Simultaneous removal of harmful anions from geothermal waters using OH- intercalated Mg-Fe-LDH: batch and field column studies

Regulation of Structure and Anion-Exchange Performance of Layered Double Hydroxide: Function of the Metal Cation Composition of a Brucite-like Layer

As anion-exchange materials, layered double hydroxides (LDHs) have attracted increasing attention in the fields of selective adsorption and separation, controlled drug release, and environmental remediation. The metal cation composition of the laminate is the essential factor that determines the anion-exchange performance of LDHs. Herein, we review the regulating effects of the metal cation composition on the anion-exchange properties and LDH structure. Specifically, the internal factors affecting the anion-exchange performance of LDHs were analyzed and summarized. These include the intercalation driving force, interlayer domain environment, and LDH morphology, which significantly affect the anion selectivity, anion-exchange capacity, and anion arrangement. By changing the species, valence state, size, and mole ratio of the metal cations, the structural characteristics, charge density, and interlayer spacing of LDHs can be adjusted, which affect the anion-exchange performance of LDHs. The present challenges and future prospects of LDHs are also discussed. To the best of our knowledge, this is the first review to summarize the essential relationship between the metal ion composition and anion-exchange performance of laminates, providing important insights for regulating the anion-exchange performance of LDHs.

Efficient and Fast Removal of Aqueous Tungstate by an Iron-Based LDH Delaminated in L-Asparagine

High concentrations of tungstate in aqueous systems pose a severe threat to the environment and human health. This study explored the potential of iron-based LDHs to remove tungstate from water. To improve its tungstate uptake capacity, environment-friendly L-asparagine was used to delaminate iron-based LDH synthesized via a coprecipitation method. The successful delamination was proved by AFM, revealing that the thickness of the obtained nanoparticles was approximately 1–2 times that of a single LDH layer. XRD, TEM, and XPS analyses confirmed that the delaminated LDHs were amorphous and ultrathin and had surface defects within their nanosheets that acted as active sites, leading to a very fast tungstate sorption rate and superior tungstate uptake capacity. Notably, the original layered structure of the L-asparagine-treated LDH was recovered upon its reaction with tungstate-bearing solutions, and therefore, the high availability of aqueous tungstate to the interlayer regions during the structural restoration of the delaminated iron-based LDH contributed to its excellent capability of tungstate removal as well. In addition, the tungstate uptake by the delaminated iron-based LDH was not affected substantially by the presence of coexisting anions, implying that the strong inner-sphere complexation between the tungstate and LDH layers with defects (i.e., Fe-O bonds) was the primary mechanism responsible for the tungstate removal. The delamination process described in this paper was validated to be an effective way to enhance the immobilization of tungstate by iron-based LDHs without inducing secondary pollutions, and delaminated iron-based LDHs are promising to be used extensively in the practice of treating tungstate-rich waters.