Biocompatibility and corrosion evaluation of niobium oxide coated AZ31B alloy for biodegradable implants

A Novel PLLA/MgF2 Coating on Mg Alloy by Ultrasonic Atomization Spraying for Controlling Degradation and Improving Biocompatibility

Problems of rapid degradation and poor biocompatibility (endothelialization and hemocompatibility) limit magnesium (Mg) alloy's further applications in vascular stents. To solve these problems, a novel composite coating was designed on Mg alloy via a two-step method. First, a Mg alloy sample was immersed in hydrofluoric acid. Then, a poly-l-lactic acid (PLLA) coating was made by ultrasonic atomization spraying with 5 and 10 layers (referred to as PLLA(5)-HF-Mg and PLLA(10)-HF-Mg). Characterizations were analyzed from the microstructure, element distribution, and wettability. The degradation behavior was tested with an electrochemical test and immersion test. Endothelialization was investigated using human umbilical vein endothelial cells (HUVECs). Hemocompatibility was examined with a platelet adhesion test. The results showed that the PLLA coating could not only cover the surface, but also could permeate through and cover the holes on the MgF₂ layer, mechanically locked with the substrate. Thus, the composite coating had higher corrosion resistance. The PLLA/MgF₂ coating, especially on PLLA(10)-HF-Mg, enhanced HUVECs' viability and growth. While incubated with platelets, the PLLA/MgF₂ coating, especially on PLLA(10)-HF-Mg, had the lowest platelet adhesion number and activity. Taken together, the novel PLLA/MgF₂ coating controls Mg alloy's degradation by spraying different layers of PLLA, resulting in better endothelialization and hemocompatibility, providing a promising candidate for cardiovascular stents.

A comprehensive review of properties of the biocompatible thin films on biodegradable Mg alloys

Magnesium (Mg) and its alloys have attracted attention as biodegradable materials for biomedical applications owing to their mechanical properties being comparable to that of bone. Mg is a vital trace element in many enzymes and thus forms one of the essential factors for human metabolism. However, before being used in biomedical applications, the early stage or fast degradation of Mg and its alloys in the physiological environment should be controlled. The degradation of Mg alloys is a critical criterion that can be controlled by a surface modification which is an effective process for conserving their desired properties. Different coating methods have been employed to modify Mg surfaces to provide good corrosion resistance and biocompatibility. This review aims to provide information on different coatings and discuss their physical and biological properties. Finally, the current withstanding challenges have been highlighted and discussed, followed by shedding some light on future perspectives.

The effect of friction stir process on the mechanical, tribological, and biocompatibility properties of AZ31B magnesium alloy as a biomaterial: A pilot study

Recently, AZ31B magnesium alloy has been widely employed in automotive, aerospace, and bio implant industries due to its light-weight and biocompatibility properties. However, the equilibrium of ductility and strength of this material and the negativity brought by its poor wear behavior have limited its versatile use. Friction stir processing (FSP) has been commonly used as severe plastic deformation method for improving mechanical and tribological properties of metal sheets. The effect of this method on the biocompatibility of materials is a matter of curiosity that should be emphasized. So, the present study aims to investigate the effect of friction stir process on the mechanical, tribological, and biocompatibility properties of AZ31B magnesium alloy. It is observed that FSP enhanced the tensile properties of the alloy but decreased its elongation. It was determined that the base material exhibited ductile character on the fracture surface of the specimens, and mixed ductile/brittle fracture was evident with the FSP. In the FSP zone, the hardness value was improved by 17% compared to the base material. Also, the wear performance of the alloy enhanced in ambient air and Simulated Body Fluid (SBF) solution. Wear properties in SBF solution were better due to less adhesive bonds between the friction surfaces. This assessment was supported by SEM images of the wear path and surface of counter bodies. On the other hand, FSPed AZ31B alloy materials with improved strength properties were not cytotoxic for human gingival fibroblasts, and these results may suggest that the materials are safe for clinical uses.

Special Issue: Ceramic and Metallic Biomaterials Nanoparticles for Applications in Medical Sciences

Nowadays, the development of new materials that can be used to treat, repair, diagnose, replace, or restore a function of the human body represents one of the key research topics for the worldwide scientists and medical industries [...]