Evaluation of Ultrasonically ZnO Loading Effect on Photocatalytic Self-Cleaning, UV Protection and Antibacterial Activity of Plasma/Citric Acid-Activated Cotton Fabric

Zinc oxide (ZnO) nanoparticles were loaded over non-thermal plasma (P1) and citric acid (P2)-functionalized cotton fabrics using a room temperature sonification process. The cotton samples were pretreated with dielectric barrier discharge (DBD) plasma and citric acid to introduce some reactive moieties on the fabric to enhance the adhesion power of ZnO nanoparticles with an average particle size of 41 nm. The nanoparticles were dispersed homogeneously on the surface of the P1 sample, which enhanced the antibacterial, UV protection and photocatalytic self-cleaning characteristics of ZnO-loaded fabric. The self-cleaning efficiency of P1 and P2 samples was measured to be about 77% and 63%, respectively. The inhibition zones of 5.5 mm and 5.4 mm were produced by sample P1 against E. coli and S. aureusbacteria, respectively, which were slightly higher than the inhibition zones produced by sample P2. The inhibition zone of the samples roughly decreased by 17% after performing 10 wash cycles. The unloaded cotton fabric had a UPF value of 70.02 units and blocking percentage of 70.92% and 76.54% for UVA and UVB radiations, respectively. The UVA-blocking capacity of samples P1 and P2 was 95.27% and 91.22, respectively. Similarly, the UVB blocking capacity was 94.11% and 92.65%, respectively. The pre-coating plasma treatment was found to be helpful in improving the UV-blocking ability of ZnO-loaded cotton fabric.

Testing of photocatalytic potential of silver nanoparticles produced through nonthermal plasma reduction reaction and stabilized with saccharides

In this study, silver nanoparticles (AgNPs) were produced through an atmospheric pressure plasma reduction reaction and tested for photodegradation of methyl blue (MB) under sunlight exposure. The argon plasma born reactive species were used to reduce silver ions to AgNPs in the solution. Glucose, fructose and sucrose were also added in the solution to stabilize the growth process. The glucose stabilized reaction produced the smallest nanoparticles of 12 nm, while sucrose stabilized reaction produced relatively larger nanoparticles (14 nm). The nanoparticles exhibited rough morphology and narrow diameter distribution regardless of stabilizer type. The narrow diameter distribution and small band gap helped activating majority of nanoparticles at a single wavelength of light spectrum. The band gap energy of AgNPs varied from 2.22 eV to 2.41 eV, depending on the saccharide type. The photoluminescence spectroscopy of AgNPs produced emission peaks at 413 nm, 415 nm, and 418 nm. The photocatalytic potential of AgNP samples was checked by degrading MB dye under sunlight. The degradation reaction reached a saturation level of 98% after 60 min of light exposure.