Nonthermal plasma sulfurized CuInS2/S-doped MgO nanosheets for efficient solar-light photocatalytic degradation of tetracycline

Sulfur-doped activated carbon for the efficient degradation of tetracycline with persulfate: Insight into the effect of pore structure on catalytic performance

Sulfur-doped activated carbon has proved to be a promising metal-free catalyst for persulfate (PDS) catalytic activation for the oxidation of aqueous refractory organics. Herein, sulfur-doped porous carbon (ACS) catalysts with different pore structures and doped-S contents were prepared via a template method using d(+)-glucose as the carbon source, sulfur as the sulfur source, and nano-MgO with different particle sizes as templates. Characterization results showed that the particle size of MgO significantly affects the pore structure and doped-S content of ACSs catalysts: a sample synthesized with 20 nm MgO as template (ACS-20) presented the highest content of doped-S and a mesoporous structure, which endowed it with superior adsorption and catalytic performance toward tetracycline (TC) removal. The effect of catalyst dosage, TC concentration, PDS concentration and solution pH on TC removal efficiency were evaluated. The reaction mechanism, investigated by combination of EPR, quenching experiments and LC-MS, indicated that the reactive species included HO·, SO4˙-, and 1O2, but that 1O2 played the dominant role in TC oxidation through a non-radical oxidation pathway. In addition, the reusability and regeneration properties of the ACS-20 catalyst were also studied. This work provides a promising strategy and some theoretical basis for the design and preparation of activated carbon catalysts for advanced oxidation reactions from the viewpoint of pore structure design and S-doping.

Highly Efficient Cd2+ Removal Using Tobermorite with pH Self-Adjustment Ability from Aqueous Solution

Cadmium (Cd), as a type of heavy metal, can increase the incidence of many diseases, even in low concentrations. In this study, tobermorite was hydrothermally synthesized and then applied to adsorb Cd²⁺ from an aqueous solution. The physicochemical characteristics of the synthesized tobermorite were detected, and the results indicated that the well-crystallized tobermorite had a lot of mesopores and a large specific surface area of 140.92 m²/g. It acquired a pH self-adjustment ability via spontaneously releasing Ca²⁺ and OH^- into the aqueous solution. The effects of different factors on Cd²⁺ removal were investigated. For Cd²⁺, the removal efficiency could reach 99.71% and the maximum adsorption capacity was 39.18 mg/g using tobermorite. The adsorption data was best fitted with the pseudo-second-order kinetic and Langmuir isotherm models. In addition, there was no strict limit on the solution pH in Cd²⁺ adsorption because the tobermorite could adjust the solution pH to an alkaline atmosphere spontaneously. The efficient removal of Cd²⁺ using tobermorite was a result of surface complexation and ion exchange.

Efficient Adsorption-Photocatalytic Removal of Tetracycline Hydrochloride over Octahedral MnS

To disclose the effect of crystal plane on the adsorption-photocatalytic activity of MnS, octahedral MnS was prepared via the hydrothermal route to enhance the adsorption and photocatalytic efficiencies of tetracycline hydrochloride (TCH) in visible light region. The optimal MnS treated at 433 K for 16 h could remove 94.83% TCH solution of 260 mg L⁻¹ within 180 min, and its adsorption-photocatalytic efficiency declined to 89.68% after five cycles. Its excellent adsorption-photocatalytic activity and durability were ascribed to the sufficient vacant sites of octahedral structure for TCH adsorption and the feasible band-gap structure for visible-light response. In addition, the band gap structure (1.37 eV) of MnS with a conduction band value of −0.58 eV and a valence band value of 0.79 eV was favorable for the generation of O²⁻, while unsuitable for the formation of OH. Hence, octahedral MnS was a potential material for the removal of antibiotics from wastewater.