SILAR deposited nickel sulphide-nickel hydroxide nanocomposite for high performance asymmetric supercapacitor

Hydrothermal Synthesis of β-NiS Nanoparticles and Their Applications in High-Performance Hybrid Supercapacitors

In this work, β-NiS nanoparticles (NPs) were efficiently prepared by a straightforward hydrothermal process. The difference in morphology between these NiS NPs was produced by adding different amounts of thiourea, and the corresponding products were denoted as NiS-15 and NiS-5. Through electrochemical tests, the specific capacity (Cs) of NiS-15 was determined to be 638.34 C g-1 at 1 A g-1, compared to 558.17 C g-1 for NiS-5. To explore the practical application potential of such β-NiS NPs in supercapacitors, a hybrid supercapacitor (HSC) device was assembled with activated carbon (AC) as an anode. Benefitting from the high capacity of the NiS cathode and the large voltage window of the device, the NiS-15//AC HSC showed a high energy density (Ed) of 43.57 W h kg-1 at 936.92 W kg-1, and the NiS-5//AC HSC provided an inferior Ed of 37.89 W h kg-1 at 954.79 W kg-1. Both HSCs showed excellent cycling performance over 6000 cycles at 10 A g-1. The experimental findings suggest that both NiS-15 and NiS-5 in this study can serve as potential cathodes for high-performance supercapacitors. This current synthesis method is simple and can be extended to the preparation of other transition metal sulfide (TMS)-based electrode materials with exceptional electrochemical properties.

Review of NiS-Based Electrode Nanomaterials for Supercapacitors

As a new type of energy storage device, supercapacitors have the advantages of high-power densities, high safety factors, and low maintenance costs, so they have attracted widespread attention among researchers. However, a major problem with supercapacitors is that their energy densities are not high enough, which limits their application. Therefore, it is crucial to expand the application scenarios of supercapacitors to increase their energy density as much as possible without diminishing their advantages. The classification and working principles of supercapacitors are introduced in this paper. The electrochemical properties of pure NiS materials, NiS composites with carbon materials, NiS composites with sulfide materials, and NiS composites with transition metal oxides for supercapacitors are summarized. This paper may assist in the design of new electrode materials for NiS-based supercapacitors.

Synthesis of Ni3S2 and MOF-Derived Ni(OH)2 Composite Electrode Materials on Ni Foam for High-Performance Supercapacitors

Honeycomb-like Ni(OH)₂/Ni₃S₂/Ni foam (NF) was fabricated via a two-step hydrothermal process and subsequent alkalization. Ni₃S₂ with a honeycombed structure was in-situ synthesized on the NF surface by a hydrothermal process. MOF-derived Ni(OH)₂ nanosheets were then successfully grown on the Ni₃S₂/NF surface by a second hydrothermal process and alkaline treatment, and a large number of nanosheets were interconnected to form a typical honeycomb-like structure with a large specific surface area and porosity. As a binder-free electrode, the prepared honeycomb-like Ni(OH)₂/Ni₃S₂/NF exhibited a high specific capacitance (2207 F·g^-1 at 1 A·g^-1, 1929.7 F·g^-1 at 5 mV·s^-1) and a remarkable rate capability and cycling stability, with 62.3% of the initial value (1 A·g^-1) retained at 10 A·g^-1 and 90.4% of the initial value (first circle at 50 mV·s^-1) retained after 5000 cycles. A hybrid supercapacitor (HSC) was assembled with Ni(OH)₂/Ni₃S₂/NF as the positive electrode and activated carbon (AC) as the negative electrode and exhibited an outstanding energy density of 24.5 Wh·kg^-1 at the power density of 375 W·kg^-1. These encouraging results render the electrode a potential candidate for energy storage.