Surface and Interparticle Effects in Amorphous Magnetic Nanoparticles

Magnetic studies of ultrafine CoFe2O4 nanoparticles with different molecular surface coatings

Surface functionalized ultrafine CoFe2O4 nanoparticles (NPs), with mean diameter ∼5 nm, were investigated by means of DC magnetization and AC susceptibility over the temperature range of 4-400 K. All NPs present the same CoFe2O4 core, with different molecular surface coatings, increasing gradually the number of carbon atoms in the coating layer: glycine (C2H5NO2), alanine (C3H7NO2), aminobutanoic acid (C4H9NO2), aminohexanoic acid (C6H13NO2), and aminododecanoic acid (C12H25NO2). Samples were intentionally fabricated in order to modulate the core-core magnetic dipolar interaction, as the thickness of the coating layer increases with the number of carbon atoms in the coating molecule. The magnetic data of the uncoated CoFe2O4 NPs were also collected for comparison. All investigated CoFe2O4 NPs (coated and uncoated) are in a magnetically blocked state at room temperature as evidenced by ZFC/FC measurements and the presence of hysteresis with ∼700 Oe coercivity. Low temperature magnetization scans show slightly constricted hysteresis loops with coercivity decreasing systematically with a decreasing number of carbon atoms in the coating molecule, possibly resulting from differences in magnetic dipole coupling between NPs. Large thermomagnetic irreversibility, slow monotonic increase in the FC magnetization and non-saturation of the magnetization give evidence for the cluster glass (CG) nature in the CoFe2O4 NPs. The out of phase part (χ'') of AC susceptibility for all samples shows a clear frequency dependent hump which was analyzed to distinguish superparamagnetic (SPM), cluster glass (CG) and spin glass (SG) behavior by using Néel-Arrhenius, Vogel-Fulcher, and power law fittings. These analyses rule out the SPM state and suggest the presence of significant inter-cluster dipolar interaction, giving rise to CG cooperative freezing in the high-temperature region. In the low-temperature range, however, the disordered spins on the nanoparticle's surface play an important role in the formation of the SG-like state, as evidenced by Arrott plots and temperature dependency of dM/dH in the initial magnetization curves. In summary, the magnetic measurements showed that undercooling the system evolves from a SPM state of weakly interacting spin clusters, through the CG state induced by strong dipolar interaction, to the SG state resulting from the frustration of the disordered surface spins.

Magnetic studies of layer-by-layer assembled polyvinyl alcohol/iron oxide nanofilms

The importance of the substrate surface effects on the magnetic behavior of layer-by-layer assembled polyvinyl alcohol/iron oxide nanofilms is evidenced.

The glassy behaviour of poorly crystalline Fe2O3 nanorods obtained by thermal decomposition of ferrous oxalate

Nanorod ferrous oxalate dihydrate (FeC2O4 × 2H2O) which had been synthesized by the microemulsion method, was used as a precursor in the thermal decomposition process performed in air atmosphere. The formation of nanocrystalline hematite as the final product was preceded by the appearence of an intermediate product. Comprehensive study comprising several complementary techniques (x-ray diffraction, transmission electron microscopy, selected area electron diffraction, thermogravimetric/differential thermal analyses and SQUID magnetometry) confirmed that the intermediate product corresponds to the poorly crystalline Fe2O3. Due to the specific nanorod shape and poorly crystalline structure, the investigated Fe2O3 showed high coercive field value of ~0.5 T at 5 K. Special attention in this study was devoted to the peculiar magnetic properties of poorly crystalline Fe2O3, which were thoroughly investigated by employing sophisticated experimental procedures such as relaxation of thermoremanent magnetization for different cooling fields, zero field and field cooled memory effects as well as aging experiments for different waiting times. At low temperatures and weak applied magnetic fields, the investigated system behaves similarly to spin glasses, manifesting slow, collective relaxation dynamics of magnetic moments through memory, rejuvenation and aging effects.

Some physicochemical aspects of nanoparticulate magnetic iron oxide colloids in neat water and in the presence of poly(vinyl alcohol)

The preparation of magnetic iron oxide colloids directly from the coprecipitation of Fe (2+) and Fe (3+) species at different temperatures may lead to crystallites of higher size as the temperature of the reaction increases. On the other hand, dynamic light scattering investigations and dielectric measurements rather point to the similar colloidal size of the entities existing in their aqueous or solid-state dispersions, irrespective of the size of the primary nanocrystallites. Significant enhancement of the stability of the colloids, even in the presence of high electrolyte concentrations, is furnished after the addition of relatively small amounts of poly(vinyl alcohol), and the stabilization mechanism is discussed in terms of the various forces participating in the system. The experimental results suggest that the increased colloidal stability is triggered from the particles' decrease of velocity rather than from steric (entropic) effects originating from polymer absorption.

“Nanocasting”: Using SBA-15 Silicas as Hard Templates to Obtain Ultrasmall Monodispersed γ-Fe2O3 Nanoparticles

This work describes the use of mesoporous SBA-15 silicas as hard templates for the size-controlled synthesis of oxide nanoparticles, with the pores acting as nanoscale reactors. This fundamental work is mainly aimed at understanding unresolved issues concerning the occurrence and size dependence of phase transitions in oxide nanocrystals. Aqueous solutions of Fe(NO3)3*9H2O are deposited inside the pores of SBA-15 silicas with mesopore diameters of 4.3, 6.6, and 9.5 nm. By calcination, the nitrate salt transforms into FeOx oxides. The XRD peaks of nanocrystals are broad and overlapping, resulting in ambiguities attributed to a given allotropic variety of Fe2O3 (alpha, epsilon, or gamma) or Fe3O4. The association of XRD, SAED, and Raman information is necessary to solve these ambiguities. The metastable gamma-Fe2O3 variety is selectively formed at low Fe/Si atomic ratio (ca. 0.20) and when a low calcination temperature is used (773 or 873 K followed by quenching to room temperature once the targeted temperature is reached). The small size dispersion of the patterned nanoparticles, suggested on a local scale by TEM, is confirmed statistically by magnetic measurements. The nanoparticles have a superparamagnetic behavior around room temperature. Their magnetic moments (from 220 to 370 mB), their sizes (from 4.0 to 4.8 nm), and their blocking temperatures (from 36 to 58 K) increase with the silica template mesopore diameter. Their magnetic properties are compared to those of standard gamma-Fe2O3 nanoparticles of similar size, obtained by coprecipitation in water and stabilized by a citrate coating.