Electrocatalytic behavior of thin Co–Te–O films in oxygen evolution and reduction reactions

Charge storage in oxygen deficient phases of TiO2: defect Physics without defects

Defects in semiconductors can exhibit multiple charge states, which can be used for charge storage applications. Here we consider such charge storage in a series of oxygen deficient phases of TiO2, known as Magnéli phases. These Magnéli phases (TinO2n-1) present well-defined crystalline structures, i.e., their deviation from stoichiometry is accommodated by changes in space group as opposed to point defects. We show that these phases exhibit intermediate bands with an electronic quadruple donor transitions akin to interstitial Ti defect levels in rutile TiO2. Thus, the Magnéli phases behave as if they contained a very large pseudo-defect density: ½ per formula unit TinO2n-1. Depending on the Fermi Energy the whole material will become charged. These crystals are natural charge storage materials with a storage capacity that rivals the best known supercapacitors.

Selective preparation of macroporous monoliths of conductive titanium oxides Ti(n)O(2n-1) (n = 2, 3, 4, 6)

Monolithic conductive titanium oxides Ti(n)O(2n-1) (n = 2, 3, 4, 6) with well-defined macropores have been successfully prepared as a single phase, via reduction of a macroporous TiO(2) precursor monolith using zirconium getter. Despite substantial removal of oxide ions, all the reduced monoliths retain the macropore properties of the precursor, i.e., uniform pore size distribution and pore volume. Furthermore, compared to commercial porous Ebonex (shaped conductive Ti(n)O(2n-1)), the bulk densities (1.8 g cm(-3)) are half, and the porosities (60%) are about 3 times higher. The obtained Ti(n)O(2n-1) (n = 2, 3, 4, 6) macroporous monoliths could find applications as electrodes for many electrochemical reactions.