Surface characteristics and osteoblast cell response on TiN- and TiAlN-coated Ti implant

Ti(C, N) as Barrier Coatings

Metals and their alloys are materials that have long been used in stomatological prosthetics and orthodontics. The side effects of their application include reactions of the body such as allergies. Their source can be corrosion products as well as metal ions released in the corrosion process, which penetrate the surrounding tissue. In order to prevent the harming effect of metal alloys, intensive research has been performed to purify metal prosthetic restorations by way of modifying their surface. The study presents the investigation results of Ti(C, N)-type coatings applied to alloy Ni–Cr by means of the magnetronic method. Five coatings differing in the nitrogen and carbon content were investigated. The studies included the determination of the coatings’ chemical composition, construction, as well as the amount of ions released into the environment: distilled water, 0.9% NaCl and artificial saliva. The performed investigations showed that, in reference to an alloy without a coating, each coating constitutes a barrier reducing the amount of ions transferred into the examined solutions. So, Ti(C, N)-type coatings can be considered for biomedical applications as protective coatings of non-precious metal alloys.

Biological Behaviour and Enhanced Anticorrosive Performance of the Nitrided Superelastic Ti-23Nb-0.7Ta-2Zr-0.5N Alloy

The influence of gas nitriding surface treatment on the superelastic Ti-23Nb-0.7Ta-2Zr-0.5N alloy was evaluated. A thorough characterization of bare and nitrided Ti-based alloy and pure Ti was performed in terms of surface film composition and morphology, electrochemical behaviour, and short term osteoblast response. XPS analysis showed that the nitriding treatment strongly influenced the composition (nitrides and oxynitrides) and surface properties both of the substrate and of the bulk alloy. SEM images revealed that the nitrided surface appears as a similar dotted pattern caused by the formation of N-rich domains coexisting with less nitrided domains, while before treatment only topographical features could be observed. All the electrochemical results confirmed the high chemical stability of the nitride and oxynitride coating and the superiority of the applied treatment. The values of the corrosion parameters ascertained the excellent corrosion resistance of the coated alloy in the real functional conditions from the human body. Cell culture experiments with MG63 osteoblasts demonstrated that the studied biomaterials do not elicit any toxic effects and support cell adhesion and enhanced cell proliferation. Altogether, these data indicate that the nitrided Ti-23Nb-0.7Ta-2Zr-0.5N alloy is the most suitable substrate for application in bone implantology.

Surface characterization and biocompatibility of titanium alloys implanted with nitrogen by Hardion+ technology

In this study, the new Hardion+ micro-implanter technology was used to modify surface properties of biomedical pure titanium (CP-Ti) and Ti-6Al-4V ELI alloy by implantation of nitrogen ions. This process is based on the use of an electron cyclotron resonance ion source to produce a multienergetic ion beam from multicharged ions. After implantation, surface analysis methods revealed the formation of titanium nitride (TiN) on the substrate surfaces. An increase in superficial hardness and a significant reduction of friction coefficient were observed for both materials when compared to non-implanted samples. Better corrosion resistance and a significant decrease in ion release rates were observed for N-implanted biomaterials due to the formation of the protective TiN layer on their surfaces. In vitro tests performed on human fetal osteoblasts indicated that the cytocompatibility of N-implanted CP-Ti and Ti-6Al-4V alloy was enhanced in comparison to that of the corresponding non treated samples. Consequently, Hardion+ implantation technique can provide titanium alloys with better qualities in terms of corrosion resistance, cell proliferation, adhesion and viability.