Designing the heterostructured FeWO4/FeS2 nanocomposites for an enhanced photocatalytic organic dye degradation

Enhanced photocatalytic degradation of organic pollutants by green-synthesized gold nanoparticles using polysaccharide for environmental remediation

The recent rise in textile dye wastewater discharge into the environment has detrimental effects on living organisms and human health. The present study reports a facile approach to green-synthesized AuNPs employing sesbania gum for catalytic and photocatalytic degradation of organic pollutants. The obtained AuNPs were characterized by various techniques such as UV-vis, FT-IR, SEM, TEM, AFM, zeta potential, LC-MS, and XPS. The XRD patterns revealed a highly crystalline and face-centered cubic structure. XPS and EDX analysis defined the chemical composition and product purity of SBG-AuNPs. Photocatalytic degradation of hazardous dyes congo red and safranin-O using SBG-AuNPs showed a rapid decomposition rate with 94.69 % under visible light irradiation. The effect of pH, dye concentration, and catalyst dose on photodegradation and recyclability was also studied. The kinetic plots were used to calculate the rate constant, showing a pseudo-first-order reaction. Scavenger trap experiments confirmed the role of h+ and superoxide(.O2-) as active species, and LCMS analysis was used to identify the degradation intermediates. The catalytic reduction of SBG-AuNPs was studied for brilliant green (BG) and methylene blue (MB) in the presence of NaBH4, resulting the degradation efficiency of 90.37 % and 84.52 %, respectively. This study presents an innovative approach for designing highly efficient photocatalysts for environmental remediation and wastewater treatment from textile dyes.

Hydrothermal synthesis and photocatalytic application of ZnS-Ag composites based on biomass-derived carbon aerogel for the visible light degradation of methylene blue

A facile and cost-effective hydrothermal followed by precipitation method is employed to synthesize visible light-driven ZnS-Ag ternary composites supported on carbon aerogel (CA). Extensive studies were conducted on the structural, morphological, and optical properties, confirming the successful formation of ternary nanocomposites. The obtained results evidently demonstrate the successful loading of ZnS and Ag onto the surface of the CA. High-resolution transmission electron microscopy analysis revealed that ZnS and Ag nanoparticles (AgNPs) were uniformly distributed on the surface of the CA with an average diameter of 18 nm. The biomass-derived CA, containing a hierarchical porous nano-architecture and an abundant number of -NH2 functional groups on the surface, can greatly prevent the agglomeration, stability and reduce particle size. Brunauer-Emmett-Teller analysis results indicated specific surface areas of 4.62 m2 g-1 for the CA, 48.50 m2 g-1 for the CA/ZnS composite, and 62.62 m2 g-1 for the CA/ZnS-Ag composite. These values demonstrate an increase in surface area upon the incorporation of ZnS and Ag into the CA matrix. Under visible light irradiation, the synthesized CA/ZnS-Ag composites displayed remarkably improved photodegradation efficiency of methylene blue (MB). Among the tested samples, the CA/ZnS-Ag composites exhibited the highest percentage of photodegradation efficiency, surpassing ZnS, CA, and CA/ZnS. The obtained percentages of degradation efficiency for CA, ZnS, CA/ZnS, and CA/ZnS-Ag composites were determined as 26.60%, 52.12%, 68.39%, and 98.64%, respectively. These results highlight the superior photocatalytic performance of the CA/ZnS-Ag composites in the degradation of MB under visible light conditions. The superior efficiency of the CA/ZnS-Ag composite can be attributed to multiple factors, including its elevated specific surface area, inhibition of electron-hole pair recombination, and enhanced photon absorption within the visible light spectrum. The CA/ZnS-Ag composites displayed consistent efficiency over multiple cycles, confirming their stable performance, reusability, and enduring durability, thereby showcasing the robust nature of this composite material.

The Design of PAN-Based Janus Membrane with Adjustable Asymmetric Wettability in Wastewater Purification

In this paper, an environmentally friendly polyacrylonitrile-based (PAN-based) composite membrane with a Janus structure for wastewater treatment was successfully fabricated. To achieve the optimum adsorption of PAN-based Janus composite membrane, the asymmetric wettability was regulated through electrospinning, resulting in TiO2 modifying PAN as the hydrophilic substrate layer, and PCL gaining a different thickness as the hydrophobic layer. The prepared Janus composite membrane (PAN/TiO2-PCL20) showed excellent oil/water separation performance for diverse surfactant-stabilized oil-in-water emulsions. For n-hexane-in-water emulsion, the permeate flux and separation efficiency reached 1344 L m-2 h-1 and 99.52%, respectively. Even after 20 cycles of separation, it still had outstanding reusability and the separation efficiency remained above 99.15%. Meanwhile, the PAN/TiO2-PCL20 also exhibited an excellent photocatalytic activity, and the removal rate for RhB reached 93.2%. In addition, the research revealed that PAN/TiO2-PCL20 possessed good mechanical property and unidirectional water transfer capability. All results indicated that PAN/TiO2-PCL20 with photocatalysis and oil/water separation performance could be used for practical complex wastewater purification.

ZnO-based heterojunction catalysts for the photocatalytic degradation of methyl orange dye

In this study, a variety of ZnO-based heterojunctions with disparate wt.% doping of WO3 and BiOI have been prepared for the photodestruction of methyl orange (MO) dye in aqueous solution. The composites were analysed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, optical studies, and nitrogen adsorption-desorption isotherms. The SEM images revealed non-uniform surfaces of the ZnO-BiOI based composites while mostly nodular morphology was observed for all three samples of ZnO-WO3. As the WO3 loading increased, more clustering was detected. The analysed samples exhibited characteristic peaks representative of the triclinic phase of WO3 and the hexagonal wurtzite structure of ZnO, while the diffractogram observed from the materials displayed distinct peaks corresponding to the crystalline phases of both BiOI and ZnO in their pure forms. Further evidence of the samples' characteristics includes the presence of distinct crystalline patterns without any impurity peaks, a red shift in the absorption spectra of the heterostructure, the detection of only the reference elements, and mostly Type IV isotherm adsorption. This study identified the ZnO-[10%]BiOI and ZnO-[10%]WO3 heterojunctions as the best performing photocatalysts, as MO was completely destroyed in 120 and 90 min, respectively. Thus, confirming 10% wt. as the optimal doping concentration for the best photo-activity in this study. The impact of varying process parameters demonstrates that at an elevated photocatalyst mass of 40 mg, both heterojunctions effectively degraded MO. The photodegradation efficiency of MO was more pronounced in strong acidic conditions (pH 2) when compared to high alkaline conditions (pH 11) for the ZnO-[10%]BiOI heterostructure. However, a decrease in performance was observed for both strong acidic and high alkaline pH values when the ZnO-[10%]WO3 heterostructure was applied. The kinetic analysis of the photodegradation study reveals that all the photodegradation experiments can be represented by the pseudo-first-order kinetic model. The findings from this investigation propose that the ZnO-[10%]BiOI heterojunction photocatalyst holds significant potential for the effective treatment of dye-contaminated wastewater.