Preparation of Mesoporous Si Nanoparticles by Magnesiothermic Reduction for the Enhanced Reactivity

In this study, mesoporous silicon nanoparticles (M-Si) were successfully prepared by a magnesiothermic reduction of mesoporous silica nanoparticles, which were synthesized by a templated sol-gel method and used as the precursors. M-Si exhibited a uniform size distribution with an average diameter of about 160 nm. The measured BET surface area was 93.0 m² g^-1, and the average pore size calculated by the BJH method was 16 nm. The large internal surface area provides rich reaction sites, resulting in unique interfacial properties and reduced mass diffusion limitations. The mechanism of the magnesiothermic reduction process was discussed. The reactivity of prepared M-Si was compared with that of commercially available non-porous Si nanopowder (with the average diameter of about 30 nm) by performing simultaneous thermogravimetry and differential scanning calorimetry in the air. The results showed that the reaction onset temperature indicated by weight gain was advanced from 772 °C to 468 °C, indicating the promising potential of M-Si as fuel for metastable intermolecular composites.

Application of Silicon Dioxide as the Inert Component or Oxide Component Enhancer in ANFO

Non-ideal explosives with differing contents of silicon dioxide (silica or dioxosilane) added in the form of powder and gel were tested. Measurements of structure, crystallinity and morphology were performed by means of infrared spectroscopy (IR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). IR and XRD analysis revealed a lack of SiO2 influence on the non-ideal explosive structure. SEM analysis indicated that all the surface deformations of ammonium nitrate(V) prill were filled by a thin fuel film layer on which SiO2 was present. The additional calculations of selected theoretical properties of non-ideal compositions were made using ZMWCyw software. Based on this, it was established that the optimum semimetal content was 1.0 wt.%. Blasting tests confirmed that the addition of 1.0 wt.% SiO2 to the Ammonium Nitrate Fuel Oil (ANFO) resulted in the lowest volume of post-blast fumes. Moreover, it was established that finer SiO2 powder cannot be used as the oxide component enhancer due to the inhibition of detonation reaction. SiO2 should be used only as an inert component.