Physicochemical characterization and mechanical performance analysis of biaxially oriented PLA/PCL tubular scaffolds for intended stent application

Physicochemical Properties of UV-Irradiated, Biaxially Oriented PLA Tubular Scaffolds

PLA and its blends are the most extensively used materials for various biomedical applications such as scaffolds, implants, and other medical devices. The most extensively used method for tubular scaffold fabrication is by using the extrusion process. However, PLA scaffolds show limitations such as low mechanical strength as compared to metallic scaffolds and inferior bioactivities, limiting their clinical application. Thus, in order to improve the mechanical properties of tubular scaffolds, they were biaxially expanded, wherein the bioactivity can be improved by surface modifications using UV treatment. However, detailed studies are needed to study the effect of UV irradiation on the surface properties of biaxially expanded scaffolds. In this work, tubular scaffolds were fabricated using a novel single-step biaxial expansion process, and the surface properties of the tubular scaffolds after different durations of UV irradiation were evaluated. The results show that changes in the surface wettability of scaffolds were observed after 2 min of UV exposure, and wettability increased with the increased duration of UV exposure. FTIR and XPS results were in conjunction and showed the formation of oxygen-rich functional groups with the increased UV irradiation of the surface. AFM showed increased surface roughness with the increase in UV duration. However, it was observed that scaffold crystallinity first increased and then decreased with the UV exposure. This study provides a new and detailed insight into the surface modification of the PLA scaffolds using UV exposure.

The effect of alginate scaffolds on bone healing in defects formed with drilling model in rat femur diaphysis

Alginate (ALG) is a biocompatible and biodegradable polymer. Mechanical weakness is one of the main problems for the alginate-based scaffolds. Various plasticizer additives or modifications tested to improve the mechanical properties. In the presented study, ALG plasticized with triacetin (TA), and tributyl citrate (TBC) than tested on bone healing. In the presented study, the alginate modified with triacetin or tributyl citrate. In-vitro, and in-vivo efficiency of the scaffolds tested on bone tissue regeneration. Scaffolds fabricated by solvent casting, and physicochemical characterizations performed. Monocytes (THP-1) cultured with scaffolds, and macrophage-released cytokines was determined. In-vivo efficacy of the scaffolds was tested in the rat drill hole model. Alginate and tributyl citrate-modified scaffolds have no cytotoxic effect on osteoblastic cells (MC-3T3). Tributyl citrate modification increased tumor necrosis factor-alpha (TNF-alpha) level but did not increase interleukin -1 beta (IL-1 beta) level. In vivo studies showed that osteoblastic growth was significant in alginate and triacetin-modified scaffolds. However, the best values for osteoclastic activity and osteoid tissue formation seen in the triacetin modification. The results demonstrated that the modified alginate scaffolds were more successful than non-modified alginate scaffolds and can used as long-term bone repairing treatments.