Dental resin materials in vivo - TEM results after one year: a pilot study

Evaluation of the bond strength between aged composite cores and luting agent

PURPOSE

The aim of this study was to evaluate effect of different surface treatment methods on the bond strength between aged composite-resin core and luting agent.

MATERIALS AND METHODS

Seventy-five resin composites and also seventy-five zirconia ceramic discs were prepared. 60 composite samples were exposed to thermal aging (10,000 cycles, 5 to 55℃) and different surface treatment. All specimens were separated into 5 groups (n=15): 1) Intact specimens 2) Thermal aging-air polishing 3) Thermal aging- Er:YAG laser irradiation 4) Thermal aging- acid etching 5) Thermal-aging. All specimens were bonded to the zirconia discs with resin cement and fixed to universal testing machine and bond strength testing loaded to failure with a crosshead speed of 0.5 mm/min. The fractured surface was classified as adhesive failure, cohesive failure and adhesive-cohesive failure. The bond strength data was statistically compared by the Kruskal-Wallis method complemented by the Bonferroni correction Mann-Whitney U test. The probability level for statistical significance was set at α=.05.

RESULTS

Thermal aging and different surface treatment methods have significant effect on the bond strength between composite-resin cores and luting-agent (P<.05). The mean baseline bond strength values ranged between 7.07 ± 2.11 and 26.05 ± 6.53 N. The highest bond strength of 26.05 ± 6.53 N was obtained with Group 3. Group 5 showed the lowest value of bond strength.

CONCLUSION

Appropriate surface treatment method should be applied to aged composite resin cores or aged-composites restorations should be replaced for the optimal bond strength and the clinical success.

Effect of Mechanical Surface Treatment on the Repair Bond Strength of the Silorane-based Composite Resin

Background and aims. A proper bond must be created between the existing composite resin and the new one for successful repair. The aim of this study was to compare the effect of three mechanical surface treatments, using diamond bur, air abrasion, and Er,Cr:YSGG laser, on the repair bond strength of the silorane-based composite resin. Materials and methods. Sixty cylindrical composite resin specimens (Filtek Silorane) were fabricated and randomly divided into four groups according to surface treatment: group 1 (control group) without any mechanical surface treatment, groups 24 were treated with air abrasion, Er,Cr:YSGG laser, and diamond bur, respectively. In addition, a positive control group was assigned in order to measure the cohesive strength. Silorane bonding agent was used in groups 14 before adding the new composite resin. Then, the specimens were subjected to a shear bond strength test and data was analyzed using one-way ANOVA and post hoc Tukey tests at a significance level of P &0.05. The topographical effects of surface treatments were characterized under a scanning electron microscope. Results. There were statistically significant differences in the repair bond strength values between groups 1 and 2 and groups 3 and 4 (P &0.001). There were no significant differences between groups 1 and 2 (P = 0.98) and groups 3 and 4 (P= 0.97). Conclusion. Surface treatment using Er,Cr:YSGG laser and diamond bur were effective in silorane-based composite resin repair.

Investigation of mechanical properties of modern dental composites after artificial aging for one year

This in vitro study investigated the aging behavior of dental composites with regard to surface roughness (SR), Vickers hardness (VH) and flexural strength (FS), and the study elucidated the impact of artificial aging parameters. One hundred and sixty-five rectangular specimens were prepared from five composites (Filtek Supreme XT, Filtek Silorane, CeramX, Quixfil, experimental ormocer) and subjected to various artificial aging protocols (storage in distilled water/ethanol/artificial saliva for 7, 90 and 365 days; thermal cycling, 2 x 3000 cycles 5/55 degrees C). SR, VH and FS were determined at baseline and after each aging treatment. Means and standard deviations were calculated; statistical analysis was performed using three-way ANOVA and the Tukey-Kramer multiple comparison test (alpha=.05). The results showed a significant influence in the composite and aging duration on mechanical parameters; the aging medium did not have a significant influence on VH and FS, but there was a significant influence on SR. The highest overall VH was found for theexperimental ormocer; Filtek Silorane yielded the lowest values. For FS, the significantly highest values were found for Filtek Silorane, and the lowest values were found for the experimental ormocer. Prolonged aging periods (90 or 365 days) or thermal cycling led to significant decreases in both VH and FS and significant increases in SR. The findings of the current study indicate that composites differ significantly for SR and its mechanical properties with regard to FS and VH, as well as in aging behavior. Generally, artificial aging leads to a significant decrease in mechanical properties, which underlines the relevance of continuous improvement of dental composites.

Influence of artificial ageing on surface properties and Streptococcus mutans adhesion to dental composite materials

The aim of this in vitro study was to investigate the influence of artificial ageing on the surface properties and early Streptococcus mutans adhesion to current dental composites for the direct restoration of class II defects. Three hundred and thirty specimens each were prepared from five dental composites, and were randomly allotted to various artificial ageing protocols (storage in distilled water/ethanol/artificial saliva for 7/90/365 days; thermal cycling, 6,000 cycles 5/55 degrees C). Prior and after each treatment, surface roughness (R(a)) and hydrophobicity were determined, and S. mutans adhesion (ATCC 25175; 2.5 h, 37 degrees C) was simulated with and without prior exposition to human whole saliva (2 h, 37 degrees C). Adherence of S. mutans was determined fluorometrically. Means and standard deviations were calculated, and analyzed using three-way ANOVA and post-hoc analysis (alpha = 0.05). For both R(a) and S. mutans adherence to uncoated and saliva-coated specimens, significant influences of the composite material, the ageing medium and the ageing duration have been observed; for surface hydrophobicity, significant influences of the composite material and the ageing duration were found. For uncoated specimens, significant increases in S. mutans adhesion were observed with prolonged artificial ageing, whereas significant decreases in S. mutans adhesion were found for the saliva-coated specimens. The data indicate influences of the artificial ageing method on surface parameters such as R(a) and hydrophobicity as well as microbial adhesion. The results underline the relevance of saliva coating on the outcome of studies simulating microbial adhesion, and highlight differences in the susceptibility of dental composites for the adhesion of oral bacteria.

Surface properties and in vitro Streptococcus mutans adhesion to dental resin polymers

OBJECTIVES

This study aimed to characterize the surface properties of experimental resin polymers consisting of monomers differing in functionality and chain length, and to evaluate differences in Streptococcus mutans adhesion.

MATERIAL AND METHODS

Six resins were prepared (70/30 ratio UDMA/monomer); camphorquinone and ethyl-4-dimethylaminebenzoate were added for light activation. A conventional composite was used as a control. Surface free energy was determined prior and after saliva exposition (2 h, 37 degrees C). After saliva incubation (2 h, 37 degrees C), specimens were incubated with Streptococcus mutans NCTC 10449 for 2.5 h at 37 degrees C. Adherent bacteria were quantified by determining the relative substratum area covered by bacteria using SEM analysis, and by using a fluorometric assay for viable cell quantification.

RESULTS

No statistically significant differences in total surface free energies were found for uncoated specimens (mean total surface free energies ranging from 39.79 to 49.73 mJ/m(-2)); after saliva coating, statistically significant differences were observed for some of the polymers (mean total surface free energies ranging from 44.13 to 65.81 mJ/m(-2)). Few differences were observed between SEM and fluorescence quantification, finding statistically significant differences in streptococcal adhesion to the experimental polymers. Median bacteria surface coverage ranged from 1.4% for UDMA mixed with 1,10-decandiol dimethacrylate to 16.2% for the control composite material; lowest fluorescence intensities indicating lowest adhesion of bacteria were found for UDMA mixed with 1,10-decandiol dimethacrylate (median 712), and highest values indicating highest adhesion of bacteria were found for UDMA mixed with polyethyleneglycol (600) dimethacrylate (median 11974).

CONCLUSION

Streptococcus mutans adhesion appears to be different on polymers differing in monomer mixtures, yet correlations between substratum surface free energy and streptococcal adhesion were poor. Further studies are necessary to evaluate additional substratum surface properties and pellicle distribution and composition more thoroughly.