The use of an elastomeric methacrylate monomer (Exothane 24) to reduce the polymerization shrinkage stress and improve the two-body wear resistance of bulk fill composites

Physicochemical properties of flowable composites using isobornyl methacrylate as diluent monomer

OBJECTIVE

this study sought to evaluate the effect of isobornyl methacrylate (IBOMA) as a diluent monomer on the physicochemical properties of experimental flowable resin composites.

METHODOLOGY

the organic resin matrix of a modal flowable resin composite was formulated with 50 wt.% of bisphenol-A-glycidyl methacrylate (Bis-GMA) and 50 wt.% of a diluent monomer, in which IBOMA was used as a combining or substituent diluent monomer to triethylene glycol dimethacrylate (TEGDMA). The resin matrices were filled with 55 wt.% particles, of which 10 wt.% was 0.05-μm fumed silica, and 45 wt.% was 0.7-μm BaBSiO2 glass. Polymerization shrinkage stress (PSS; n=10), degree of conversion (DC; n=3), maximum rate of polymerization (Rpmax; n=3), film thickness (FT; n=10), sorption (Wsp; n=10), solubility (Wsl; n=10), flexural strength (FS; n=10), flexural modulus (FM; n=10), Knoop microhardness (KH; n=10), and microhardness reduction after chemical softening (HR; n=10) were evaluated. Data were analyzed using one-way ANOVA, followed by Tukey's test (α=0.05; β=0.2).

RESULTS

the results showed that the substitution or addition of IBOMA reduced FT (p=0.001), PSS (p=0.013), Rpmax (p=0.001), DC (p=0.001), FM (p=0.006) Wsp (p=0.032), and Wsl (p=0.021). However, when used as a complete substituent, IBOMA demonstrated significantly lower FS (p=0.017) and KH (p=0.008), while TEGDMA demonstrated significantly lower HR (p=0.022).

CONCLUSION

the flowable composite containing IBOMA combined with TEGDMA showed no effect in KH and FS and effectively reduced the PSS, RP, FT, Wsp, and Wsl. However, it showed a reduction in DC, FS, and an increase in HR.

Effect of butylated hydroxytoluene (BHT) concentrations on polymerization shrinkage stress and other physicochemical properties of experimental resin composites

The present study examined different concentrations of the butylated hydroxytoluene (BHT) inhibitor on the kinetics of conversion, polymerization shrinkage stress, and other correlated physicochemical properties of experimental resin composites (ERC). A model composite was formulated with 75 wt% filler containing 0.5 wt% camphorquinone and 1 wt% amine with BHT concentrations of 0.01 wt% (BHT-0.01); 0.1 wt% (BHT-0.1); 0.25 wt% (BHT-0.25); 0.5 wt% (BHT-0.5); 1 wt% (BHT-1), and control (no BHT). They were tested on polymerization shrinkage stress (PSS; n = 5), degree of conversion (DC; n = 3), maximum polymerization rate (RpMAX; n = 5), water sorption (Wsp; n = 0), and solubility (Wsl; n = 10), flexural strength (FS; n = 10), flexural modulus (FM; n = 10), Knoop microhardness (KH; n = 10), and microhardness reduction (HR; n = 10). Data concerning these tests were submitted to one-way ANOVA and Tukey's test (α = 0.05; β = 0.2). BHT-0.25, BHT-0.5, and BHT-1 showed a gradually significant decrease in PSS (p = 0.037); however, BHT-1 demonstrated a decrease in the physicochemical properties tested. Thus, within the limitations of this study, it was possible to conclude that BHT concentrations between 0.25 and 0.5 wt% are optimal for reducing shrinkage stress without affecting other physicochemical properties of ERCs.

Surface Analysis of a Universal Resin Composite and Effect of Preheating on its Physicochemical Properties

This study was aimed at analyzing the surface properties of a universal resin composite and evaluating the effect of preheating on its physicochemical properties. Two commercial resin composites were used under two conditions: Filtek Universal Restorative (UR); UR preheated (URH); Filtek Supreme (FS) and FS preheated (FSH). The film thickness (FT) test (n = 10) was done using two glass slabs under compression. Flexural strength (FLS) and modulus (FLM) were evaluated using a three-point flexion test (n = 10). Polymerization shrinkage stress (PSS) was evaluated in a universal testing machine (n = 5). Gap width (GW) between composite and mold was measured in internally polished metallic molds (n = 10). The degree of conversion (DC) was evaluated by Fourier Transform Infrared spectroscopy (n = 3). The morphology of the filler particles was checked by scanning electron microscope (SEM) and EDX analysis. Surface gloss (SG) and surface roughness (SR) were evaluated before and after mechanical brushing (n = 10). The outcomes were submitted to 2-way ANOVA and Tukey's test (α = 0.05). Lower mean values of FT were observed for the preheated groups when compared to the non-preheated groups. URH and FSH showed higher mean values of FLS and FLM when compared with UR and FS. No differences were observed between groups in the PSS test. The GW was higher for the UR and FS groups when compared with URH and FSH. The DC was higher for preheated resin composites when compared to the non-preheated groups. The SR of the UR composite was higher than the FS after mechanical brushing, while the SG was higher for the FS groups. In conclusion, the universal resin composite tested generally presented similar physicochemical properties compared with the nanofilled resin composite and either similar or slightly inferior surface properties. The preheating improved or maintained all properties evaluated.

Effect of elastomeric urethane monomer on physicochemical properties and shrinkage stress of resin composites

This study aimed to evaluate the effect of an elastomeric urethane monomer (Exothane-24) in different concentrations on physicochemical properties, gap formation, and polymerization shrinkage stress of experimental resin composites. All experimental composites were prepared with 50 wt.% of Bis-GMA and 50 wt.% of TEGDMA, to which 0 wt.% (control), 10 wt.%, 20 wt.%, 30 wt.%, and 40 wt.% of Exothane-24 were added. Filler particles (65 wt.%) were then added to these resin matrixes. Ultimate tensile strength (UTS: n = 10), flexural strength (FS: n = 10), flexural modulus (FM: n = 10), hardness (H: n = 10), hardness reduction (HR: n = 10), degree of conversion (DC: n = 5), gap width (GW: n = 10), and polymerization shrinkage stress in Class I (SS-I: n = 10) and Class II (SS-II: n = 10) simulated configuration. All test data were analyzed using one-way ANOVA and Tukey's test (α = 0.05;  = 0.2). Exothane-24 in all concentrations decreased the H, HR, DC, GW, SS-I, and SS-II (p < 0.05) without affecting the UTS, and FS (p > 0.05). Reduction in FM was observed only in the Exothane 40% and 30% groups compared to the control (p < 0.05). Exothane-24 at concentrations 20% and 30% seems suitable since it reduced GW and polymerization SS without affecting the properties of the composite resins tested, except for H.

Effect of preheating on mechanical properties of a resin-based composite containing elastomeric urethane monomer

This study investigated the effect of preheating an elastomeric urethane monomer (Exothane-24) experimental resin composite on its physicochemical properties. Two resin matrices were formulated: (a) 50 wt% Bisphenol-glycidyl methacrylate (Bis-GMA) and 50 wt% triethylene glycol dimethacrylate (TEGDMA); and (b) 20 wt% Exothane-24, 40 wt% Bis-GMA and 40 wt% TEGDMA. A photoinitiator system (0.25 wt% camphorquinone and 0.50 wt% ethyl-4-dimethylamino benzoate) and 65 wt% of the inorganic filler (20 wt% 0.05 μm silica and 80 wt% 0.7 μm BaBSiO₂ glass) were added to both matrices. These formulations were then assigned to four groups: Exothane-24 (E); Exothane-24 plus preheating (EH); no Exothane-24 (NE); and no Exothane-24 plus preheating (NEH). NEH and EH were preheated at 69 °C. The dependent variables were as follows: film thickness (FT); polymerization shrinkage stress (PSS); gap width (GW); maximum rate of polymerization (Rp_max); and degree of conversion (DC). Data were statistically analyzed by two-way ANOVA and Tukey's test (α = 0.05). Preheating reduced FT for both composites. PSS and GW were significantly lower for EH, when compared with E. The DC for EH and NEH and the Rp_max for EH increased significantly. Preheating improved most of the physicochemical properties (FT, PSS, GW, and DC) of the experimental resin composite containing Exothane-24.