Surface modified TiO2/reduced graphite oxide nanocomposite anodes for lithium ion batteries

Efficient photoelectrocatalytic degradation of azo-dyes over polypyrrole/titanium oxide/reduced graphene oxide electrodes under visible light: Performance evaluation and mechanism insights

Herein, polypyrrole/titanium oxide/reduced graphene oxide (PTi/r-GO) electrodes were prepared and successfully applied for the photoelectrocatalytic (PEC) degradation of methyl orange (MO) under visible light. Polypyrrole-TiO₂ composites rich in p-n heterojunctions were first prepared, then modified with r-GO to improve the electrical conductivity and facilitate charge separation under visible light irradiation. The obtained PTi/r-GO composites were then deposited onto a titanium mesh, which served as the working electrode in PEC experiments. A MO removal efficiency of 93% was achieved in 50 min using PTi/r-GO electrode under PEC conditions (Xe lamp, λ > 420 nm, bias of 0.6 V, 0.1 M Na₂SO₄ electrolyte), which was far higher than MO removal efficiencies under electrocatalytic oxidation (22%) or photocatalytic oxidation (47%) conditions. This confirmed that excellent activity of the PTi/r-GO electrode under PEC conditions was due to a combination of electrochemical and photocatalytic oxidation processes (involving •OH and •O₂^- generation). Further, PTi/r-GO was very stable under the applied PEC conditions, with the MO removal efficiency remaining >90% after five cycles. PEC degradation pathways for MO on PTi/r-GO were explored, with a number of key intermediates in the MO mineralization process identified. Results demonstrate that PEC electrodes combining p-type polypyrrole, n-type TiO₂ and rGO are very effective in the treatment of hazardous organic compounds in wastewater.

Graphitic nitrogen in carbon catalysts is important for the reduction of nitrite as revealed by naturally abundant 15N NMR spectroscopy

Metal-free nitrogen-doped carbon is considered as a green functional material, but the structural determination of the atomic positions of nitrogen remains challenging. We recently demonstrated that directly-excited solid state 15N NMR (ssNMR) spectroscopy is a powerful tool for the determination of such positions in N-doped carbon at natural 15N isotope abundance. Here we report a green chemistry approach for the synthesis of N-doped carbon using cellulose as a precursor, and a study of the catalytic properties and atomic structures of the related catalyst. N-doped carbon (NH3) was obtained by the oxidation of cellulose with HNO3 followed by ammonolysis at 800 °C. It had a N content of 6.5 wt% and a surface area of 557 m2 g-1, and 15N ssNMR spectroscopy provided evidence for graphitic nitrogen besides regular pyrrolic and pyridinic nitrogen. This structural determination allowed probing the role of graphitic nitrogen in electrocatalytic reactions, such as the hydrogen evolution reaction (HER), oxygen evolution reaction (OER), and nitrite reduction reaction. The N-doped carbon catalyst (NH3) showed higher electrocatalytic activities in the OER and HER under alkaline conditions and higher activity for nitrite reduction, as compared with a catalyst prepared by the carbonization of HNO3-treated cellulose in N2. The electrocatalytic selectivity for nitrite reduction of the N-doped carbon catalyst (NH3) was directly related to the graphitic nitrogen functions. Complementary structural analyses by means of 13C and 1H ssNMR, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and low-temperature N2 adsorption were performed and provided support to the findings. The results show that directly-excited 15N ssNMR spectroscopy at natural 15N abundance is generally capable of providing information on N-doped carbon materials if relaxation properties are favorable. It is expected that this approach can be applied to a wide range of solids with an intermediate concentration of N atoms.