Packing Effect on Latex Film Dissolution: A UV-Visible Study

Film formation from pure and mixed latices; transient fluorescence study

A fast transient fluorescence technique was used to study latex film formation induced by organic solvent vapor. Mixtures of pyrene (P)- and naphthalene (N)-labeled and/or pure naphthalene-labeled latex films were prepared separately from poly(methyl methacrylate) (PMMA) particles. Then these pure and mixed latex films were exposed to vapor of various chloroform-heptane mixtures in seven different experiments. In both films, fluorescence lifetimes from N were monitored during vapor-induced film formation. It was observed that N lifetimes decreased as the vapor exposure time is increased. A Stern-Volmer kinetic analysis was used for low quenching efficiencies to interpret the decrease in N lifetimes. A Prager-Tirrell model was employed to obtain back-and-forth frequencies, nu, of reptating PMMA chains during latex film formation induced by solvent vapor. In both pure and mixed latex films, nu values were found to be correlated with the chloroform content in the vapor mixture. It was observed that polymer interdiffusion obeyed a t1/2 law during film formation.

Fast transient fluorescence technique (FTRF) for studying vapor-induced latex film formation

A fast transient fluorescence (FTRF) technique was used to study latex film formation induced by organic solvent vapor. Seven different films with the same latex content were prepared separately from poly(methyl methacrylate) (PMMA) particles and exposed to vapor of various chloroform-heptane mixtures in seven different experiments. Latex films were prepared from pyrene (Py)-labeled latex particles and fluorescence lifetimes of Py were monitored during vapor-induced film formation. It was observed that pyrene lifetimes decreased as vapor exposure time increased. A Stern-Volmer kinetic analysis was used for low quenching efficiencies to interpret the decrease in pyrene lifetimes. A Prager-Tirrel model was employed to obtain back-and-forth frequencies, nu, of the reptating PMMA chains during latex film formation induced by solvent vapor. nu values were found to be correlated with chloroform content in vapor mixture. It was observed that polymer interdiffusion obeyed a t(1/2) law during film formation. The results of optical transmission experiments were found to support these findings.

Molecular weight effect on latex film formation induced by solvent vapor: an optical transmission study

Two different sets of powder latex film were prepared from high- and low-molecular-weight (HM and LM) poly(methyl methacrylate) (PMMA). The optical transmission method was used to the study film formation induced by organic vapor. Various HM and LM films with the same latex content were prepared separately from the PMMA particles and exposed to vapor of a chloroform-heptane mixture in various volume percents of chloroform. Transmitted light intensities, I(tr), from these films increased in time under vapor exposure, which was attributed to the increase in "crossing density" at the junction surface. The Prager-Tirrell model was employed to obtain the back-and-forth frequency, nu, of the reptating polymer chain during film formation induced by solvent vapor. nu values were obtained and found to be strongly correlated with the percent of chloroform in the solvent mixture and the molecular weight of the polymer chain. It is observed that high-molecular-weight chains reptate much more slowerly than low-molecular-weight chains.