Zhang Y, Zhu Q, Su C, Li C. Electrochemical behavior of Mg electrode in sodium salt electrolyte system.
Front Chem 2022;
10:992400. [PMID:
36157046 PMCID:
PMC9500388 DOI:
10.3389/fchem.2022.992400]
[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/12/2022] [Accepted: 08/16/2022] [Indexed: 11/18/2022] Open
Abstract
A suitable electrolyte is crucial to enhancing the electrochemical performance of magnesium (Mg) batteries. Here, the influence of Na2SiO3 on the electrochemical behavior of AZ31B Mg alloy in the Na2SO4-NaNO3 composite electrolyte was investigated. The results revealed that the activation potential of the AZ31B Mg alloy first represented a negative shift and then a positive shift with the increase in Na2SiO3. The most negative activation potential (−1.51 V) and the lowest polarization (−3.20 V) were found when 6 mM of Na2SiO3 was added; no discharge hysteresis was observed, and the polarization resistance value (R1) was 3,806 Ω. After 24 h immersion in the composite electrolyte with Na2SiO3, more and wider cracks appeared on the alloy surface, where a thick, dense film was formed, showing excellent discharge performance and corrosion resistance.
Collapse