Evaluation and comparison of the effect of different surface preparations on bond strength of glass ionomer cement with nickel-chrome metal-ceramic alloy: a laboratory study

Bond strength of self-adhesive resin cement to base metal alloys having different surface treatments

Background

This study aimed to assess and compare the shear bond strength of self-etch and self-adhesive resin cement to nickel-chromium-cobalt alloy with different surface treatments.

Materials and Methods

In this in vitro study, a total of 120 disks were fabricated of VeraBond II base metal alloy. Specimens were divided into 15 groups of 8 based on the type of cement and surface treatment. The five surface treatments studied included sandblasting alone, application of Alloy Primer with and without sandblasting, and application of Metal Primer II with and without sandblasting. The three cement tested included Panavia F2.0, RelyX Unicem (RU), and G-Cem (GC). After receiving the respective surface treatments, the specimens were thermocycled for 1500 cycles and underwent shear bond strength testing. Data were analyzed using SPSS 20.0 and three-way analysis of variance. P values of the significant level of 0.05 were reported.

Results

The results exhibited that the mean bond strengths in sandblasted groups were higher than nonsandblasted one. These differences were significantly higher in the sandblasted groups of Panavia F2.0 and RU cement (P < 0.05). The mean bond strength values between GC and Panavia F2.0 were not statistically significant (P > 0.05). The highest bond strength was recorded for Panavia F2.0 with the surface treatment of both sandblasting and Metal Primer II.

Conclusion

Based on the results, sandblasting improves the shear bond strength of self-etch and self-adhesive resin cement to base metal alloys. The best results can be achieved with a combination of sandblasting and metal primers. The performance of resin cement depends on to their chemical composition, not to the type of system.

Comparison of the effect of different surface treatments on the bond strength of different cements with nickel chromium metal alloy: An in vitro study

Background

For success of any indirect metal restoration, a strong bond between cement and the intaglio surface of metal is imperative. The aim of this study is to evaluate and compare the effect of different surface treatment on the tensile and shear bond strength of different cements with nickel–chromium alloy.

Material and Methods

120 premolars were sectioned horizontally parallel to the occlusal surface to expose the dentin. Wax patterns were fabricated for individual tooth followed by casting them in nickel chromium alloy. 60 samples were tested for tensile bond strength, and the remaining 60 for shear bond strength. The samples were divided into three groups (of 20 samples each) as per the following surface treatment: oxidation only, oxidation and sandblasting, or oxidation, sandblasting followed by application of alloy primer. Each group was subdivided into 2 subgroups of 10 samples each, according to the bonding cement i.e RM-GIC and resin cement. Samples were subjected to thermocycling procedure followed by evaluation of bond strength.

Results

Two-way analyses of variance (ANOVA) was performed to compare the means of tensile and shear bond strength across type of surface treatment and cement, followed by post hoc parametric analysis. For all tests ‘p’ value of less than 0.05 was considered statistically significant.

Conclusions

The surface treatment of oxidation and sandblasting followed by application of alloy primer offered the maximum tensile and shear bond strength for both RM GIC and resin cement. Resin cement exhibited greater tensile and shear bond strength than RM-GIC for all the three surface treatment methods.

Key words:Resin cement, resin modified glass ionomer cement, oxidation, sandblasting, alloy primer, tensile bond strength, shear bond strength, universal testing machine.

Tensile strength of Ni-Cr copings subjected to inner surface sandblasting using different cementing agents: An in vitro study

OBJECTIVES

To evaluate the effect of thermal cycling and inner surface treatment with aluminum oxide at different granulations on the tensile strength of Ni-Cr copings cemented with different cementing agents.

MATERIALS AND METHODS

Ninety-six metal copings were manufactured and divided into two groups: before and after thermal cycling (n = 48). The copings of both groups were internally treated by sandblasting with aluminum oxide particles of 100 (n = 24) and 320 (n = 24) mesh. The copings were cemented on previously manufactured metal cores using zinc phosphate (n = 8), conventional glass ionomer (CGIC) (n = 8) and resin-modified glass ionomer (RMGIC) (n = 8) cements. The tensile strength before and after thermal cycling was then determined (Newtons).

RESULTS

The tensile strength before and after thermal cycling was significantly higher in copings cemented with RMGIC compared to CGIC (p < 0.05) and was similar to that for zinc phosphate (p > 0.05). Thermal cycling and sandblasting of the inner surface of the metal copings with different granulations did not influence retention (p > 0.05).

CONCLUSIONS

Zinc phosphate cements and RMGIC showed similar retention. Additionally, the retention of the cements was not influenced by either thermal cycling or the particle size of the aluminum oxide.