Enhancing biodegradation of PBAT through bio-stimulation using Pseudozyma jejuensis for effective plastic waste reduction

Biodegradation of poly(butylene adipate terephthalate) and poly(vinyl alcohol) within aquatic pathway

Understanding the environmental fate of biodegradable plastics in aquatic systems is crucial, given the alarming amount of plastic waste and microplastic particles transported through aquatic pathways. In particular, there is a need to analyze the biodegradation of commercialized biodegradable plastics upon release from wastewater treatment plants into natural aquatic systems. This study investigates the biodegradation behaviors of poly(butylene adipate terephthalate) (PBAT) and poly(vinyl alcohol) (PVA) in wastewater, freshwater, and seawater. Biodegradation of PBAT and PVA assessed through biochemical oxygen demand (BOD) experiments and microcosm tests revealed that the type of aquatic system governs the biodegradation behaviors of each plastic, with the highest biodegradation rate achieved in wastewater for both PBAT and PVA (25.6 and 32.2 % in 30 d, respectively). Plastic release pathway from wastewater into other aquatic systems simulated by sequential incubation in different microcosms suggested that PBAT exposed to wastewater and freshwater before reaching seawater was more prone to degradation than when directly exposed to seawater. On the other hand, PVA displayed comparable biodegradation rate regardless of whether it was directly exposed to seawater or had passed through other environments beforehand. Metagenome amplicon sequencing of 16S rRNA genes revealed distinct community shifts dependent on the type of plastics in changing environments along the simulated aquatic pathway. Several bacterial species putatively implicated in the biodegradation of PBAT and PVA are discussed. Our findings underscore the significant influence of pollution routes on the biodegradation of PBAT and PVA, highlighting the potential for wastewater treatment to facilitate rapid degradation compared to direct exposure to pristine aquatic environments.

Comparison of anaerobic digestion of starch- and petro-based bioplastic under hydrogen-rich conditions

To identify an economically viable waste management system for bioplastics, thermoplastic starch (TPS) and poly(butylene adipate-co-terephthalate) (PBAT) were anaerobically digested under hydrogen (H2)/carbon dioxide (CO2) and nitrogen (N2) gas-purged conditions to compare methane (CH4) production and biodegradation. Regardless of the type of bioplastics, CH4 production was consistently higher with H2/CO2 than with N2. The highest amount of CH4 was produced at 307.74 mL CH4/g volatile solids when TPS digested with H2/CO2. A stepwise increased in CH4 yield was observed, with a nominal initial increment followed by accelerated methanogenesis conversion as H2 was depleted. This may be attributed to a substantial shift in the microbial structure from hydrogenotrophic methanogen (Methanobacteriales and Methanomicrobiales) to heterotrophs (Spirochaetia). In contrast, no significant change was observed with PBAT, regardless of the type of purged gas. TPS was broken down into numerous derivatives, including volatile fatty acids. TPS produced more byproducts with H2/CO2 (i.e., 430) than with N2 (i.e., 320). In contrast, differential scanning calorimetry analysis on PBAT revealed an increase in crystallinity from 10.20 % to 12.31 % and 11.36 % in the H2/CO2- and N2-purged conditions, respectively, after 65 days of testing. PBAT surface modifications were characterized via Fourier transform infrared spectroscopy and scanning electron microscopy. The results suggest that the addition of H2/CO2 can enhance the CH4 yield and increase the breakdown rate of TPS more than that of PBAT. This study provides novel insights into the CH4 production potential of two bioplastics with different biodegradabilities in H2/CO2-mediated anaerobic digestion systems.

Enhanced Biodegradation Rate of Poly(butylene adipate-co-terephthalate) Composites Using Reed Fiber

To enhance the degradability of poly(butylene adipate-co-terephthalate) (PBAT), reed fiber (RF) was blended with PBAT to create composite materials. In this study, a fifteen day degradation experiment was conducted using four different enzyme solutions containing lipase, cellulase, Proteinase K, and esterase, respectively. The degradation process of the sample films was analyzed using an analytical balance, Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). The PBAT/RF composites exhibited an increased surface hydrophilicity, which enhanced their degradation capacity. Among all the enzymes tested, lipase had the most significant impact on the degradation rate. The weight loss of PBAT and PBAT/RF, caused by lipase, was approximately 5.63% and 8.17%, respectively. DSC analysis revealed an increase in the melting temperature and crystallinity over time, especially in the film containing reed fibers. FTIR results indicated a significant weakening of the ester bond peak in the samples. Moreover, this article describes a biodegradation study conducted for three months under controlled composting conditions of PBAT and PBAT/RF samples. The results showed that PBAT/RF degraded more easily in compost as compared to PBAT. The lag phase of PBAT/RF was observed to decrease by 23.8%, while the biodegradation rate exhibited an increase of 11.8% over a period of 91 days. SEM analysis demonstrated the formation of more cracks and pores on the surface of PBAT/RF composites during the degradation process. This leads to an increased contact area between the composites and microorganisms, thereby accelerating the degradation of PBAT/RF. This research is significant for preparing highly degradable PBAT composites and improving the application prospects of biodegradable green materials. PBAT/RF composites are devoted to replacing petroleum-based polymer materials with sustainable, natural materials in advanced applications such as constructional design, biomedical application, and eco-environmental packaging.