Electrodepositing manganese oxide into a graphene hydrogel to fabricate an asymmetric supercapacitor

A high-performance and flexible electrode film based on bacterial cellulose/polypyrrole/nitrogen-doped graphene for supercapacitors

With the development and popularity of portable electronic devices, there is an urgent need for flexible energy storage devices suitable for mass production. We report freestanding paper electrodes for supercapacitors fabricated via a simple but efficient two-step method. Nitrogen-doped graphene (N-rGO) was first prepared via a hydrothermal method. This not only obtained nitrogen atom-doped nanoparticles but also formed reduced graphene oxide. Pyrrole (Py) was then deposited on the bacterial cellulose (BC) fibers as a polypyrrole (PPy) pseudo-capacitance conductive layer by in situ polymerization and filtered with nitrogen-doped graphene to prepare a self-standing flexible paper electrode with a controllable thickness. The synthesized BC/PPy/N₁₅-rGO paper electrode has a remarkable mass specific capacitance of 441.9 F g^-1, a long cycle life (96 % retention after 3000 cycles), and excellent rate performance. The BC/PPy/N₁₅-rGO-based symmetric supercapacitor shows a high volumetric specific capacitance of 244 F cm^-3 and a max energy density of 67.9 mWh cm^-3 with a power density of 1.48 W cm^-3, suggesting that they will be promising materials for flexible supercapacitors.

Engineering Co3O4/MnO2 nanocomposite materials for oxygen reduction electrocatalysis

Stable and active electrocatalysts preparation for the oxygen reduction reaction (ORR) is essential for an energy storage and conversion materials (e.g. metal-air batteries). Herein, we prepared a highly-active MnO₂ and Co₃O₄/MnO₂ nanocomposite electrocatalysts using a facial co-precipitation approach. The electrocatalytic activity was examined in alkaline media with LSV and CV. Additionally, the physicochemical characteristics of the MnO₂ and Co₃O₄/MnO₂ composite materials were studied via SEM, XRD, BET, UV-Vis, TGA/DTA, ICP-OES and FTIR. Morphological studies indicated that a pure MnO₂ has a spherical flower-like architecture, whereas Co₃O₄/MnO₂ nanocomposites have an aggregated needle-like structure. Moreover, from the XRD investigation parameters such as the dislocation density, micro-strain, and crystallite size were analyzed. The calculated energy bandgaps for the MnO₂, Co₃O₄/MnO₂-1-5, and Co₃O₄/MnO₂-1-1 nanocomposites were 3.07, 2.6, and 2.3 eV, correspondingly. The FTIR spectroscopy was also employed to study the presence of M-O bonds (M = Mn, Co). The thermal gravimetric investigation showed that the Co₃O₄/MnO₂ nanocomposite materials exhibited improved thermal stability, confirming an enhanced catalytic activity of ORR for MnO₂/Co₃O₄-1-1 composite materials for ORR. These results confirm that the prepared Co₃O₄/MnO₂ composite materials are promising air electrode candidates for the energy storage and conversion technologies.

Anchoring carbon layers and oxygen vacancies endow WO3−x/C electrode with high specific capacity and rate performance for supercapacitors

Herein, novel hierarchical carbon layer-anchored WO_3−x/C ultra-long nanowires were developed via a facile solvent-thermal treatment and a subsequent rapid carbonization process. The inner anchored carbon layers and abundant oxygen vacancies endowed the WO_3−x/C nanowire electrode with high conductivity, as measured with a single nanowire, which greatly enhanced the redox reaction active sites and rate performance. Surprisingly, the WO_3−x/C electrode exhibited outstanding specific capacitance of 1032.16 F g⁻¹ at the current density of 1 A g⁻¹ in a 2 M H₂SO₄ electrolyte and maintained the specific capacitance of 660 F g⁻¹ when the current density increased to 50 A g⁻¹. Significantly, the constructed WO_3−x/C//WO_3−x/C symmetric supercapacitors achieved specific capacitance of 243.84 F g⁻¹ at the current density of 0.5 A g⁻¹ and maintained the capacitance retention of 94.29% after 5000 charging/discharging cycles at the current density of 4 A g⁻¹. These excellent electrochemical performances resulted from the fascinating structure of the WO_3−x/C nanowires, showing a great potential for future energy storage applications.

A high-performance supercapacitor electrode comprising hierarchical carbon layer-anchored WO_3−x/C nanowires with inner abundant redox reaction active sites and numerous oxygen vacancies is presented.