Electrochemical characterisation of dental alloys: its possibilities and limitations

The Video Microscopy-Linked Electrochemical Cell: An Innovative Method to Improve Electrochemical Investigations of Biodegradable Metals

An innovative, miniature video-optical-electrochemical cell was developed and tested that allows for the conducting of electrochemical corrosion measurements and simultaneous microscopic observations over a small, well-defined surface area of corroding or degrading samples. The setup consisted of a miniature electrochemical cell that was clamped onto the metal sample and fixed under a video microscope before being filled with electrolyte. The miniature cell was comprised of afferent/efferent electrolyte ducts as well as a connection to the Mini Cell System (MCS) for electrochemical measurements. Consequently, all measured and induced currents and voltages referred to the same small area corroding completely within the field of view of the microscope, thus allowing for real-time observation and linking of surface phenomena such as hydrogen evolution and oxide deposition to electrochemical data. The experimental setup was tested on commercial purity (cp) and extra-high purity (XHP) magnesium (Mg) samples using open circuit potential and cyclic voltammetry methods under static and flowing conditions. The corrosion potential was shifted more anodically for cp Mg in comparison to XHP Mg under dynamic conditions. The corrosion current assessed from the cyclic voltametric curves were higher for the cp Mg in comparison to XHP Mg. However, there were no differences between static and flow conditions in the case of XHP Mg in contrast to cp Mg, where the current density was two times higher at dynamic conditions. The measurements and observations with this new method pave the way for a more detailed understanding of magnesium corrosion mechanisms, thus improving predictive power of electrochemical corrosion measurements on newly developed magnesium or other biodegradable alloys applied for medical devices. Different electrochemical tests can be run under various conditions, while being easy to set up and reproduce as well as being minimally destructive to the sample.

Metallurgical and electrochemical characterization of contemporary silver-based soldering alloys

OBJECTIVE

To investigate the microstructure, hardness, and electrochemical behavior of four contemporary Ag-based soldering alloys used for manufacturing orthodontic appliances.

MATERIALS AND METHODS

The Ag-based alloys tested were Dentaurum Universal Silver Solder (DEN), Orthodontic Solders (LEO), Ortho Dental Universal Solder (NOB), and Silver Solder (ORT). Five disk-shaped specimens were produced for each alloy, and after metallographic preparation their microstructural features, elemental composition, and hardness were determined by scanning electron microscopy with energy-dispersive X-ray (EDX) microanalysis, X-ray diffraction (XRD) analysis, and Vickers hardness testing. The electrochemical properties were evaluated by anodic potentiodynamic scanning in 0.9% NaCl and Ringer's solutions. Hardness, corrosion current (Icorr), and corrosion potential (Ecorr) were statistically analyzed by one-way analysis of variance and Tukey test (α=.05).

RESULTS

EDX analysis showed that all materials belong to the Ag-Zn-Cu ternary system. Three different mean atomic contrast phases were identified for LEO and ORT and two for DEN and NOB. According to XRD analysis, all materials consisted of Ag-rich and Cu-rich face-centered cubic phases. Hardness testing classified the materials in descending order as follows: DEN, 155±3; NOB, 149±3; ORT, 141±4; and LEO, 136±8. Significant differences were found for Icorr of NOB in Ringer's solution and Ecorr of DEN in 0.9% NaCl solution.

CONCLUSION

Ag-based soldering alloys demonstrate great diversity in their elemental composition, phase size and distribution, hardness, and electrochemical properties. These differences may anticipate variations in their clinical performance.

Electrochemical corrosion and surface analyses of a ni-cr alloy in bleaching agents

PURPOSE

The aim of this study was to evaluate the corrosion behavior of a Ni-Cr dental casting alloy subjected to 10% hydrogen peroxide (HP) and 10% carbamide peroxide (CP) bleaching solutions and to determine the composition of the surface oxide layer formed on the alloy specimens.

MATERIALS AND METHODS

Ten cylindrical specimens (4 mm in diameter × 25 mm in height) were cast from a Ni-Cr alloy (Wiron 99) and divided into two groups (n = 5). A potentiodynamic polarization test was used to compare the corrosion rates of specimens in HP and CP (pH = 6.5). Before cyclic polarization tests, all alloy specimens were allowed to reach a steady open circuit potential (Ecorr ) for a period of 1 hour. Then tests were initiated at 100 mV versus standard calomel electrode (SCE) below Ecorr and scanned at a rate of 1 mV/s in the anodic direction until reaching 1000 mV over the Ecorr value. The scan then was reversed back to the Ecorr of the specimens. The open circuit potentials (Ecorr ) and the current densities (Icorr ) were determined using the anodic Tafel regions extrapolating from the curves. Differences in Ecorr and Icorr were determined using one-way ANOVA (α = 0.05). In addition, corrosion rates were calculated from these curves. Before and after polarization tests, a scanning electron microscope (SEM) examination accompanied by energy dispersive X-ray spectroscopy (EDS) was used to analyze the surface morphology. The surface characterization of the passive film formed on alloy specimens was also performed by using X-ray photoelectron spectroscopy (XPS).

RESULTS

In this study, bleaching agents had an effect on the anodic process for two groups. Although no statistical difference was identified between the groups for both corrosion parameters, results indicated that the effect of CP on the corrosion behavior was less than that of HP. These results agreed with the SEM observations. XPS data showed that oxide layers formed on all groups contained mainly Cr2 O3 , NiO, and MoO3 , and the amounts of oxides formed on CP-treated specimens were higher than HP treated ones. Also, molybdenum rates were increased with CP application compared to HP.

CONCLUSIONS

The comparison of the effects of the two bleaching agents at 10% showed that the alloy suffered less corrosion with CP than HP. This result was also confirmed by the SEM and XPS data. The presence of Mo on the oxide layer affected the oxide layer, leading to lower corrosion rates.