Optical and mechanical factors in the temporal development of tooth-composite bond

Optical effects of graphene addition on adhesives for orthodontic lingual retainers

The objective of this study was to determine the effects on the colour of adding increasing concentrations of graphene to orthodontic fixed retainer adhesives and to evaluate changes in optical transmission during light curing and the resultant degree of conversion. Two different types of adhesives commonly used for fixed retainers were investigated: A packable composite (Transbond) and a flowable composite (Transbond Supreme). Graphene was added to the adhesives in three different concentrations (0.01, 0.05, and 0.1 wt%). Adhesives without graphene addition were set as control groups. A Minolta colourimeter was used to measure the colour and translucency parameters. Irradiance transmitted during curing was quantified using MARC Light Collector. Fourier-transform infrared spectroscopy was used to record degree of conversion. Data were statistically analysed with the Student's t-test and one-way ANOVA with Tukey's tests (α = 0.05). The findings showed that incorporating graphene darkened the adhesive colour significantly and reduced translucency. As the graphene concentration reached 0.1 wt%, samples became opaque; yet, no adverse effect on degree of conversion was observed. The addition of graphene reduces optical transmission of lingual retainer adhesives; the effect increases with graphene concentration.

Niobium silicate particles promote in vitro mineral deposition on dental adhesive resins

OBJECTIVE

This study aims to analyze the addition of niobium silicate particles to dental adhesive resins and evaluate its physicomechanical and biological properties.

METHODS

The SiNb particles were produced by the sol-gel route and presented a mean particle size of 2.1 μm and a specific surface area of 616,96m2/g. An experimental adhesive resin was formulated with 66 wt% Bisphenol A-Glycidyl Methacrylate and 33 wt% Hydroxyethyl methacrylate with diphenyl(2,4,6-trimethyl benzoyl)phosphine oxide as the photoinitiator. The SiNb particles were incorporated into the adhesive resins in 1 wt% (SiNb1%) and 2 wt% (SiNb2%) concentration. A control group (SiNb0%) without the addition of particles was used. The developed adhesives were evaluated by their polymerization kinetics, refractive index, softening in solvent, cytotoxicity, mineral deposition, ultimate tensile strength, and micro shear bond strength.

RESULTS

The refractive index range was increased by the addition of niobium silicate particles. No statistically significant difference was found between groups in the degree of conversion,.softening in solvent analysis, cytotoxicity and ultimate tensile strength. The deposition of minerals increased after immersion of specimens in SBF after 14 days on the SiNb2%. The SiNb2% group showed high micro shear bond strength values, reaching 33.87 MPa.

CONCLUSION

In the present study, the addition of 2 wt% of niobium silicate into dental adhesive resins promoted the mineral deposition with increased bond strength without affecting other material properties.

CLINICAL SIGNIFICANCE

Bioactive fillers must maintain the physical-chemical properties of dental adhesives, guaranteeing their clinical performance. Niobium silicate particles could promote the remineralization of dentin hard tissues without compromising the physico-mechanical properties on these materials.