Tobacco Exposure Is Associated With Extremely Low Polyethylene Oxidation in Total Knee Arthroplasty Components

Failure Analysis of Ultra-High Molecular Weight Polyethylene Tibial Insert in Total Knee Arthroplasty

Knee osteoarthritis is treated based on total knee arthroplasty (TKA) interventions. The most frequent failure cause identified in surgical practice is due to wear and oxidation processes of the prothesis' tibial insert. This component is usually manufactured from ultra-high molecular weight polyethylene (UHMWPE). To estimate the clinical complications related to a specific prosthesis design, we investigated four UHMWPE tibial inserts retrieved from patients from Clinical Hospital Colentina, Bucharest, Romania. For the initial analysis of the polyethylene degradation modes, macrophotography was chosen. A light stereomicroscope was used to estimate the structural performance and the implant surface degradation. Scanning electron microscopy confirmed the optical results and fulfilled the computation of the Hood index. The oxidation process in UHMWPE was analyzed based on Fourier-transform infrared spectroscopy (FTIR). The crystallinity degree and the oxidation index were computed in good agreement with the existing standards. Mechanical characterization was conducted based on the small punch test. The elastic modulus, initial peak load, ultimate load, and ultimate displacement were estimated. Based on the aforementioned experimental tests, a variation between 9 and 32 was found in the case of the Hood score. The oxidation index has a value of 1.33 for the reference sample and a maximum of 9.78 for a retrieved sample.

Posterior intraprosthetic dislocation of cervical arthroplasty: illustrative case

BACKGROUND

Cervical disc herniation is a common condition usually treated with anterior cervical discectomy and fusion (ACDF) or, more recently, with cervical disc arthroplasty (CDA). Both treatments offer similar clinical results. However, CDA has been found to offer fewer medium- to long-term complications as well as potential reduction of long-term adjacent disc degeneration.

OBSERVATIONS

A 40-year-old man was treated with cervical discectomy and arthroplasty due to a C6-C7 disc herniation with left C7 radiculopathy. After the treatment, his postoperative follow-up appointments were uneventful for 9 months. However, after 9 months, he reported cervical pain and a right C7 radiculopathy after neck extension. Imaging confirmed a posterior intraprosthetic dislocation, the first case reported to date. The patient was received emergency surgery under neuromonitoring, and the prosthesis was replaced by an ACDF and anterior plate. The insert presented a rupture of the anterior horn. The patient presented no preoperative or postoperative neurological deficit, and his follow-up review revealed no issues.

LESSONS

Posterior intraprosthetic dislocation is an extremely rare complication. It may occur with Mobi-C cervical arthroplasty in the case of rupture and oxidation of the polyethylene insert. Spine surgeons should be aware of this potential major complication.