Improved hydrophilicity and durability of polarized PVDF coatings on anodized titanium surfaces to enhance mineralization ability

Optimizing implant osseointegration, soft tissue responses, and bacterial inhibition: A comprehensive narrative review on the multifaceted approach of the UV photofunctionalization of titanium

Titanium implants have revolutionized restorative and reconstructive therapy, yet achieving optimal osseointegration and ensuring long-term implant success remain persistent challenges. In this review, we explore a cutting-edge approach to enhancing implant properties: ultraviolet (UV) photofunctionalization. By harnessing UV energy, photofunctionalization rejuvenates aging implants, leveraging and often surpassing the intrinsic potential of titanium materials. The primary aim of this narrative review is to offer an updated perspective on the advancements made in the field, providing a comprehensive overview of recent findings and exploring the relationship between UV-induced physicochemical alterations and cellular responses. There is now compelling evidence of significant transformations in titanium surface chemistry induced by photofunctionalization, transitioning from hydrocarbon-rich to carbon pellicle-free surfaces, generating superhydrophilic surfaces, and modulating the electrostatic properties. These changes are closely associated with improved cellular attachment, spreading, proliferation, differentiation, and, ultimately, osseointegration. Additionally, we discuss clinical studies demonstrating the efficacy of UV photofunctionalization in accelerating and enhancing the osseointegration of dental implants. Furthermore, we delve into recent advancements, including the development of one-minute vacuum UV (VUV) photofunctionalization, which addresses the limitations of conventional UV methods as well as the newly discovered functions of photofunctionalization in modulating soft tissue and bacterial interfaces. By elucidating the intricate relationship between surface science and biology, this body of research lays the groundwork for innovative strategies aimed at enhancing the clinical performance of titanium implants, marking a new era in implantology.

Scaffold-Based Poly(Vinylidene Fluoride) and Its Copolymers: Materials, Fabrication Methods, Applications, and Perspectives

Tissue engineering involves implanting grafts into damaged tissue sites to guide and stimulate the formation of new tissue, which is an important strategy in the field of tissue defect treatment. Scaffolds prepared in vitro meet this requirement and are able to provide a biochemical microenvironment for cell growth, adhesion, and tissue formation. Scaffolds made of piezoelectric materials can apply electrical stimulation to the tissue without an external power source, speeding up the tissue repair process. Among piezoelectric polymers, poly(vinylidene fluoride) (PVDF) and its copolymers have the largest piezoelectric coefficients and are widely used in biomedical fields, including implanted sensors, drug delivery, and tissue repair. This paper provides a comprehensive overview of PVDF and its copolymers and fillers for manufacturing scaffolds as well as the roles in improving piezoelectric output, bioactivity, and mechanical properties. Then, common fabrication methods are outlined such as 3D printing, electrospinning, solvent casting, and phase separation. In addition, the applications and mechanisms of scaffold-based PVDF in tissue engineering are introduced, such as bone, nerve, muscle, skin, and blood vessel. Finally, challenges, perspectives, and strategies of scaffold-based PVDF and its copolymers in the future are discussed.

Investigation of nanotopography on SOCE mediated cell migration via live-cell : Imaging on opaque implant surface

The exploration of cell response to nanotopography has attracted considerable attentions for years. This article focuses on the influence of nanotopography on the intracellular Ca2+ dynamics, the most ubiquitous but ignored second messenger. The classic titanium nanotubes (NT) were fabricated by anodization to formulate nanoporous surfaces. Firstly, the store operative calcium entry (SOCE) in endoplasmic reticulum (ER) and functional Ca2+ release-activated Ca2+ (CRAC) channels were significantly enhanced on NT surfaces that revealed by live-cell Ca2+ imaging and fluorescence resonance energy transfer (FRET) identification of orai1-stim1 connection. To investigate the potential implication of Ca2+ elevation, the dynamic cell migration trajectory was monitored by a self-made holder, which could not only be suitable for the opaque implant surface but also guarantee the focus fields identical during samples shifting. The cell migration on NT surface was more vigorous and rapid, which was correlated with higher focal adhesion proteins expression, Ca2+-dependent calpain activity and stim1 level. In conclusion, this study has confirmed the novel ER Ca2+ hemostasis pathway on nanosurfaces and its crucial role in cell migration regulation, which may help for more biofavorable implant surface design.

Functionally Tailored Metal-Organic Framework Coatings for Mediating Ti Implant Osseointegration

Owing to their mechanical resilience and non-toxicity, titanium implants are widely applied as the major treatment modality for the clinical intervention against bone fractures. However, the intrinsic bioinertness of Ti and its alloys often impedes the effective osseointegration of the implants, leading to severe adverse complications including implant loosening, detachment, and secondary bone damage. Consequently, new Ti implant engineering strategies are urgently needed to improve their osseointegration after implantation. Remarkably, metalorganic frameworks (MOFs) are a class of novel synthetic material consisting of coordinated metal species and organic ligands, which have demonstrated a plethora of favorable properties for modulating the interfacial properties of Ti implants. This review comprehensively summarizes the recent progress in the development of MOF-coated Ti implants and highlights their potential utility for modulating the bio-implant interface to improve implant osseointegration, of which the discussions are outlined according to their physical traits, chemical composition, and drug delivery capacity. A perspective is also provided in this review regarding the current limitations and future opportunities of MOF-coated Ti implants for orthopedic applications. The insights in this review may facilitate the rational design of more advanced Ti implants with enhanced therapeutic performance and safety.

Application of piezoelectric materials in the field of bone: a bibliometric analysis

In the past 4 decades, many articles have reported on the effects of the piezoelectric effect on bone formation and the research progress of piezoelectric biomaterials in orthopedics. The purpose of this study is to comprehensively evaluate all existing research and latest developments in the field of bone piezoelectricity, and to explore potential research directions in this area. To assess the overall trend in this field over the past 40 years, this study comprehensively collected literature reviews in this field using a literature retrieval program, applied bibliometric methods and visual analysis using CiteSpace and R language, and identified and investigated publications based on publication year (1984-2022), type of literature, language, country, institution, author, journal, keywords, and citation counts. The results show that the most productive countries in this field are China, the United States, and Italy. The journal with the most publications in the field of bone piezoelectricity is the International Journal of Oral & Maxillofacial Implants, followed by Implant Dentistry. The most productive authors are Lanceros-Méndez S, followed by Sohn D.S. Further research on the results obtained leads to the conclusion that the research direction of this field mainly includes piezoelectric surgery, piezoelectric bone tissue engineering scaffold, manufacturing artificial cochleae for hearing loss patients, among which the piezoelectric bone tissue engineering scaffold is the main research direction in this field. The piezoelectric materials involved in this direction mainly include polyhydroxybutyrate valerate, PVDF, and BaTiO3.

Surface modification of polyether ether ketone implant with a novel nanocomposite coating containing poly (vinylidene fluoride) toward improving piezoelectric and bioactivity performance

Polyether ether ketone (PEEK) is an appropriate biomaterial for orthopedic implant applications due to its superior mechanical properties, chemical resistance, nontoxicity, and Magnetic resonance imaging (MRI) compatibility. Unfortunately, the inherent bio-inertness of PEEK restricted its application and required some modification to provide better bioactivity. Besides it, the generated electrical signals in the bone due to its piezoelectricity features have a vital role in regulating bone repair and regeneration. We aimed to modify the surface of PEEK with a dual-functionality nanocomposite that provides surface bioactivity and simulates the piezoelectricity of bone. So, we introduced a novel piezoelectric-bioactive nanocomposite of dispersed poly (vinylidene fluoride) (PVDF) in a sulfonated PEEK (SPEEK) matrix containing Nanohydroxyapatite (nHA) and Carbon nanofiber (CNF) fillers for coating on PEEK substrate to improve its biological activity and simulate the electrical microenvironment for bone tissue. Furthermore, sulfonation of the PEEK surface was conducted as an intermediate layer to prepare better adhesion between the coating nanocomposite and the PEEK sublayer. Surface and cross-section morphology, apatite formation, and cell attachment were investigated on the different treated PEEK surfaces using field-emission scanning electron microscopy (FESEM) and energy dispersive X-ray analysis (EDX). Also, piezoelectric performance, electrical conductivity, contact angle, and mechanical properties were examined on the prepared samples. Moreover, cell viability and cell morphology were investigated for biological evaluation with human osteoblast-like MG-63 cells. Collectively, the hydrophilicity of modified PEEK (mPEEK) coated with nanocomposite was improved due to the synergistic effects of SPEEK functional groups and nHA. Also, comprehensive investigation on the mPEEK treated with nanocomposite indicated a noticeably better bone-like apatite formation, cell proliferation, and cell attachments in the presence of nHA. The transfer of induced piezoelectric charges from dispersed PVDF in the matrix to the surface of nanocomposite containing 2 wt% of CNF increased output voltage to 1893 mV. On the other hand, the presence of CNF in nanocomposites enhanced tensile strength and Young's modulus by 92% and 117%, respectively.

Electrical stimulation of piezoelectric BaTiO3 coated Ti6Al4V scaffolds promotes anti-inflammatory polarization of macrophages and bone repair via MAPK/JNK inhibition and OXPHOS activation

Bone regeneration is a highly synchronized process that requires multiple biochemical, bioelectrical, mechanical, and other physiological cues. The restoration and delivery of electrical cues locally through piezoelectric materials have been demonstrated to facilitate osteogenesis in vitro and bone repair in vivo. However, the underlying mechanism by which piezoelectric stimulation promotes osteogenesis and bone repair remains unclear yet, limiting the design and clinical application of piezoelectric materials for bone repair. Herein, a piezoelectric BaTiO3/Ti6Al4V (BT/Ti) scaffold was prepared by hydrothermal synthesis of a uniform BaTiO3 layer on three dimensionally printed Ti6Al4V scaffold. The BT/Ti scaffolds exhibited piezoelectricity and favorable biocompatibility with RAW264.7 macrophages after polarization. In vitro results demonstrated that the piezoelectric effects of the poled BT/Ti scaffolds promoted M2 polarization of macrophages and immunoregulatory osteogenesis of MC-3T3 osteoblasts. In a subcutaneous implantation model, a higher proportion of CD68⁺ CD206⁺ M2 macrophages was observed in the tissues around the poled BT/Ti scaffolds under low intensity pulsed ultrasound (LIPUS) stimulation. Improvements in macrophage M2 polarization and bone regeneration were further identified in a sheep cervical corpectomy model. RNA sequencing and mechanistic investigation revealed that the piezoelectric BT/Ti (poled) scaffolds inhibited the inflammatory MAPK/JNK signaling cascade and activated oxidative phosphorylation (OXPHOS) and ATP synthesis in macrophages. Collectively, our study provides a promising method for regulating the immune microenvironment and enhancing bone regeneration using polarized piezoelectric BT/Ti scaffolds.

The Osteogenic Role of Barium Titanate/Polylactic Acid Piezoelectric Composite Membranes as Guiding Membranes for Bone Tissue Regeneration

Purpose

Biopiezoelectric materials have good biocompatibility and excellent piezoelectric properties, and they can generate local currents in vivo to restore the physiological electrical microenvironment of the defect and promote bone regeneration. Previous studies of guided bone regeneration membranes have rarely addressed the point of restoring it, so this study prepared a Barium titanate/Polylactic acid (BT/PLA) piezoelectric composite membrane and investigated its bone-formation, with a view to providing an experimental basis for clinical studies of guided bone tissue regeneration membranes.

Methods

BT/PLA composite membranes with different BT ratio were prepared by solution casting method, and piezoelectric properties were performed after corona polarization treatment. The optimal BT ratio was selected and then subjected to in vitro cytological experiments and in vivo osteogenic studies in rats. The effects on adhesion, proliferation and osteogenic differentiation of the pre-osteoblastic cell line (MC3T3-E1) were investigated. The effect of composite membranes on bone repair of cranial defects in rats was investigated after 4 and 12 weeks.

Results

The highest piezoelectric coefficient d33 were obtained when the BT content was 20%, reaching (7.03 ± 0.26) pC/N. The value could still be maintained at (4.47±0.17) pC/N after 12 weeks, meeting the piezoelectric constant range of bone. In vitro, the MC3T3-E1 cells showed better adhesion and proliferative activity in the group of polarized 20%BT. The highest alkaline phosphatase (ALP) content was observed in cells of this group. In vivo, it promoted rapid bone regeneration. At 4 weeks postoperatively, new bone formation was evident at the edges of the defect, with extensive marrow cavity formation; after 12 weeks, the defect was essentially completely closed, with density approximating normal bone tissue and significant mineralization.

Conclusion

The BT/PLA piezoelectric composite membrane has good osteogenic properties and provides a new idea for guiding the research of membrane materials for bone tissue regeneration.

Influence of surface electric charge of Ti implants on osteoblastic interaction: A systematic review

Objective

A critical analysis of the existing literature to answer “What is the influence of electrical charge of titanium alloys in the electrical interaction with osteoblastic cells for osseointegration?”.

Design

This systematic review followed PRISMA. The personalized search strategy was applied in PubMed, Science Direct, Embase, and Scopus databases, furthermore, in the grey literature in the Google Scholar and ProQuest. The selection process was carried out in two stages independently by two reviewers according to the eligibility criteria. The risk of bias was also analyzed.

Results

When applying the search strategy, 306 articles were found, after removing duplicates 277 were analyzed by title and abstract, of which 33 were selected for full reading, of which 10 met the eligibility criteria. And one was included from the additional literature search. Of these, all had a low risk of bias.

Conclusions

1. The phenomenon of osseointegration is complex and, independent of the superficial electrical charge of the implant, it may occur. To understand osseointegration, attention must be paid to the synergistic action of the electrical potential; chemical composition, intrinsic to the alloy and from surface treatment; and topography, which will determine the speed of adhesion, proliferation, and osteoblast differentiation. 2. The presence of Ca2+ deposited on the surface acts as a driving force for biomineralization that induces osteoblastic attraction and differentiation; 3. For a better understanding of the current literature, more studies are needed to describe the osteogenic regulation process through protein mediation; 4. Topography and chemical composition act as decisive parameters for cell viability independent of the attractive electrical charge.

Comparison of surface properties, cell behaviors, bone regeneration and osseointegration between nano tantalum/PEEK composite and nano silicon nitride/PEEK composite

Both tantalum (Ta) and silicon nitride (SN) exhibit osteogenic bioactivity and antibacterial property. In addition, as a biomaterial for bone repair, polyetheretherketone (PEEK) has outstanding biocompatibility and mechanical performances while it is biologically inert. In this study, by blending PEEK with Ta and SN nanoparticles, respectively, Ta/PEEK composite (TPC) and SN/PEEK composite (SPC) were fabricated for load-bearing bone repair. The surface roughness, hydrophilicity and surface energy of TPC containing Ta nanoparticles were higher than SPC containing SN nanoparticles and PEEK. In addition, TPC with Ta nanoparticles exhibited low antibacterial property while SPC with SN nanoparticles showed high bacterial property. Moreover, the MC3T3-E1 cells responses (e.g. proliferation and differentiation) to TPC was the highest while PEEK was the lowest in vitro. Furthermore, new bone formation and osseointegration for TPC was the highest while PEEK was the lowest in vivo. In conclusion, compared with PEEK, addition of Ta and SN nanoparticles into PEEK fabricated bioactive composites of TPC and SPC with optimized surface property, which played crucial roles in inducing cellular response/bone regeneration. Although the osteogenic activity of SPC was lower than TPC, SPC exhibited osteogenic activity and good antibacterial property, which could prevent infection from bacterial. Therefore, SPC would have better potential for bone substitute.