Mono or polycrystalline alumina-modified hybrid ceramics

Microstructural and mechanical analysis of two CAD-CAM lithium disilicate glass-reinforced ceramics

The aim of this study was to analyze the structural, morphological and mechanical properties of two different lithium disilicate glass-reinforced ceramics for CAD-CAM systems (IPS e.max CAD and Rosetta SM). Five methodologies were used for both ceramics: microstructure (n = 2) was analyzed using x-ray diffraction (XRD); morphological properties (n = 2) were analyzed by scanning electron microscopy (SEM), with and without hydrofluoric etching; porosity (n = 3) was assessed using 3D micro-computed tomography (micro-CT); flexural strength was measured (n =1 0) using the three-point bending test; and bond strength was determined with self-adhesive resin cement (n = 10), using a microshear bond test. After performing all the tests, the data were analyzed using t-Student test and two-way ANOVA. All the tests used a significance level of α = 0.05. High peak positions corresponding to standard lithium metasilicate and lithium disilicate with similar intensities were observed for both ceramics in the XRD analysis. Morphological analysis showed that the crystalline structure of the two ceramics studied showed no statistical difference after acid etching. Additionally, no significant differences were recorded in the number or size of the pores for the ceramics evaluated. Moreover, no differences in flexural strength were found for the ceramic materials tested, or in the bond strength to ceramic substrates for the resin cements. Based on the study results, no significant differences were found between the two CAD-CAM lithium disilicate glass-reinforced ceramics tested, since they presented similar crystalline structures with comparable intensities, and similar total porosity, flexural strength and bond strength.

Functionalized pink Al2O3:Mn pigments applied in prosthetic dentistry

STATEMENT OF PROBLEM

The color of dental poly(methyl methacrylate) (PMMA) is conventionally rendered by organic and inorganic pigments, which are usually not bonded to the polymer network. Functionalized ceramic pigments can be used to color PMMA, allowing improved chemical interaction with the resin matrix.

PURPOSE

The purpose of this in vitro study was to synthesize, functionalize, and characterize pink manganese-doped alumina ceramic pigments. The hypothesis tested was that functionalized ceramic pigments would render pink coloration to a translucent PMMA without jeopardizing its mechanical properties.

MATERIAL AND METHODS

Pink alumina powders doped with 1 or 2 mol% of manganese (Al₂O₃:Mn) were prepared by means of a polymeric precursor method. Pigment (Pig.) particles were functionalized with a silica coating method followed by silanation before preparation of PMMA-based composite resins (5 wt% pigment). The color of composite resins (Pig.1% and Pig.2%) and PMMA controls (Pink and translucent [Trans]) was evaluated (CIELab color coordinates), and their mechanical properties were tested (3-point bending).

RESULTS

The microstructure of the pigment particles showed approximately 55-nm nanocrystals of manganese-doped α-alumina clustered into irregular porous particles up to 60 μm. The composite resins and pink PMMA showed similar color parameters (CIE a* pink=20.1, Pig.1%=14.6, Pig.2%=16.0, Trans=0.19, P<.001; CIE b* Pink=17.0, Pig.1%=18.6, Pig.2%=19.0, Trans=2.52, P<.001). No statistical differences were observed in mechanical properties among groups (σ_f pink=98.4, Pig.1%=98.1, Pig.2%=98.8, trans=89.1, P=.136).

CONCLUSIONS

The addition of the functionalized pink ceramic pigments to a translucent PMMA yielded similar coloration to that of the regular pink PMMA used in dentistry and did not jeopardize its mechanical properties.