Microstructured poly(2-hydroxyethyl methacrylate)/poly(glycerol monomethacrylate) interpenetrating network hydrogels: UV-scattering induced accelerated formation and tensile behavior

Microscopic Structure of Swollen Hydrogels by Scanning Electron and Light Microscopies: Artifacts and Reality

The exact knowledge of hydrogel microstructure, mainly its pore topology, is a key issue in hydrogel engineering. For visualization of the swollen hydrogels, the cryogenic or high vacuum scanning electron microscopies (cryo-SEM or HVSEM) are frequently used while the possibility of artifact-biased images is frequently underestimated. The major cause of artifacts is the formation of ice crystals upon freezing of the hydrated gel. Some porous hydrogels can be visualized with SEM without the danger of artifacts because the growing crystals are accommodated within already existing primary pores of the gel. In some non-porous hydrogels the secondary pores will also not be formed due to rigid network structure of gels that counteracts the crystal nucleation and growth. We have tested the limits of true reproduction of the hydrogel morphology imposed by the swelling degree and mechanical strength of gels by investigating a series of methacrylate hydrogels made by crosslinking polymerization of glycerol monomethacrylate and 2-hydroxyethyl methacrylate including their interpenetrating networks. The hydrogel morphology was studied using cryo-SEM, HVSEM, environmental scanning electron microscopy (ESEM), laser scanning confocal microscopy (LSCM) and classical wide-field light microscopy (LM). The cryo-SEM and HVSEM yielded artifact-free micrographs for limited range of non-porous hydrogels and for macroporous gels. A true non-porous structure was observed free of artifacts only for hydrogels exhibiting relatively low swelling and high elastic modulus above 0.5 MPa, whereas for highly swollen and/or mechanically weak hydrogels the cryo-SEM/HVSEM experiments resulted in secondary porosity. In this contribution we present several cases of severe artifact formation in PHEMA and PGMA hydrogels during their visualization by cryo-SEM and HVSEM. We also put forward empirical correlation between hydrogel morphological and mechanical parameters and the occurrence and intensity of artifacts.

Reusable Surface-Modified Bacterial Cellulose Based on Atom Transfer Radical Polymerization Technology with Excellent Catalytic Properties

The high catalytic activity of membrane-binding gold nanoparticles (AuNPs) makes its application in oxidation or reduction an attractive challenge. Herein, surface-functionalized bacterial cellulose (BC-poly(HEMA)) was successfully prepared with 2-hydroxyethyl methacrylate (HEMA) as monomers via the atom transfer radical polymerization (ATRP) method. BC-poly(HEMA) was further utilized as not only reducing agent but also carrier for uniform distribution of the AuNPs in the diameter of about 8 nm on the membrane surface during the synthesis stage. The synthesized AuNPs/BC-poly(HEMA) exhibited excellent catalytic activity and reusability for reducing 4-nitrophenol (4-NP) from NaBH₄. The results proved that the catalytic performance of AuNPs/BC-poly(HEMA) was affected by the surrounding temperature and pH, and AuNPs/BC-poly(HEMA) maintained the extremely high catalytic activity of AuNPs/BC-poly(HEMA) even after 10 reuses. In addition, no 4-NP was detected in the degradation solution after being stored for 45 days. The reusable catalyst prepared by this work shows a potential industrial application prospect.

Biomimetic modification of dual porosity poly(2-hydroxyethyl methacrylate) hydrogel scaffolds-porosity and stem cell growth evaluation

The macroporous synthetic poly(2-hydroxyethyl methacrylate) (pHEMA) hydrogels as 3D cellular scaffolds with specific internal morphology, so called dual pore size, were designed and studied. The morphological microstructure of hydrogels was characterized in the gel swollen state and the susceptibility of gels for stem cells was evaluated. The effect of specific chemical groups covalently bound in the hydrogel network by copolymerization on cell adhesion and growth, followed by effect of laminin coating were investigated. The evaluated gels contained either carboxyl groups of the methacrylic acid or quaternary ammonium groups brought by polymerizable ammonium salt or their combinations. The morphology of swollen gel was visualized using the laser scanning confocal microscopy. All hydrogels had very similar porous structures - their matrices contained large pores (up to 10² μm) surrounded with gel walls with small pores (10⁰ μm). The total pore volume in hydrogels swollen in buffer solution ranged between 69 and 86 vol%. Prior to the seeding of the mouse embryonal stem cells, the gels were coated with laminin. The hydrogel with quaternary ammonium groups (with or without laminin) stimulated the cell growth the most. The laminin coating lead to a significant and quaternary ammonium groups. The gel chemical modification influenced also the topology of cell coverage that ranged from individual cell clusters to well dispersed multi cellular structures. Findings in this study point out the laser scanning confocal microscopy as an irreplaceable method for a precise and quick assessment of the hydrogel morphology. In addition, these findings help to optimize the chemical composition of the hydrogel scaffold through the combination of chemical and biological factors leading to intensive cell attachment and proliferation.