Synthesis of polyynes by intense femtosecond laser irradiation of SWCNTs suspended in methanol

Direct Fabrication of Te-Doped Black Si with an Enhanced Photoelectric Performance by Femtosecond Laser Irradiation under Water

Tellurium (Te)-doped black silicon (Si) with enhanced absorption and photoelectric performance over a broad wavelength range of 0.2-2.5 μm was obtained using femtosecond (fs) laser irradiation in liquid water. Prior to laser irradiation, the Si sample was covered with a Te thin film (thickness 200 nm) over an adhesion layer of Cr (thickness 5 nm). Surface analyses by scanning electron microscopy and three-dimensional confocal microscopy evidence the presence of hierarchical surface structures combining quasi-periodic stripes with a spatial period of about 5 μm and subwavelength laser-induced periodic surface structures directed in directions parallel and perpendicular to the direction of the laser polarization, respectively. Moreover, the incorporation of Te generates intermediate levels within the Si bandgap. The Te-doped black Si shows a significant enhancement of the absorption, which reaches values of about 48% in the UV and visible (0.2-1.1 μm) and 70% in the near-infrared (1.1-2.5 μm) spectral ranges, respectively, due to the synergistic effects of multiscale surface structures and Te incorporation. Moreover, the surface reflectance is reduced to almost zero across the entire spectrum. The Te-doped black Si sample is used to realize a photodetector which displays an impressive photoelectric capability, being characterized by a responsivity of 328 mA/W, and an external quantum efficiency of 49.27% at a voltage bias of -10 V for 1064 nm light illumination, with rising and falling times of 55 and 67 ms, respectively. These figures remarkably outperform the response of unprocessed Si under the same experimental conditions.

Fabrication of Au-Ag Bimetallic Nanoparticles Using Pulsed Laser Ablation for Medical Applications: A Review

In recent years, the synthesis of Au-Ag bimetallic nanoparticles has garnered immense attention due to their potential applications in diverse fields, particularly in the realm of medicine and healthcare. The development of efficient synthesis methods is crucial in harnessing their unique properties for medical applications. Among the synthesis methods, pulsed laser ablation in a liquid environment has emerged as a robust and versatile method for precisely tailoring the synthesis of bimetallic nanoparticles. This manuscript provides an overview of the fundamentals of the pulsed laser ablation in a liquid method, elucidating the critical factors involved. It comprehensively explores the pivotal factors influencing Au-Ag bimetallic nanoparticle synthesis, delving into the material composition, laser parameters, and environmental conditions. Furthermore, this review highlights the promising strides made in antibacterial, photothermal, and diagnostic applications. Despite the remarkable progress, the manuscript also outlines the existing limitations and challenges in this advanced synthesis technique. By providing a thorough examination of the current state of research, this review aims to pave the way for future innovations in the field, driving the development of novel, safe, and effective medical technologies based on Au-Ag bimetallic nanoparticles.

Magnesium Nanoparticle Synthesis from Powders via Pulsed Laser Ablation in Liquid for Nanocolloid Production

Magnesium nanoparticles of various mean diameters (53–239 nm) were synthesised in this study via pulsed laser ablation in liquid (PLAL) from millimetre sized magnesium powders within isopropyl alcohol. It was observed via a 3 × 3 full factorial design of experiments that the processing parameters can control the nanoparticle distribution to produce three size-distribution types (bimodal, skewed and normal). Ablation times of 2, 5, and 25 min where investigated. An ablation time of 2 min produced a bimodal distribution with the other types seen at higher periods of processing. Mg nanoparticle Ultraviolet–Visible spectroscopy (UV–Vis) absorbance at 204 nm increased linearly with increasing ablation time, indicating an increase in nanoparticle count. The colloidal density (mg/mL) generally increased with increasing nanoparticle mean diameter as noted via increasing UV–Vis absorbance. High laser scan speeds (within the studied range of 3000–3500 mm/s) tend to increase the nanoparticle count/yield. For the first time, the effect of scan speed on colloidal density, UV–Vis absorbance and nanoparticle diameter from metallic powder ablation was investigated and is reported herein. The nanoparticles formed dendritic structures after being drop cast on aluminium foil as observed via field emission scanning electron microscope analysis. Dynamic light scattering was used to measure the size of the nanoparticles. Magnesium nanoparticle inks show promise for use in the fabrication conductive tracks or thermal insulation in electronics.