Structure of polyvinyl alcohol-borax ferrogels: a small angle neutron scattering study

Dual Properties of Polyvinyl Alcohol-Based Magnetorheological Plastomer with Different Ratio of DMSO/Water

Polyvinyl alcohol (PVA)-based magnetorheological plastomer (MRP) possesses excellent magnetically dependent mechanical properties such as the magnetorheological effect (MR effect) when exposed to an external magnetic field. PVA-based MRP also shows a shear stiffening (ST) effect, which is very beneficial in fabricating pressure sensor. Thus, it can automatically respond to external stimuli such as shear force without the magnetic field. The dual properties of PVA-based MRP mainly on the ST and MR effect are rarely reported. Therefore, this work empirically investigates the dual properties of this smart material under the influence of different solvent compositions (20:80, 40:60, 60:40, and 80:20) by varying the ratios of binary solvent mixture (dimethyl sulfoxide (DMSO) to water). Upon applying a shear stress with excitation frequencies from 0.01 to 10 Hz, the storage modulus (G′) for PVA-based MRP with DMSO to water ratio of 20:40 increases from 6.62 × 10⁻⁵ to 0.035 MPa. This result demonstrates an excellent ST effect with the relative shear stiffening effect (RSTE) up to 52,827%. In addition, both the ST and MR effect show a downward trend with increasing DMSO content to water. Notably, the physical state of hydrogel MRP could be changed with different solvent ratios either in the liquid-like or solid-like state. On the other hand, a transient stepwise experiment showed that the solvent’s composition had a positive effect on the arrangement of CIPs within the matrix as a function of the external magnetic field. Therefore, the solvent ratio (DMSO/water) can influence both ST and MR effects of hydrogel MRP, which need to be emphasized in the fabrication of hydrogel MRP for appropriate applications primarily with soft sensors and actuators for dynamic motion control.

Solvent Dependence of the Rheological Properties in Hydrogel Magnetorheological Plastomer

Chemically crosslinked hydrogel magnetorheological (MR) plastomer (MRP) embedded with carbonyl iron particles (CIPs) exhibits excellent magnetic performance (MR effect) in the presence of external stimuli especially magnetic field. However, oxidation and desiccation in hydrogel MRP due to a large amount of water content as a dispersing phase would limit its usage for long-term applications, especially in industrial engineering. In this study, different solvents such as dimethyl sulfoxide (DMSO) are also used to prepare polyvinyl alcohol (PVA) hydrogel MRP. Thus, to understand the dynamic viscoelastic properties of hydrogel MRP, three different samples with different solvents: water, DMSO, and their binary mixtures (DMSO/water) were prepared and systematically carried out using the oscillatory shear. The outcomes demonstrate that the PVA hydrogel MRP prepared from precursor gel with water shows the highest MR effect of 15,544% among the PVA hydrogel MRPs. However, the samples exhibit less stability and tend to oxidise after a month. Meanwhile, the samples with binary mixtures (DMSO/water) show an acceptable MR effect of 11,024% with good stability and no CIPs oxidation. Otherwise, the sample with DMSO has the lowest MR effect of 7049% and less stable compared to the binary solvent samples. This confirms that the utilisation of DMSO as a new solvent affects the rheological properties and stability of the samples.