Cavity formation and stress-oscillation during the tensile test of injection molded specimens made of PET

Isotactic Poly(propylene oxide): A Photodegradable Polymer with Strain Hardening Properties

Leakage and accumulation of highly stable commercial plastics has led to substantial contamination of the environment. Highly isotactic poly(propylene oxide) (iPPO) was investigated as a potential high-strength thermoplastic with greater susceptibility toward degradation under ambient conditions. Various stereoregular forms of iPPO including enantiopure, enantioenriched, racemic, and stereoblock were synthesized with a single catalyst architecture in the presence of chain transfer agents. These materials were found to possess the same approximate ultimate tensile strength (UTS) via uniaxial tensile elongation analysis (∼75 MPa). A serrated tensile response corresponding to stress oscillations was observed in all forms of iPPO. An investigation on strain rate dependence showed that an increase in strain rate results in the decay and disappearance of the serrated response. Further evaluation of iPPO revealed its dramatic strain hardening afforded an UTS comparable to that of nylon-6,6. Exposing iPPO to UVA light (365 nm) resulted in photolytic degradation. Following 30 days of continuous exposure at 250 μW cm^-2, the M_n decreased from 93 kDa to 21 kDa, while samples not exposed to UVA light remained unchanged. Through selective stabilization with antioxidant additives, we believe iPPO could be a suitable replacement for nylon-6,6 in environmentally susceptible applications.

Stress-oscillation behaviour of semi-crystalline polymers: the case of poly(butylene succinate)

Stress oscillation has been observed in a number of linear thermoplastic polymers during the cold-drawing process, where the polymers exhibit periodic self-excited oscillatory neck propagation. However, the origin of the mechanical stress oscillation process and its relationship with the crystalline morphology of the polymer are still under debate. In this work, we revisit the stress oscillation behavior by studying a semi-crystalline polyester, poly(butylene succinate) (PBS), a biodegradable polymer suitable for biomedical and packaging applications. Stress oscillation of PBS is observed when deformed at a range of elongation rates from 10 to 200 mm min-1, and the fluctuation magnitude decays as the deformation temperature increases from 23 to 100 °C. Periodic transparent/opaque bands form during necking of PBS, which consists of alternating regions of highly oriented crystalline zones and microcavities due to crazing and voiding, although the degree of crystallinity did not change significantly in the bands. Simultaneous small- and wide-angle X-ray scattering confirms that the alternating stress increases, as shown in the stress-strain curves, correspond to the appearance of the transparent bands in the sample, and the abrupt drop of the stress is the result of voiding during the neck propagation. The voiding and cavitation are ultimately responsible for the stress oscillation process in PBS. The in-depth analysis of this work is important in understanding and controlling the occurrence of instabilities/cavitation during polymer processing such as film blowing, biaxial stretching and injection moulding of biodegradable polymer materials.