Phenyl siloxane hybrid xerogels: structure and porous texture

Tunability of Hybrid Silica Xerogels: Surface Chemistry and Porous Texture Based on the Aromatic Precursor

The interest in new materials with specific properties has increased because they are essential for the environmental and technological needs of our society. Among them, silica hybrid xerogels have emerged as promising candidates due to their simple preparation and tunability: when they are synthesised, depending on the organic precursor and its concentration, their properties can be modulated, and thus, it is possible to prepare materials with à la carte porosity and surface chemistry. This research aims to design two new series of silica hybrid xerogels by co-condensation of tetraethoxysilane (TEOS) with triethoxy(p-tolyl)silane (MPhTEOS) or 1,4-bis(triethoxysilyl)benzene (Ph(TEOS)₂ and to determine their chemical and textural properties based on a variety of characterisation techniques (FT-IR, ²⁹Si NMR, X-ray diffraction and N₂, CO₂ and water vapour adsorption, among others). The information gathered from these techniques reveals that depending on the organic precursor and its molar percentage, materials with different porosity, hydrophilicity and local order are obtained, evidencing the easy modulation of their properties. The ultimate goal of this study is to prepare materials suitable for a variety of applications, such as adsorbents for pollutants, catalysts, films for solar cells or coatings for optic fibre sensors.

Novel Silica Hybrid Xerogels Prepared by Co-Condensation of TEOS and ClPhTEOS: A Chemical and Morphological Study

The search for new materials with improved properties for advanced applications is, nowadays, one of the most relevant and booming fields for scientists due to the environmental and technological needs of our society. Within this demand, hybrid siliceous materials, made out of organic and inorganic species (ORMOSILs), have emerged as an alternative with endless chemical and textural possibilities by incorporating in their structure the properties of inorganic compounds (i.e., mechanical, thermal, and structural stability) in synergy with those of organic compounds (functionality and flexibility), and thus, bestowing the material with unique properties, which allow access to multiple applications. In this work, synthesis using the sol-gel method of a series of new hybrid materials prepared by the co-condensation of tetraethoxysilane (TEOS) and 4-chlorophenyltriethoxysilane (ClPhTEOS) in different molar ratios is described. The aim of the study is not only the preparation of new materials but also their characterization by means of different techniques (FT-IR, ²⁹Si NMR, X-ray Diffraction, and N₂/CO₂ adsorption, among others) to obtain information on their chemical behavior and porous structure. Understanding how the chemical and textural properties of these materials are modulated with respect to the molar percentage of organic precursor will help to envisage their possible applications: From the most conventional such as catalysis, adsorption, or separation, to the most advanced in nanotechnology such as microelectronics, photoluminescence, non-linear optics, or sensorics.

Modification of Silica Xerogels with Polydopamine for Lipase B from Candida antarctica Immobilization

Silica xerogels have been proposed as a potential support to immobilize enzymes. Improving xerogels’ interactions with such enzymes and their mechanical strengths is critical to their practical applications. Herein, based on the mussel-inspired chemistry, we demonstrated a simple and highly effective strategy for stabilizing enzymes embedded inside silica xerogels by a polydopamine (PDA) coating through in-situ polymerization. The modified silica xerogels were characterized by scanning and transmission electron microscopy, Fourier tranform infrared spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy and pore structure analyses. When the PDA-modified silica xerogels were used to immobilize enzymes of Candida antarctica lipase B (CALB), they exhibited a high loading ability of 45.6 mg/gsupport, which was higher than that of immobilized CALB in silica xerogels (28.5 mg/gsupport). The immobilized CALB of the PDA-modified silica xerogels retained 71.4% of their initial activities after 90 days of storage, whereas the free CALB retained only 30.2%. Moreover, compared with the immobilization of enzymes in silica xerogels, the mechanical properties, thermal stability and reusability of enzymes immobilized in PDA-modified silica xerogels were also improved significantly. These advantages indicate that the new hybrid material can be used as a low-cost and effective immobilized-enzyme support.

Effect of sodium bicarbonate solution on methyltrimethoxysilane-derived silica aerogels dried at ambient pressure

Here we present an economical ambient pressure drying method of preparing monolithic silica aerogels from methyltrimethoxysilane precursor while using sodium bicarbonate solution as the exchanging solvent. We prepared silica aerogels with a density and a specific surface area of 0.053 g·cm−3 and 423 m2·g−1, respectively. The average pore diameter of silica aerogels is 23 nm as the pore specific volume is 1.11 cm3·g−1. Further, the contact angle between water droplet and the surface of silica aerogels in specific condition can be as high as 166°, which indicates a super-hydrophobic surface of aerogels.