p-TSA) as the dopant, in which the spherical hydroxyl iron (Fe[OH], 0.5-5 microm in diameter) functioned not only as the hard template, but also as the "core" of the micro/nanostructure, and the self-assembled PPy-p-TSA nanofibers (20-30 nm in diameter) acted as the "shell" (50-100 nm in thickness) of the microspheres. We found that the core-shell micro/nanostructures exhibit controllable electromagnetic properties by adjusting the mass ratio of Fe[OH] to pyrrole monomer. The micelle model was proposed to interpret the self-assembly of the core-shell micro/nanostructured composites.