Er:YAG laser-induced damage to a dental composite in simulated clinical scenarios for inadvertent irradiation: an in vitro study

The efficacy of Er,Cr:YSGG laser and contemporary universal adhesive systems on composite resin repair bond strength: an in vitro study

The aim of this study is to investigate the repair bond strength of composite resin following three different surface treatments (bur-grinding, silanization, and Er,Cr:YSGG laser irradiation) using various universal adhesives. A total of 160 resin composite specimens, produced in cylindrical form (6 × 2 mm) with a nanohybrid composite resin within metal molds, were subjected to 5000 cycles of aging in a thermocycler. The aged samples were categorized into four groups based on surface treatments: control, bur, silane, and Er,Cr:YSGG laser. Following surface treatments, the specimens underwent repair using the same resin composite and four different adhesive systems: Tokuyama Universal Bond (TUB), Prime Bond Universal (PBU), Gluma Bond Universal (GBU), and Clearfil SE Bond (CSB). Subsequently, the specimens were subjected to shear forces, and statistical analysis was performed using two-way ANOVA and Tukey tests (p < 0.05). The failure modes were examined using a stereomicroscope, and the surface topography of the roughened resin composite was assessed through scanning electron microscopy (SEM). Results indicated that silane + GBU exhibited the highest shear bond strength (SBS) (15.61 MPa) while control + TUB showed the lowest SBS (7.63 MPa). Silane demonstrated significantly higher SBS values (p ≤ 0.05), with no significant difference observed between bur and laser methods (p = 0.998). It is recommended to include an additional silanization step before applying universal adhesive, as it effectively enhances the bond strength of the repaired composite.

In vitro studies the influence of Nd: YAG laser on dental enamels

The present work aimed at assessing chemical, topographical, and morphological changes induced by Nd : YAG laser treatment of dental enamels by means of energy dispersive X-ray spectroscopy (EDS), atomic force microscopy (AFM), and scanning electron microscopy (SEM). Fifteen human enamel specimens were obtained, three of samples were kept untreated as a control while the others twelve samples were equally divided into four groups where each group have a three samples according to treating approach as: G1:(untreated);G2: (treated with Nd:YAG laser, 100 mJ/pulse,10 Hz/1064nm); G3(treated with Nd:YAG laser, 500 mJ/pulse, 10 Hz/1064nm); G4(treated with Nd:YAG laser 1000 mJ/pulse, 10 Hz/1064nm), and finally G5(treated with Nd:YAG laser, 1000 mJ/pulse, 10 Hz/532nm) respectively. Beside many craters and cracks, the AFM results showed fractures with depths of 19.23 nm, 174.7 nm, 216.9 nm, 207.4 nm and 156.5 nm and width of 559.2 nm, 833.4 nm, 1115 nm, 695.0 nm, and 5142 nm for all Groups respectively. The highest surface roughness was found in G5 with 111.4 nm while the lowest surface roughness was found in G1 to be 14.3 nm. The inside surface of the fissures was also rough. The SEM micrographs revealed modifications to the morphology. EDS was used to measure the phosphorous (P), calcium (Ca), oxygen (O), and carbon (C) percentages presented in crater areas and their surroundings, Ca, P, O, and C levels were observed to vary significantly at the crater and its rim, a lower percentage of C wt% were realized corresponding to laser treatment of 1000 mJ/Pulse laser energy. However, it was not feasible to recognize a specific chemical arrangement in the craters. It is also concluded that the higher depth and particular edge of ablated part when teeth were irradiated by laser with 1000 mJ/10Hz/1064nm.

Evaluation of repair bond strength of a dental CAD/CAM resin composite after surface treatment with two Er,Cr:YSGG laser protocols following artificial aging

The aim of the present study was to evaluate the impact of two Er,Cr:YSGG laser surface treatments on the repair bond strength of a dental CAD/CAM resin composite (Brilliant Crios) after artificial aging. Twenty-four resin-based CAD/CAM blocks were cut and 48 rectangular slabs (3 x 12 x 14 mm) were prepared. Preliminary SEM observations indicated the most favorable laser settings regarding surface modification of the tested restorative material. The CAD/CAM specimens were then divided into 4 groups (n=12) based on their surface pretreatment: no treatment, air abraded with 50-μm Al2O3 particles, and laser irradiated with two different protocols using Er,Cr:YSGG laser with average power 3.5 and 4.5 W, pulse repetition rate 35 and 50 Hz, and pulse energy 100 and 90 mJ, respectively. After surface treatments each group followed a bonding protocol with silane and a flowable resin composite was used to prepare 48 microrods. Half of the microrods of each group were subjected on shear bond strength (SBS) test (chisel-shaped blade, load cell of 500 N, crosshead speed of 1 mm/min) after 24 h, while the other half underwent artificial aging (15,000 cycles, 5-55 °C) and then SBS test. The debonded specimens were examined under an optical microscope to determine the failure mode. All specimens were also evaluated using SEM to assess the surface topography after the treatments. The results showed that SBS significantly decreased after thermocycling in all the experimental groups (p<0.05). Control group presented much lower SBS values than the other groups after both 24 h and thermocycling (p<0.05). The highest values of SBS exhibited air-abrasion group (p<0.05), followed by the two laser groups, which did not differ to each other (p>0.05). The results of the current study indicated that Er,Cr:YSGG laser irradiation can be an alternative treatment for repairing the tested resin-based CAD/CAM restorative material.