Manganese oxide increases bleaching efficacy and reduces the cytotoxicity of a 10% hydrogen peroxide bleaching gel

Influence of coating dental enamel with a TiF4-loaded polymeric primer on the adverse effects caused by a bleaching gel with 35% H2O2

OBJECTIVE

To evaluate whether coating enamel with a polymeric primer (PPol) containing titanium tetrafluoride (TiF4) before applying a bleaching gel with 35% H2O2 (35% BG) increases esthetic efficacy, prevents changes in morphology and hardness of enamel, as well as reduces the cytotoxicity from conventional in-office bleaching.

MATERIALS AND METHODS

Standardized enamel/dentin discs were stained and bleached for 45 min (one session) with 35% BG. Groups 2TiF4, 6TiF4, and 10TiF4 received the gel on the enamel previously coated with PPol containing 2 mg/mL, 6 mg/mL, or 10 mg/mL, respectively. No treatment or application of 35% BG directly on enamel were used as negative control (NC), and positive control (PC), respectively. UV-reflectance spectrophotometry (CIE L*a*b* system, ΔE00, and ΔWI, n = 8) determined the bleaching efficacy of treatments. Enamel microhardness (Knoop, n = 8), morphology, and composition (SEM/EDS, n = 4) were also evaluated. Enamel/dentin discs adapted to artificial pulp chambers (n = 8) were used for trans-amelodentinal cytotoxicity tests. Following the treatments, the extracts (culture medium + bleaching gel components diffused through the discs) were collected and applied to odontoblast-like MDPC-23 cells, which were assessed concerning their viability (alamarBlue, n = 8; Live/Dead, n = 4), oxidative stress (n = 8), and morphology (SEM). The amount of H2O2 in the extracts was also determined (leuco crystal violet/peroxidase, n = 8). The numerical data underwent one-criterion variance analysis (one-way ANOVA), followed by Tukey's test, at a 5% significance level.

RESULTS

Regarding the ΔE00, no difference was observed among groups 2TiF4, 6TiF4, and PC (p > 0.05). The ΔWI was similar between groups 2TiF4 and PC (p > 0.05). The ΔWI of group 6TiF4 was superior to PC (p < 0.05), and group 10TiF4 achieved the highest ΔE00 and ΔWI values (p < 0.05). Besides limiting enamel microstructural changes compared to PC, group 10TiF4 significantly increased the hardness of this mineralized dental tissue. The highest cellular viability occurred in 10TiF4 compared to the other bleached groups (p < 0.05). Trans-amelodentinal H2O2 diffusion decreased in groups 2TiF4, 6TiF4, and 10TiF4 in comparison with PC (p < 0.05).

CONCLUSION

Coating enamel with a PPol containing TiF4 before applying a 35% BG may increase enamel microhardness and esthetic efficacy and reduce the trans-amelodentinal cytotoxicity of conventional in-office tooth bleaching. The PPol containing 10 mg/mL of TiF4 promoted the best outcomes.

Catalysis-based approaches with biopolymers and violet LED to improve in-office dental bleaching

This in vitro experimental investigation aimed to evaluate the impact of the combined application of a nanofiber scaffold (NS), a polymeric catalyst primer (PCP) containing 10 mg/mL of heme peroxidase enzyme, and violet LED (LEDv) on the esthetic efficacy (EE), trans-amelodentinal cytotoxicity (TC), and procedural duration of conventional in-office bleaching therapy. To achieve this, 96 standardized enamel/dentin discs were individually placed in artificial pulp chambers. A 35% hydrogen peroxide (H2O2) bleaching gel was administered for 45, 30, or 15 min to the enamel, either previously coated with NS + PCP or left uncoated, followed by irradiation with LEDv for 15 min or no irradiation. The established groups were as follows: G1, negative control (no treatment); G2, 35% H2O2/45 min; G3, NS + PCP + LEDv; G4, NS + PCP + 35%H2O2/45 min + LEDv; G5, NS + PCP + 35%H2O2/30 min + LEDv; and G6, NS + PCP + 35%H2O2/15 min + LEDv. Extracts (culture medium + gel components diffused through the discs) were collected and applied to odontoblast-like MDPC-23 cells. EE (ΔE00 and ΔWI) and TC were assessed using ANOVA/Tukey analysis (p < 0.05). The EE analysis revealed no statistical differences between G6 and G2 (p > 0.05). Cells in G6 exhibited higher viability and lower oxidative stress compared to other bleached groups (p < 0.05). In conclusion, employing NS + PCP + LEDv to catalyze a 35%H2O2 bleaching gel applied for 15 min to the enamel resulted in successful esthetic improvements and reduced the cytotoxicity commonly linked with traditional in-office bleaching procedures.

Can different agents reduce the damage caused by bleaching gel to pulp tissue? A systematic review of basic research

Objectives

This study aimed to investigate the effectiveness of different topical/systemic agents in reducing the damage caused by bleaching gel to pulp tissue or cells.

Materials and Methods

Electronic searches were performed in July 2023. In vivo and in vitro studies evaluating the effects of different topical or systemic agents on pulp inflammation or cytotoxicity after exposure to bleaching agents were included. The risk of bias was assessed.

Results

Out of 1,112 articles, 27 were included. Nine animal studies evaluated remineralizing/anti-inflammatories agents in rat molars subjected to bleaching with 35%-38% hydrogen peroxide (HP). Five of these studies demonstrated a significant reduction in inflammation caused by HP when combined with bioglass or MI Paste Plus (GC America), or following KF-desensitizing or Otosporin treatment (n = 3). However, orally administered drugs did not reduce pulp inflammation (n = 4). Cytotoxicity (n = 17) was primarily assessed using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide assay on human dental pulp cells and mouse dental papilla Cell-23 cells. Certain substances, including sodium ascorbate, butein, manganese chloride, and peroxidase, were found to reduce cytotoxicity, particularly when applied prior to bleaching. The risk of bias was high in animal studies and low in laboratory studies.

Conclusions

Few in vivo studies have evaluated agents to reduce the damage caused by bleaching gel to pulp tissue. Within the limitations of these studies, it was found that topical agents were effective in reducing pulp inflammation in animals and cytotoxicity. Further analyses with human pulp are required to substantiate these findings.

Trial Registration

PROSPERO Identifier: CRD42022337192.

Effects of experimental bleaching gels containing co-doped titanium dioxide and niobium pentoxide combined with violet light

OBJECTIVES

The objective of the study is to evaluate the bleaching potential of 6% hydrogen peroxide (6% HP) gels containing NF_TiO2 or Nb2O5 irradiated with a violet LED light and the effects on enamel mineral content and surface morphology.

METHODS

Particles were synthesized, and experimental gels were chemically analyzed by preliminary and accelerated stability tests, pH, and HP decomposition rate. Bovine enamel blocks were treated with 6% HP gels containing (n = 10): 5% NF_TiO2, 5% Nb2O5, 2.5% NF_TiO2 + 2.5% Nb2O5 or without particles (6% HP), irradiated or not with LED, and the control was treated with 35% HP. Color (∆E00) and whitening index (∆WID) variations, surface microhardness (SH), average roughness (∆Ra), Ca-P concentration (EDS), and enamel morphology (SEM) were assessed. Bleaching was performed in 3 sessions of 30 min and 7-day intervals. Data were submitted to two- (pH, decomposition rate, ∆E00, and ∆WID) or three-way ANOVA and Bonferroni (SH), Kruskal-Wallis (∆Ra), and Dunnet tests (α = 0.05).

RESULTS

No changes in the gel's color, odor, or translucency were observed. The pH (6 to 6.5) remained stable over time, and light irradiation boosted the HP decomposition rate. NF_TiO2 and Nb2O5-containing gels displayed higher ∆E00 and ΔWID when light-irradiated (p < 0.05). Nb2O5 and Nb2O5 + NF_TiO2 decreased enamel SH (p < 0.05), but no SH changes were found among groups (p > 0.05). No differences among groups were noted in ∆Ra, Ca-P content, and enamel morphology after treatments (p > 0.05).

CONCLUSION

Experimental light-irradiated 6% HP gels containing NF_TiO2 or Nb2O5 were chemically stable and exhibited bleaching potential comparable with 35% HP.

CLINICAL RELEVANCE

Low-concentrated HP gels containing NF_TiO2 or Nb2O5 and light-irradiated stand as a possible alternative to in-office bleaching.

Influence of violet LED and fluoride-containing carbamide peroxide bleaching gels on early-stage eroded/abraded teeth

PURPOSE

This study evaluated enamel with early-stage erosion/abrasion following bleaching with 20% and 45% carbamide peroxide (CP) gels containing fluoride (F) and irradiated with violet LED (LED).

METHODS

Enamel blocks were immersed in 1% citric acid (5 min) and artificial saliva (120 min) three times to produce early-stage enamel erosion. Simulated toothbrushing was performed only after the first saliva immersion, to provoke enamel abrasion. The erosive/abraded enamel samples were submitted to (n=10): LED/CP20, CP20, LED/CP20_F, CP20_F, LED/CP45, CP45, LED/CP45_F, CP45_F, LED, and control (without treatment). The pH of the gels was assessed, and color (ΔE₀₀) and whiteness index (ΔWI_D) changes were calculated after cycling (T₁), and 7 days from bleaching (T₂). Enamel surface roughness average (Ra) and Knoop microhardness (kg/mm², %SHR) were evaluated at baseline (T₀) at T₁ and T_2. Scanning electron microscopy evaluated the enamel surface morphology at T₂.

RESULTS

The gels' pH was neutral and CP20 and CP45 exhibited no differences in ΔE₀₀ and ΔWI_D (p>0.05) but LED increased these parameters for CP20_F and CP45. Erosion/abrasion significantly decreased mean kg/mm², and the LED group was the only one not increasing microhardness after bleaching (p>0.05). None of the groups fully recovered the initial microhardness. All groups exhibited %SHR similar to the control (p>0.05) and the increase in Ra was detected only after erosion/abrasion. CP20_F groups exhibited a more preserved enamel morphology.

CONCLUSION

Light irradiation combined with low-concentrated CP gel promoted a bleaching effect comparable to the high-concentrated CP. The bleaching protocols did not adversely impact the surface of early-stage eroded/abraded enamel.