Chemical deposition and exfoliation from liquid crystal template: Nickel/nickel (II) hydroxide nanoflakes electrocatalyst for a non-enzymatic glucose oxidation reaction

Recent Progress in MOF-Based Electrochemical Sensors for Non-Enzymatic Glucose Detection

In recent years, substantial advancements have been made in the development of enzyme-free glucose sensors utilizing pristine metal-organic frameworks (MOFs) and their combinations. This paper provides a comprehensive exploration of various MOF-based glucose sensors, encompassing monometallic MOF sensors as well as multi-metal MOF combinations. These approaches demonstrate improved glucose detection capabilities, facilitated by the augmented surface area and availability of active sites within the MOF structures. Furthermore, the paper delves into the application of MOF complexes and derivatives in enzyme-free glucose sensing. Derivatives incorporating carbon or metal components, such as carbon cloth synthesis, rGO-MOF composites, and core-shell structures incorporating noble metals, exhibit enhanced electrochemical performance. Additionally, the integration of MOFs with foams or biomolecules, such as porphyrins, enhances the electrocatalytic properties for glucose detection. Finally, this paper concludes with an outlook on the future development prospects of enzyme-free glucose MOF sensors.

Hydrazine High-Performance Oxidation and Sensing Using a Copper Oxide Nanosheet Electrocatalyst Prepared via a Foam-Surfactant Dual Template

This work demonstrates hydrazine electro-oxidation and sensing using an ultrathin copper oxide nanosheet (CuO-NS) architecture prepared via a versatile foam-surfactant dual template (FSDT) approach. CuO-NS was synthesised by chemical deposition of the hexagonal surfactant Brij^®58 liquid crystal template containing dissolved copper ions using hydrogen foam that was concurrently generated by a sodium borohydride reducing agent. The physical characterisations of the CuO-NS showed the formation of a two-dimensional (2D) ultrathin nanosheet architecture of crystalline CuO with a specific surface area of ~39 m²/g. The electrochemical CuO-NS oxidation and sensing performance for hydrazine oxidation revealed that the CuO nanosheets had a superior oxidation performance compared with bare-CuO, and the reported state-of-the-art catalysts had a high hydrazine sensitivity of 1.47 mA/cm² mM, a low detection limit of 15 μM (S/N = 3), and a linear concentration range of up to 45 mM. Moreover, CuO-NS shows considerable potential for the practical use of hydrazine detection in tap and bottled water samples with a good recovery achieved. Furthermore, the foam-surfactant dual template (FSDT) one-pot synthesis approach could be used to produce a wide range of nanomaterials with various compositions and nanoarchitectures at ambient conditions for boosting the electrochemical catalytic reactions.

Foam Synthesis of Nickel/Nickel (II) Hydroxide Nanoflakes Using Double Templates of Surfactant Liquid Crystal and Hydrogen Bubbles: A High-Performance Catalyst for Methanol Electrooxidation in Alkaline Solution

This work demonstrates the chemical synthesis of two-dimensional nanoflakes of mesoporous nickel/nickel (II) hydroxide (Ni/Ni(OH)₂-NFs) using double templates of surfactant self-assembled thin-film and foam of hydrogen bubbles produced by sodium borohydride reducing agent. Physicochemical characterizations show the formation of amorphous mesoporous 2D nanoflakes with a Ni/Ni(OH)₂ structure and a high specific surface area (165 m²/g). Electrochemical studies show that the electrocatalytic activity of Ni/Ni(OH)₂ nanoflakes towards methanol oxidation in alkaline solution is significantly enhanced in comparison with that of parent bare-Ni(OH)₂ deposited from surfactant-free solution. Cyclic voltammetry shows that the methanol oxidation mass activity of Ni/Ni(OH)₂-NFs reaches 545 A/cm² g_cat at 0.6 V vs. Ag/AgCl, which is more than five times higher than that of bare-Ni(OH)₂. Moreover, Ni/Ni(OH)₂-NFs reveal less charge transfer resistance (10.4 Ω), stable oxidation current density (625 A/cm² g_cat at 0.7 V vs. Ag/AgCl), and resistance to the adsorption of reaction intermediates and products during three hours of constant-potential methanol oxidation electrolysis in alkaline solution. The high-performance electrocatalytic activity of Ni/Ni(OH)₂ nanoflakes is mainly derived from efficient charge transfer due to the high specific surface area of the 2D mesoporous architecture of the nanoflakes, as well as the mass transport of methanol to Ni²⁺/Ni³⁺ active sites throughout the catalyst layer.

Electrospinning One-dimensional Surface-phosphorized CuCo/C nanofibers for Enzyme-free Glucose Sensing

Developing novel electrocatalysts is of great importance for the practical application of non-enzymatic glucose sensors. One-dimensional (1D) carbon fiber-supported copper-cobalt bimetallic electrocatalysts (CuCo-P350) are successfully prepared via electrospinning technology and...