Metal organic frameworks derived Ni-doped hierarchical NiXCo1-XS@C bundled-like nanostructures for enhanced supercapacitors

Advances in Mn-Based MOFs and Their Derivatives for High-Performance Supercapacitor

As the most widely used metal material in supercapacitors, manganese (Mn)-based materials possess the merits of high theoretical capacitance, stable structure as well as environmental friendliness. However, due to poor conductivity and easy accumulation, the practical capacitance of Mn-based materials is far lower than that of theoretical value. Therefore, accurate structural adjustment and controllable strategies are urgently needed to optimize the electrochemical properties of Mn-based materials. Metal-organic frameworks (MOFs) are porous materials with high specific surface area (SSA), tunable pore size, and controllable structure. These features make them attractive as precursors or scaffold for the synthesis of metal-based materials and composites, which are important for electrochemical energy storage applications. Therefore, a timely and comprehensive review on the classification, design, preparation and application of Mn-based MOFs and their derivatives for supercapacitors has been given in this paper. The recent advancement of Mn-based MOFs and their derivatives applied in supercapacitor electrodes are particularly highlighted. Finally, the challenges faced by Mn-MOFs and their derivatives for supercapacitors are summarized, and strategies to further improve their performance are proposed. The aspiration is that this review will serve as a beneficial compass, guiding the logical creation of Mn-based MOFs and their derivatives in the future.

Ni0.5Co0.5S nano-chains: a high-performing intercalating pseudocapacitive electrode in asymmetric supercapacitor (ASC) mode for the development of large-scale energy storage devices

Grid-scale energy storage solutions are necessary for using renewable energy sources efficiently. A supercapattery (supercapacitor + battery) has recently been introduced as a new variety of hybrid devices that engage both capacitive and faradaic charge storage processes. Nano-chain architectures of Ni0.5Co0.5S electrode materials consisting of interconnected nano-spheres are rationally constructed by tailoring the surface structure. Nano-chains of the bimetallic sulfide Ni0.5Co0.5S are presented to have a superior charge storage capacity. The Ni0.5Co0.5S nano-chain electrode presents a capacitance of 2001.6 F g-1 at 1 mV s-1, with a specific capacity of 267 mA h g-1 (1920 F g-1) at 1 A g-1 in 4 M KOH aqueous electrolyte through the galvanostatic charge-discharge (GCD) method. The reason behind the high charge storage capacity of the materials is the predominant redox-mediated diffusion-controlled pseudocapacitive mechanism coupled with surface capacitance (electrosorption), as the surface (outer) and intercalative (inner) charges stored by the Ni0.5Co0.5S electrodes are close to 46.0% and 54.0%, respectively. Additionally, a Ni0.5Co0.5S//AC two electrode full cell operating in asymmetric supercapacitor cell (ASCs) mode in 4 M KOH electrolyte exhibits an impressive energy density equivalent to 257 W h kg-1 and a power density of 0.73 kW kg-1 at a current rate of 1 A g-1.

MOF-Derived Ultrathin NiCo-S Nanosheet Hybrid Array Electrodes Prepared on Nickel Foam for High-Performance Supercapacitors

At present, binary bimetallic sulfides are widely studied in supercapacitors due to their high conductivity and excellent specific capacitance (SC). In this article, NiCo-S nanostructured hybrid electrode materials were prepared on nickel foam (NF) by using a binary metal-organic skeleton as the sacrificial template via a two-step hydrothermal method. Comparative analysis was carried out with Ni-S and Co-S in situ on NF to verify the excellent electrochemical performance of bimetallic sulfide as an electrode material for supercapacitors. NiCo-S/NF exhibited an SC of 2081 F∙g^-1 at 1 A∙g^-1, significantly superior to Ni-S/NF (1520.8 F∙g^-1 at 1 A∙g^-1) and Co-S/NF (1427 F∙g^-1 at 1 A∙g^-1). In addition, the material demonstrated better rate performance and cycle stability, with a specific capacity retention rate of 58% at 10 A∙g^-1 than at 1 A∙g^-1, and 75.7% of capacity was retained after 5000 cycles. The hybrid supercapacitor assembled by NiCo-S//AC exhibited a high energy density of 25.58 Wh∙kg^-1 at a power density of 400 W∙kg^-1.