Does Surface Topography Improve Electrochemical Behavior of Ti–6Al–4V Alloy in Different Saliva pH Levels?

A Comprehensive Review on the Corrosion Pathways of Titanium Dental Implants and Their Biological Adverse Effects

The main aim of this work was to perform a comprehensive review of findings reported by previous studies on the corrosion of titanium dental implants and consequent clinical detrimental effects to the patients. Most studies were performed by in vitro electrochemical tests and complemented with microscopic techniques to evaluate the corrosion behavior of the protective passive oxide film layer, namely TiO2. Results revealed that bacterial accumulation, dietary, inflammation, infection, and therapeutic solutions decrease the pH of the oral environment leading to the corrosion of titanium. Some therapeutic products used as mouthwash negatively affect the corrosion behavior of the titanium oxide film and promote changes on the implant surface. In addition, toothpaste and bleaching agents, can amplify the chemical reactivity of titanium since fluor ions interacting with the titanium oxide film. Furthermore, the number of in vivo studies is limited although corrosion signs have been found in retrieved implants. Histological evaluation revealed titanium macro- and micro-scale particles on the peri-implant tissues. As a consequence, progressive damage of the dental implants and the evolution of inflammatory reactions depend on the size, chemical composition, and concentration of submicron- and nanoparticles in the surrounding tissues and internalized by the cells. In fact, the damage of the implant surfaces results in the loss of material that compromises the implant surfaces, implant-abutment connections, and the interaction with soft tissues. The corrosion can be an initial trigger point for the development of biological or mechanical failures in dental implants.

Synergistic interactions between corrosion and wear at titanium-based dental implant connections: A scoping review

Two-piece implant systems are mainly used in oral implantology involving an osseointegrated implant connected to an abutment, which supports prosthetic structures. It is well documented that the presence of microgaps, biofilms and oral fluids at the implant-abutment connection can cause mechanical and biological complications. The aim of this review paper was to report the degradation at the implant-abutment connection by wear and corrosion processes taking place in the oral cavity. Most of the retrieved studies evaluated the wear and corrosion (tribocorrosion) of titanium-based materials used for implants and abutments in artificial saliva. Electrochemical and wear tests together with microscopic techniques were applied to validate the tribocorrosion behavior of the surfaces. A few studies inspected the wear on the inner surfaces of the implant connection as a result of fatigue or removal of abutments. The studies reported increased microgaps after fatigue tests. In addition, data suggest that micromovements occurring at the contacting surfaces can increase the wear of the inner surfaces of the connection. Biofilms and/or glycoproteins act as lubricants, although they can also amplify the corrosion of the surfaces. Consequently, loosening of the implant-abutment connection can take place during mastication. In addition, wear and corrosion debris such as ions and micro- and nanoparticles released into the surrounding tissues can stimulate peri-implant inflammation that can lead to pathologic bone resorption.

Production of a biofunctional titanium surface using plasma electrolytic oxidation and glow-discharge plasma for biomedical applications

In this study, the authors tested the hypotheses that plasma electrolytic oxidation (PEO) and glow-discharge plasma (GDP) would improve the electrochemical, physical, chemical, and mechanical properties of commercially pure titanium (cpTi), and that blood protein adsorption on plasma-treated surfaces would increase. Machined and sandblasted surfaces were used as controls. Standard electrochemical tests were conducted in artificial saliva (pHs of 3.0, 6.5, and 9.0) and simulated body fluid. Surfaces were characterized by scanning electron microscopy, energy-dispersive spectroscopy, x-ray photoelectron spectroscopy, atomic force microscopy, x-ray diffraction, profilometry, Vickers microhardness, and surface energy. For biological assay, the adsorption of blood serum proteins (i.e., albumin, fibrinogen, and fibronectin) was tested. Higher values of polarization resistance and lower values of capacitance were noted for the PEO and GDP groups (p < 0.05). Acidic artificial saliva reduced the corrosion resistance of cpTi (p < 0.05). PEO and GDP treatments improved the surface properties by enrichment of the surface chemistry with bioactive elements and increased surface energy. PEO produced a porous oxide layer (5-μm thickness), while GDP created a very thin oxide layer (0.76-μm thickness). For the PEO group, the authors noted rutile and anatase crystalline structures that may be responsible for the corrosion barrier improvement and increased microhardness values. Plasma treatments were able to enhance the surface properties and electrochemical stability of titanium, while increasing protein adsorption levels.